Tuning structural, optical, charge storage, and electronic transport properties of graphene oxide through functional group engineering
Abstract
This study investigates the effect of oxidation temperature on the structural, electronic, and electrochemical properties of graphene oxide (GO) synthesized at 75, 95, and 115 °C. Increasing the oxidation temperature resulted in a reduction in crystallite size from 9.95 ± 1.24 to 8.05 ± 0.49 nm and a decrease in the interlayer spacing, accompanied by partial reorganization of the sp² carbon domains. The electrical properties were significantly improved, with enhanced carrier transport at higher oxidation temperatures. The optical band gap decreased from 4.11 to 3.69 eV, while the Urbach energy increased from 285 to 625 meV, indicating enhanced energetic disorder and band-tail formation. Electrochemical analysis revealed improved charge-transfer kinetics, with the charge-transfer resistance decreasing from 911 to 598 Ω and the relaxation time decreasing from 0.842 to 0.671 ms. The electrochemical response also showed a predominantly diffusion-controlled charge-storage contribution, while the apparent diffusion coefficient decreased from 2.094 × 10⁻⁷ to 5.792 × 10⁻⁸ cm²/s with increasing oxidation temperature. In contrast, the specific capacitance decreased from 668 to 328 F/g, which is attributed to the reduction of oxygen-containing redox-active sites and restricted ion accessibility. Despite the reduced capacitive performance, the capacitance retention improved from 84.25% to 95.84% after 6000 cycles. Overall, increasing oxidation temperature promotes electronic transport and electrochemical kinetics while reducing redox-based charge-storage capacity, demonstrating a clear trade-off between electronic conductivity, ion-transport behavior, and capacitive performance.
Related
- Ab-initio Exploration of Structural, Electronic, Optical and Transport Properties of Rb2Te Photocathodes
- Structural, electronic and antioxidant properties of curcuminato chelates with group IV oxo cations using density functional theory
- Novel Lead-free double perovskite Cs2LiFeBr6 as photovoltaics: a DFT study of structural, mechanical, spin-resolved electronic and optical properties
- First-Principles Calculations of Structural, Electronic, Optical, Vibrational, Dielectric, and Elastic Properties of Tetragonal Mg2TiO4 and Mg2TiO4:Mn4+
- DFT Studies of the Structural and Electronic Properties of Fluorinated and Methoxylated 3-Amino-2-CyclopropylQuinazolin-4(3H)-one Molecules
BibTeX
@article{ismail2026tuning,
title = {{Tuning structural, optical, charge storage, and electronic transport properties of graphene oxide through functional group engineering}},
author = {Walid Ismail and Ahmad G. Ramadan and Farah Abo El-khair and A. E. Elsheikh and Mahmoud Abdelfatah and Abdelhamid El-Shaer},
journal = {Scientific Reports},
year = {2026},
month = oct,
doi = {10.1038/s41598-026-71031-1},
url = {https://www.nature.com/articles/s41598-026-71031-1},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Tuning structural, optical, charge storage, and electronic transport properties of graphene oxide through functional group engineering
AU - Walid Ismail
AU - Ahmad G. Ramadan
AU - Farah Abo El-khair
AU - A. E. Elsheikh
AU - Mahmoud Abdelfatah
AU - Abdelhamid El-Shaer
PY - 2026
DA - 2026/10/04
JO - Scientific Reports
DO - 10.1038/s41598-026-71031-1
UR - https://www.nature.com/articles/s41598-026-71031-1
AB - This study investigates the effect of oxidation temperature on the structural, electronic, and electrochemical properties of graphene oxide (GO) synthesized at 75, 95, and 115 °C. Increasing the oxidation temperature resulted in a reduction in crystallite size from 9.95 ± 1.24 to 8.05 ± 0.49 nm and a decrease in the interlayer spacing, accompanied by partial reorganization of the sp² carbon domains. The electrical properties were significantly improved, with enhanced carrier transport at higher oxidation temperatures. The optical band gap decreased from 4.11 to 3.69 eV, while the Urbach energy increased from 285 to 625 meV, indicating enhanced energetic disorder and band-tail formation. Electrochemical analysis revealed improved charge-transfer kinetics, with the charge-transfer resistance decreasing from 911 to 598 Ω and the relaxation time decreasing from 0.842 to 0.671 ms. The electrochemical response also showed a predominantly diffusion-controlled charge-storage contribution, while the apparent diffusion coefficient decreased from 2.094 × 10⁻⁷ to 5.792 × 10⁻⁸ cm²/s with increasing oxidation temperature. In contrast, the specific capacitance decreased from 668 to 328 F/g, which is attributed to the reduction of oxygen-containing redox-active sites and restricted ion accessibility. Despite the reduced capacitive performance, the capacitance retention improved from 84.25% to 95.84% after 6000 cycles. Overall, increasing oxidation temperature promotes electronic transport and electrochemical kinetics while reducing redox-based charge-storage capacity, demonstrating a clear trade-off between electronic conductivity, ion-transport behavior, and capacitive performance.
SN - 2045-2322
ER -