Effect of hot isostatic pressing on microstructural and mechanical properties of electroplated coatings on SLM-304L stainless steel
- 12Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
- 23Huazhong University of Science and Technology, Wuhan, China
- 31Chengdu Aeronautic Polytechnic University, Chengdu 610100, China
Abstract
Hot isostatic pressing (HIP) is widely used to eliminate internal defects and refine the microstructure of additively manufactured 304L stainless steel produced via selective laser melting (SLM). However, the effects of HIP on SLM-fabricated 304L coatings—particularly those with electrodeposited chromium layers—remain poorly understood and lack systematic investigation. This study systematically examines how HIP post-treatment influences the microstructural evolution, interfacial integrity, and mechanical performance of chromium-electroplated 304L coatings on SLM-built substrates. In particular, 304L stainless steel substrates were first fabricated by SLM, then coated with chromium via electrodeposition, followed by conventional heat treatment and subsequent HIP processing (600 °C, 70 MPa). Comprehensive characterization—including scanning electron microscopy, energy-dispersive x-ray spectroscopy, Vickers microhardness mapping across substrate/coating interfaces, and surface topography analysis—was performed to correlate processing conditions with microstructural features, elemental distribution, hardness gradients, and coating adhesion. Results reveal that after heat treatment alone, the chromium coating exhibits severe longitudinal cracking perpendicular to the substrate, significant surface waviness, and elevated roughness. In contrast, HIP treatment improves surface planarity but induces interfacial delamination at the Cr/304L boundary, suggesting a trade-off between surface consolidation and interfacial thermal–mechanical compatibility. The underlying mechanism is attributed to differential thermal expansion and residual stress relaxation during HIP, which compromises interfacial bonding despite microstructural homogenization within the coating. In contrast, HIP at 1150 °C and 150 MPa promotes excellent surface flatness through the synergistic effects of high temperature and pressure, resulting in a straight, dense, and well-bonded interface between the chromium coating and the substrate. The coating primarily consists of Fe–Cr and Fe–Ni intermetallic compounds, with complete elimination of elemental phase segregation. A maximum microhardness of 501.8 HV0.2 was achieved. This research provides an experimental foundation for optimizing the surface characteristics of SLM-fabricated 304L stainless steel components.
Related
- Passivation properties of ultrafine grain 316L stainless steels manufactured by ball milling and spark plasma sintering
- Microstructural and emission properties induced by Na incorporation in pure sulphide CIGS absorber
- Investigation of the Microstructural and Magnetic Properties of Ni on GeSn Layers
- Additive manufacturing of a Ni-20 wt%Cr binary alloy by laser powder bed fusion: Impact of the microstructure on the mechanical properties
- Atomic investigations on the mechanical properties of CoCrNi medium-entropy alloy nanowires
BibTeX
@article{xue2026effect,
title = {{Effect of hot isostatic pressing on microstructural and mechanical properties of electroplated coatings on SLM-304L stainless steel}},
author = {Weihai Xue and Bo Tao and Yong Li and Wei Xu},
journal = {AIP Advances},
year = {2026},
month = nov,
doi = {10.1063/5.0343319},
url = {https://doi.org/10.1063/5.0343319},
note = {CC BY},
}
RIS
TY - JOUR
TI - Effect of hot isostatic pressing on microstructural and mechanical properties of electroplated coatings on SLM-304L stainless steel
AU - Weihai Xue
AU - Bo Tao
AU - Yong Li
AU - Wei Xu
PY - 2026
DA - 2026/11/04
JO - AIP Advances
DO - 10.1063/5.0343319
UR - https://doi.org/10.1063/5.0343319
AB - Hot isostatic pressing (HIP) is widely used to eliminate internal defects and refine the microstructure of additively manufactured 304L stainless steel produced via selective laser melting (SLM). However, the effects of HIP on SLM-fabricated 304L coatings—particularly those with electrodeposited chromium layers—remain poorly understood and lack systematic investigation. This study systematically examines how HIP post-treatment influences the microstructural evolution, interfacial integrity, and mechanical performance of chromium-electroplated 304L coatings on SLM-built substrates. In particular, 304L stainless steel substrates were first fabricated by SLM, then coated with chromium via electrodeposition, followed by conventional heat treatment and subsequent HIP processing (600 °C, 70 MPa). Comprehensive characterization—including scanning electron microscopy, energy-dispersive x-ray spectroscopy, Vickers microhardness mapping across substrate/coating interfaces, and surface topography analysis—was performed to correlate processing conditions with microstructural features, elemental distribution, hardness gradients, and coating adhesion. Results reveal that after heat treatment alone, the chromium coating exhibits severe longitudinal cracking perpendicular to the substrate, significant surface waviness, and elevated roughness. In contrast, HIP treatment improves surface planarity but induces interfacial delamination at the Cr/304L boundary, suggesting a trade-off between surface consolidation and interfacial thermal–mechanical compatibility. The underlying mechanism is attributed to differential thermal expansion and residual stress relaxation during HIP, which compromises interfacial bonding despite microstructural homogenization within the coating. In contrast, HIP at 1150 °C and 150 MPa promotes excellent surface flatness through the synergistic effects of high temperature and pressure, resulting in a straight, dense, and well-bonded interface between the chromium coating and the substrate. The coating primarily consists of Fe–Cr and Fe–Ni intermetallic compounds, with complete elimination of elemental phase segregation. A maximum microhardness of 501.8 HV0.2 was achieved. This research provides an experimental foundation for optimizing the surface characteristics of SLM-fabricated 304L stainless steel components.
SN - 2158-3226
ER -