Surface Hydrophobization of Glass Wool Fibers via Methyltrimethoxysilane Silanization for Polyethylene-Based Microplastic Filtration
- 1Afyon Kocatepe University , , Ahmet Necdet Sezer Campus , ,
Abstract
This study examines the surface modification of glass wool waste for the removal of polyethylene (PE) microplastics from aqueous suspensions. The modification strategy included sequential cleaning, pretreatment with NaOH at various concentrations (0.1, 0.5, and 1 M), and coating with methyltrimethoxysilane (MTMS) at various temperatures (room temperature (RT), 40, and 60 °C). The aim is to modify the surface properties of glass wool and evaluate its potential as a filtration medium. FTIR spectroscopy, scanning electron microscopy, contact angle measurements, and X-ray photoelectron spectroscopy (XPS) showed that alkaline pretreatment increases surface hydroxylation, facilitating effective silanization. The introduction of methyl groups resulted in a transition from hydrophilic to hydrophobic behavior, with contact angles for the modified samples exceeding 130°. XPS results showed an increase in surface carbon content, accompanied by decreases in oxygen and silicon signals, indicating the formation of an organosilane-based layer. Filtration experiments revealed that untreated glass wool exhibited unstable and limited microplastic retention, whereas the modified samples demonstrated significantly improved and more consistent results. Among the conditions tested, the best results were achieved with a combination of 1 M NaOH pretreatment and silanization at 60 °C, yielding low, stable turbidity values. The observed performance is attributed to the combined effect of enhanced hydrophobic interactions, increased surface roughness, and mechanical entrapment within the fibrous structure. Reusability tests showed that the modified material retained its microplastic-removal ability across multiple cycles, although some variability in performance was observed. Overall, this study demonstrates that an MTMS-based surface modification can improve the suitability of waste glass wool as a potential filtration medium for microplastic-containing suspensions.
Related
- Early‐Life Polyethylene Microplastic Exposure Exacerbates ADHD‐Like Behaviors in Mice via PI3K/AKT1/Nrf2 Signaling: Evidence From the Pilot Cohort and Multi‐Omics Analyses
- Toxicological Evaluations Following 28-Day Oral Gavage Exposure to Polyethylene Terephthalate Microplastic Particles in Mice
- Large Seasonal Variation in Microplastic Concentration from the Truckee River, United States
- Photocatalytic strategies for mitigating microplastic pollution and greenhouse gas emissions
- Coastal microplastic concentrations increase after Hurricanes Helene and Milton (2024)
BibTeX
@article{kurtulus2026surface,
title = {{Surface Hydrophobization of Glass Wool Fibers via Methyltrimethoxysilane Silanization for Polyethylene-Based Microplastic Filtration}},
author = {Cansu Kurtuluş and Ahmet Işık},
journal = {ACS Omega},
year = {2026},
month = oct,
doi = {10.1021/acsomega.6c05772},
url = {https://pubs.acs.org/acsodf/article/11/40/61152/5443461/Surface-Hydrophobization-of-Glass-Wool-Fibers-via},
note = {CC BY-NC-ND 4.0},
}
RIS
TY - JOUR
TI - Surface Hydrophobization of Glass Wool Fibers via Methyltrimethoxysilane Silanization for Polyethylene-Based Microplastic Filtration
AU - Cansu Kurtuluş
AU - Ahmet Işık
PY - 2026
DA - 2026/10/01
JO - ACS Omega
DO - 10.1021/acsomega.6c05772
UR - https://pubs.acs.org/acsodf/article/11/40/61152/5443461/Surface-Hydrophobization-of-Glass-Wool-Fibers-via
AB - This study examines the surface modification of glass wool waste for the removal of polyethylene (PE) microplastics from aqueous suspensions. The modification strategy included sequential cleaning, pretreatment with NaOH at various concentrations (0.1, 0.5, and 1 M), and coating with methyltrimethoxysilane (MTMS) at various temperatures (room temperature (RT), 40, and 60 °C). The aim is to modify the surface properties of glass wool and evaluate its potential as a filtration medium. FTIR spectroscopy, scanning electron microscopy, contact angle measurements, and X-ray photoelectron spectroscopy (XPS) showed that alkaline pretreatment increases surface hydroxylation, facilitating effective silanization. The introduction of methyl groups resulted in a transition from hydrophilic to hydrophobic behavior, with contact angles for the modified samples exceeding 130°. XPS results showed an increase in surface carbon content, accompanied by decreases in oxygen and silicon signals, indicating the formation of an organosilane-based layer. Filtration experiments revealed that untreated glass wool exhibited unstable and limited microplastic retention, whereas the modified samples demonstrated significantly improved and more consistent results. Among the conditions tested, the best results were achieved with a combination of 1 M NaOH pretreatment and silanization at 60 °C, yielding low, stable turbidity values. The observed performance is attributed to the combined effect of enhanced hydrophobic interactions, increased surface roughness, and mechanical entrapment within the fibrous structure. Reusability tests showed that the modified material retained its microplastic-removal ability across multiple cycles, although some variability in performance was observed. Overall, this study demonstrates that an MTMS-based surface modification can improve the suitability of waste glass wool as a potential filtration medium for microplastic-containing suspensions.
SN - 2470-1343
ER -