Fracture behaviour and structural integrity of hemp fibre reinforced composites for low load-bearing aerospace applications
4 affiliations
- 1Department of Mechanical Engineering, Dayananda Sagar Academy of Technology and Management, Bengaluru, 560082, Karnataka, India. [email protected]
- 2Department of Mechanical Engineering, Nitte Meenakshi Institute of Technology (NMIT), Nitte (Deemed to be University), Yelahanka, Bengaluru, 560064, Karnataka, India
- 3Department of Mechanical and Automobile Engineering, School of Engineering and Technology, CHRIST (Deemed to be University), Kengeri Campus, Bengaluru, 560074, Karnataka, India
- 4College of Engineering and Technology, Dilla University, Po. Box 419, Dilla, Ethiopia. [email protected]
Abstract
This paper presents a research undertaking on the mechanical performance of hemp fibre reinforced epoxy composites with special attention to tensile, flexural and impact behavior. The hand lay-up technique was used to produce laminates that were composed of different proportions of hemp fibres within the range between 25 wt% and 45 wt% in an epoxy base. The findings showed that composites with 35 wt% hemp fibre had the most balanced mechanical performance. This structure was found to have tensile strength of 67.3 MPa, tensile modulus of 2.85 GPa and an elongation at break of 5.2%, which is the best combination of strength and ductility. Flexural properties were no different and similarly, the 35 wt% hemp fibre reinforced composite showed better performance viz., a flexural strength of 99.7 MPa and flexural modulus of 3.9 GPa. Impact resistance, measured under the charpy test, was 9.4 kJ/m2 for the same composition (35 wt% hemp fibre) indicating better energy absorption ability. The observed improvement in the mechanical behaviour at 35 wt% fibre loading is due to the enhancement in the fibre-matrix contact and efficient stress transfer of the composite structure. These results define an improved reinforcement level that yields further performance improvements because of the potential agglomeration of fibres or loss of matrix continuity. The novelty of this work lies in the determination of the optimum loading of hemp fibre, which maximizes the strength, stiffness, and toughness, resulting in a balanced performance profile, optimized to work in structurally-lightweight applications. Further, the findings demonstrate the possibility of hemp fibre as a viable green reinforcement in semi-structural uses of hemp fibre in automotive body panels, lightweight construction, and framework structures.
Related
- Mechanical, ballistic, and dynamic behaviour of rGO-reinforced kevlar–basalt/epoxy hybrid composites for lightweight engineering applications
- Development and multi-response optimization of sustainable hemp fibre/cassia gum reinforced polyester hybrid composites for structural and insulation applications
- Synergistic Absorption Mechanism in Flexible Polymer Composites Reinforced with Rare Earth Cobaltite and Molybdenum Carbide for EMI Shielding Applications
- Development of hybrid polypropylene composites reinforced with chemically modified rice straw and foxtail millet husk for EV automotive applications
- Evaluation of Woven Hemp-Reinforced Polyfurfuryl Alcohol Resin Composites for High-Performance Natural Fibre Composite Applications
BibTeX
@article{nagaraja2026fracture,
title = {{Fracture behaviour and structural integrity of hemp fibre reinforced composites for low load-bearing aerospace applications}},
author = {Santhosh Nagaraja and B. A. Praveena and K. Ramesha and Addisu Frinjo Emma},
journal = {Scientific Reports},
year = {2026},
month = jun,
doi = {10.1038/s41598-026-44443-2},
url = {https://doi.org/10.1038/s41598-026-44443-2},
note = {CC BY-NC-ND},
}
RIS
TY - JOUR
TI - Fracture behaviour and structural integrity of hemp fibre reinforced composites for low load-bearing aerospace applications
AU - Santhosh Nagaraja
AU - B. A. Praveena
AU - K. Ramesha
AU - Addisu Frinjo Emma
PY - 2026
DA - 2026/06/03
JO - Scientific Reports
DO - 10.1038/s41598-026-44443-2
UR - https://doi.org/10.1038/s41598-026-44443-2
AB - This paper presents a research undertaking on the mechanical performance of hemp fibre reinforced epoxy composites with special attention to tensile, flexural and impact behavior. The hand lay-up technique was used to produce laminates that were composed of different proportions of hemp fibres within the range between 25 wt% and 45 wt% in an epoxy base. The findings showed that composites with 35 wt% hemp fibre had the most balanced mechanical performance. This structure was found to have tensile strength of 67.3 MPa, tensile modulus of 2.85 GPa and an elongation at break of 5.2%, which is the best combination of strength and ductility. Flexural properties were no different and similarly, the 35 wt% hemp fibre reinforced composite showed better performance viz., a flexural strength of 99.7 MPa and flexural modulus of 3.9 GPa. Impact resistance, measured under the charpy test, was 9.4 kJ/m2 for the same composition (35 wt% hemp fibre) indicating better energy absorption ability. The observed improvement in the mechanical behaviour at 35 wt% fibre loading is due to the enhancement in the fibre-matrix contact and efficient stress transfer of the composite structure. These results define an improved reinforcement level that yields further performance improvements because of the potential agglomeration of fibres or loss of matrix continuity. The novelty of this work lies in the determination of the optimum loading of hemp fibre, which maximizes the strength, stiffness, and toughness, resulting in a balanced performance profile, optimized to work in structurally-lightweight applications. Further, the findings demonstrate the possibility of hemp fibre as a viable green reinforcement in semi-structural uses of hemp fibre in automotive body panels, lightweight construction, and framework structures.