Dual synergistic role of phosphorylated microcrystalline cellulose as organoinitiator and filler for PCL biocomposites
Abstract
In the present work, phosphorylated microcrystalline cellulose MCC@P was successfully prepared using phosphorus oxychloride (POCl 3 ) and employed both as an eco-friendly metal-free initiator for the ringopening polymerization (ROP) of 3-caprolactone (3-CL) and as an organic functional filler for the resulting biocomposites. Poly(3-caprolactone) (PCL) biocomposites were prepared under solvent-free conditions without the use of any metal catalyst. In this system, phosphorylated MCC serves a dual role. The phosphate groups associated with MCC participate in the initiation of 3-CL polymerization, while the remaining hydroxyl groups may serve as potential initiation and grafting sites, leading to the formation of MCC@P-g-PCL biocomposites. The prepared biocomposites were fully characterized using ( 31 P/ 13 C) nuclear magnetic resonance (NMR), Fourier transform infrared (FTIR), X-ray diffraction (XRD) and dynamic light scattering (DLS), and a suspension stability test to investigate the formation of the MCC@P-g-PCL biocomposites and provide complementary evidence supporting the proposed grafting of PCL onto MCC@P. The molecular-weight characteristics of the extracted free PCL fraction were determined by SEC, with M n values ranging from 8312 to 21 880 g mol -1 depending on the MCC@P content, while thermal stability of the prepared biocomposites was significantly enhanced compared to the neat PCL as demonstrated by the differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). For instance, the thermal degradation temperature at 30% (T d30% ) weight loss of MCC@Pg-PCL 1% reached 394 °C instead of 372 °C for PCL used as standard. The DSC results showed higher apparent crystallinity values for the MCC@P-g-PCL biocomposites than for neat PCL, with the highest value obtained for MCC@P-g-PCL 1% (64.8% versus 52.1% for neat PCL). The heat-release parameters measured by microscale combustion calorimetry were reduced for the MCC@P-g-PCL biocomposites, with the largest reduction in HRR observed for the 3 wt% formulation. Overall, these results highlight the potential of phosphorylated MCC as a metal-free initiating and functional-filler strategy for the development of PCL-based biocomposites with modified thermal and heat-release behavior.
Related
- Hierarchical microcrystalline cellulose/SeO2–MnO2/MWCNTs nanocomposite-based non-enzymatic electrochemical sensor for peroxide analysis in food and milk samples
- Synergistic Effects of Lignin Type and Polyethylene Glycol on the Structure Property Relationships of PLA/Lignin Biocomposites
- Selective fractionation and in situ synthesis of cellulose/calcium oxalate biocomposites from sugarcane bagasse using asymmetric Type 3 deep eutectic solvents.
- Biomaterial-Based Cu2O@Chitosan/Phosphorylated Cellulose Core–Shell Flame Retardant Fabricated via Layer-by-Layer Assembly for Enhanced Fire Safety of Epoxy Resin
- Water- and Alkali-Stable Cellulose Nanocrystal Films via Synergistic Citric Acid Cross-Linking and Poly(vinyl alcohol) Incorporation for Hydroxide-Conducting Membranes
BibTeX
@article{yachou2026dual,
title = {{Dual synergistic role of phosphorylated microcrystalline cellulose as organoinitiator and filler for PCL biocomposites}},
author = {Hassan Ait Yachou and El Hassan Boutriouia and Taha El Assimi and Sara Blilid and Abderrahim Maazouz and Hicham Ben Youcef and Khalid Lamnawar and Abdelkrim El Kadib and Mohammed Lahcini},
journal = {RSC Advances},
year = {2026},
month = sep,
doi = {10.1039/d6ra07997k},
url = {https://hal.science/hal-05787281v1},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Dual synergistic role of phosphorylated microcrystalline cellulose as organoinitiator and filler for PCL biocomposites
AU - Hassan Ait Yachou
AU - El Hassan Boutriouia
AU - Taha El Assimi
AU - Sara Blilid
AU - Abderrahim Maazouz
AU - Hicham Ben Youcef
AU - Khalid Lamnawar
AU - Abdelkrim El Kadib
AU - Mohammed Lahcini
PY - 2026
DA - 2026/09/30
JO - RSC Advances
DO - 10.1039/d6ra07997k
UR - https://hal.science/hal-05787281v1
AB - In the present work, phosphorylated microcrystalline cellulose MCC@P was successfully prepared using phosphorus oxychloride (POCl 3 ) and employed both as an eco-friendly metal-free initiator for the ringopening polymerization (ROP) of 3-caprolactone (3-CL) and as an organic functional filler for the resulting biocomposites. Poly(3-caprolactone) (PCL) biocomposites were prepared under solvent-free conditions without the use of any metal catalyst. In this system, phosphorylated MCC serves a dual role. The phosphate groups associated with MCC participate in the initiation of 3-CL polymerization, while the remaining hydroxyl groups may serve as potential initiation and grafting sites, leading to the formation of MCC@P-g-PCL biocomposites. The prepared biocomposites were fully characterized using ( 31 P/ 13 C) nuclear magnetic resonance (NMR), Fourier transform infrared (FTIR), X-ray diffraction (XRD) and dynamic light scattering (DLS), and a suspension stability test to investigate the formation of the MCC@P-g-PCL biocomposites and provide complementary evidence supporting the proposed grafting of PCL onto MCC@P. The molecular-weight characteristics of the extracted free PCL fraction were determined by SEC, with M n values ranging from 8312 to 21 880 g mol -1 depending on the MCC@P content, while thermal stability of the prepared biocomposites was significantly enhanced compared to the neat PCL as demonstrated by the differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). For instance, the thermal degradation temperature at 30% (T d30% ) weight loss of MCC@Pg-PCL 1% reached 394 °C instead of 372 °C for PCL used as standard. The DSC results showed higher apparent crystallinity values for the MCC@P-g-PCL biocomposites than for neat PCL, with the highest value obtained for MCC@P-g-PCL 1% (64.8% versus 52.1% for neat PCL). The heat-release parameters measured by microscale combustion calorimetry were reduced for the MCC@P-g-PCL biocomposites, with the largest reduction in HRR observed for the 3 wt% formulation. Overall, these results highlight the potential of phosphorylated MCC as a metal-free initiating and functional-filler strategy for the development of PCL-based biocomposites with modified thermal and heat-release behavior.
SN - 2046-2069
ER -