Effects of thermocycling on color stability and mechanical properties of universal resin composites: an in vitro comparison.
- 1Dental Materials Division, Department of Restorative Dentistry, Piracicaba Dental School, State University of Campinas (FOP/UNICAMP), Av. Limeira, 901, Piracicaba, São Paulo, 13414-903, Brazil. [email protected].
- 2Dental Materials Division, Department of Restorative Dentistry, Piracicaba Dental School, State University of Campinas (FOP/UNICAMP), Av. Limeira, 901, Piracicaba, São Paulo, 13414-903, Brazil.
Abstract
Objectives
To evaluate the effect of thermocycling on the optical and mechanical properties of universal resin composites, with emphasis on color stability, Knoop microhardness, flexural strength, flexural modulus, and filler characteristics.Methods
Four composite resins: Filtek Z250 XT (FZ), Vittra APS Unique (VT), Spectra Smart (SS), and Harmonize (HZ) were evaluated (n = 10 per group). Specimens were subjected to thermocycling (10,000 cycles; 5-55 °C). Color and Knoop microhardness were measured before and after aging (repeated measures), while flexural strength and modulus were determined using independent specimens. Color differences were calculated using the CIEDE2000 formula. SEM/EDS analyses were performed for filler characterization. Statistical significance was set at α = 0.05.Results
Thermocycling significantly affected all evaluated properties (p < 0.05), with a material-dependent response. All materials exhibited ΔE₀₀ values above clinically acceptable thresholds after aging. SS showed the lowest color variation, while VT presented the highest values. In terms of mechanical behavior, FZ and HZ exhibited greater reductions in flexural strength (> 50%) and microhardness (≈ 30-45%), whereas SS demonstrated the highest stability and VT showed intermediate performance. Additionally, FZ and HZ presented flexural strength values below 80 MPa after thermocycling.Conclusions
Thermocycling resulted in clinically relevant color changes in all evaluated universal resin composites, exceeding perceptibility and acceptability thresholds. Additionally, mechanical properties were adversely affected in a material-dependent manner, with reductions in flexural strength and microhardness suggesting decreased structural stability after aging.Clinical significance
Universal resin composites may exhibit clinically relevant color changes and significant mechanical degradation after aging. Clinicians should consider that materials with greater reductions in flexural strength and microhardness may present reduced durability over time.
Related
- Fracture resistance and color stability of monolithic CAD/CAM crowns: effect of occlusal thickness and thermocycling
- Mechanical stability of endotracheal tube fixation: a performance comparison between two tube holders and a conventional method.
- Effects of keiser-assisted Nordic hamstring curl training on hamstring flexibility, mechanical properties, and pitching performance in high school baseball pitchers
- Mechanical properties of completely autologous human tissue engineered blood vessels compared to human saphenous vein and mammary artery
- Strategies of mechanical adaptations of circulating tumor cells and properties of their cellular microenvironment have predictive and prognostic biomarker value
BibTeX
@article{souza2026effects,
title = {{Effects of thermocycling on color stability and mechanical properties of universal resin composites: an in vitro comparison.}},
author = {Alana Pinto Caroso Souza and Wilton Lima Dos Santos and Camila Ribeiro Silva and Anderson Gomes Forte and Fernanda Midori Tsuzuki-Gorham and Américo Bortolazzo Correr},
journal = {BMC oral health},
year = {2026},
month = jul,
doi = {10.1186/s12903-026-08987-z},
url = {https://europepmc.org/article/MED/42919273},
note = {CC BY},
}
RIS
TY - JOUR
TI - Effects of thermocycling on color stability and mechanical properties of universal resin composites: an in vitro comparison.
AU - Alana Pinto Caroso Souza
AU - Wilton Lima Dos Santos
AU - Camila Ribeiro Silva
AU - Anderson Gomes Forte
AU - Fernanda Midori Tsuzuki-Gorham
AU - Américo Bortolazzo Correr
PY - 2026
DA - 2026/07/01
JO - BMC oral health
DO - 10.1186/s12903-026-08987-z
UR - https://europepmc.org/article/MED/42919273
AB - Objectives To evaluate the effect of thermocycling on the optical and mechanical properties of universal resin composites, with emphasis on color stability, Knoop microhardness, flexural strength, flexural modulus, and filler characteristics.Methods Four composite resins: Filtek Z250 XT (FZ), Vittra APS Unique (VT), Spectra Smart (SS), and Harmonize (HZ) were evaluated (n = 10 per group). Specimens were subjected to thermocycling (10,000 cycles; 5-55 °C). Color and Knoop microhardness were measured before and after aging (repeated measures), while flexural strength and modulus were determined using independent specimens. Color differences were calculated using the CIEDE2000 formula. SEM/EDS analyses were performed for filler characterization. Statistical significance was set at α = 0.05.Results Thermocycling significantly affected all evaluated properties (p < 0.05), with a material-dependent response. All materials exhibited ΔE₀₀ values above clinically acceptable thresholds after aging. SS showed the lowest color variation, while VT presented the highest values. In terms of mechanical behavior, FZ and HZ exhibited greater reductions in flexural strength (> 50%) and microhardness (≈ 30-45%), whereas SS demonstrated the highest stability and VT showed intermediate performance. Additionally, FZ and HZ presented flexural strength values below 80 MPa after thermocycling.Conclusions Thermocycling resulted in clinically relevant color changes in all evaluated universal resin composites, exceeding perceptibility and acceptability thresholds. Additionally, mechanical properties were adversely affected in a material-dependent manner, with reductions in flexural strength and microhardness suggesting decreased structural stability after aging.Clinical significance Universal resin composites may exhibit clinically relevant color changes and significant mechanical degradation after aging. Clinicians should consider that materials with greater reductions in flexural strength and microhardness may present reduced durability over time.
SN - 1472-6831
ER -