Effect of hot-pressing temperature on the structure and physico-mechanical properties of kapok fiber nonwoven mats.
- 1Universiti Kuala Lumpur, Malaysian Institute of Marine Engineering Technology (UniKL MIMET), Dataran Industri Teknologi Kejuruteraan Marin Bandar Teknologi Maritim Jalan Pantai Remis Lumut 32200 Perak Malaysia [email protected].
- 2Bangladesh Army University of Engineering & Technology Bangladesh.
Abstract
Kapok fiber (KF) has gained increasing attention due to its lightweight, hollow structure and lignocellulosic nature, with excellent buoyancy, thermal insulation, and sustainability characteristics. However, it presents significant challenges during the carding process and nonwoven mat formation owing to its short fiber length and poor cohesion. Limited studies have systematically investigated the effect of controlled hot-pressing temperature on binder-free KF nonwoven mats. Therefore, this study examines the influence of hot-pressing temperature (140, 150, 160, and 170 °C) on their physical and mechanical properties. The KF nonwoven mats were fabricated using an Ashford drum carder followed by hydraulic hot pressing. Increasing the hot-pressing temperature from 140 to 170 °C reduced Grammage (GSM) and thickness from 30.08 to 28.16 g m⁻² and 0.326 to 0.250 mm, respectively, while increasing density, tensile strength, and tensile modulus to 0.450 g cm⁻³, 50.76 MPa, and 6622.7 MPa, respectively, due to enhanced fiber consolidation. Among the tested conditions, 170 °C provided the highest mechanical performance and most effective fiber consolidation. Surface morphology was analyzed using a tabletop microscope and the results revealed a progressively more compact and smoother fiber structure at higher hot-pressing temperatures. Fourier transform infrared (FTIR) spectroscopy indicated a change in the intensity of hydroxyl (-OH) absorption bands with increasing temperature, suggesting partial thermal modification of the fiber surface. Moreover, tensile strength and tensile modulus increased with increasing hot-pressing temperature. A one-way analysis of variance (ANOVA) confirmed that hot-pressing temperature had a statistically significant effect on the physical and mechanical properties of the nonwoven mats. This work provides valuable insights into the sustainable utilization of KF and offers practical guidance for the industrial production of high-performance, eco-friendly nonwoven materials.
Related
- Assessment of Meltblown High-Temperature Polymers for Fluorine-Free Low-Grammage Nonwoven Structures
- Synergistic Effects of Mechanical Properties and Self-Healing in Borate-Based Hydrogen-Bond Dynamic Crosslinked Gels in High-Temperature Water-Based Drilling Fluids
- Processing of PVDF/Nb5+ and Sr2+-Doped PZT Composites for Applications in Advanced Dielectric Insulation: Effect of Ceramic Loading on Structure, Mechanical Properties, Electrical Properties, and Thermal Aging Behavior
- Influence of Lamella Structure on Mechanical Properties and Corrosion Resistance of AlCoCrFeNi2.1 Eutectic High-Entropy Alloy Fabricated by Laser-Based Directed Energy Deposition
- First-principles and cluster expansion investigation of Ti-V-Mn AB₂ alloys: stability, electronic structure, and mechanical properties.
BibTeX
@article{idrus2026effect,
title = {{Effect of hot-pressing temperature on the structure and physico-mechanical properties of kapok fiber nonwoven mats.}},
author = {M A M Mohd Idrus and Md Saiful Islam and Mohd Yuzri Mohd Yusop and Zulzamri Salleh},
journal = {RSC advances},
year = {2026},
month = oct,
doi = {10.1039/d6ra07101e},
url = {https://europepmc.org/article/MED/42910071},
note = {CC BY},
}
RIS
TY - JOUR
TI - Effect of hot-pressing temperature on the structure and physico-mechanical properties of kapok fiber nonwoven mats.
AU - M A M Mohd Idrus
AU - Md Saiful Islam
AU - Mohd Yuzri Mohd Yusop
AU - Zulzamri Salleh
PY - 2026
DA - 2026/10/21
JO - RSC advances
DO - 10.1039/d6ra07101e
UR - https://europepmc.org/article/MED/42910071
AB - Kapok fiber (KF) has gained increasing attention due to its lightweight, hollow structure and lignocellulosic nature, with excellent buoyancy, thermal insulation, and sustainability characteristics. However, it presents significant challenges during the carding process and nonwoven mat formation owing to its short fiber length and poor cohesion. Limited studies have systematically investigated the effect of controlled hot-pressing temperature on binder-free KF nonwoven mats. Therefore, this study examines the influence of hot-pressing temperature (140, 150, 160, and 170 °C) on their physical and mechanical properties. The KF nonwoven mats were fabricated using an Ashford drum carder followed by hydraulic hot pressing. Increasing the hot-pressing temperature from 140 to 170 °C reduced Grammage (GSM) and thickness from 30.08 to 28.16 g m⁻² and 0.326 to 0.250 mm, respectively, while increasing density, tensile strength, and tensile modulus to 0.450 g cm⁻³, 50.76 MPa, and 6622.7 MPa, respectively, due to enhanced fiber consolidation. Among the tested conditions, 170 °C provided the highest mechanical performance and most effective fiber consolidation. Surface morphology was analyzed using a tabletop microscope and the results revealed a progressively more compact and smoother fiber structure at higher hot-pressing temperatures. Fourier transform infrared (FTIR) spectroscopy indicated a change in the intensity of hydroxyl (-OH) absorption bands with increasing temperature, suggesting partial thermal modification of the fiber surface. Moreover, tensile strength and tensile modulus increased with increasing hot-pressing temperature. A one-way analysis of variance (ANOVA) confirmed that hot-pressing temperature had a statistically significant effect on the physical and mechanical properties of the nonwoven mats. This work provides valuable insights into the sustainable utilization of KF and offers practical guidance for the industrial production of high-performance, eco-friendly nonwoven materials.
SN - 2046-2069
ER -