Engineering ZnTe thin films by thermal control for bandgap tuning and improved CdTe solar cell performance
- 1Bangladesh Council of Scientific and Industrial Research (BCSIR), Dhaka, 1205, Bangladesh
- 2Corresponding author.
Abstract
The study discusses a thorough experimental analysis on RF-sputtered ZnTe thin films prepared with different substrate temperatures in the range of room temperature up to 300 °C at a constant pressure of 5 mTorr and RF power of 30 W. Substrate temperature was established as a thermal design variable controlling the transition of the deposited thin film from Te-rich amorphous to polycrystalline ZnTe film. All films were maintained at a thickness of approximately 85-90 nm. Raman spectroscopy of the 300 °C film confirmed four characteristic vibrational peaks at 121, 142, 210, and 420 cm −1 , with a Zn/Te ratio of 45:55, close to the ideal stoichiometry. Increasing substrate temperature progressively improved crystallinity, enhanced p -type electrical conductivity with a bulk carrier concentration of 2.49 × 10 15 cm −3 , and tuned the direct optical bandgap from 3.04 eV (RT) to 3.39 eV (300 °C), accompanied by a reduction in Urbach energy to 0.58 eV and peak carrier mobility of 2.31 × 10 3 cm 2 V −1 s −1 . The film at 300 °C was determined to be the optimized thermal design point and was used as an interface layer in a CdTe solar cell architecture. Device characterization under illumination revealed that the ZnTe interlayer improved the V oc from 0.538 V to 0.546 V, fill factor from 30.47% to 33.20% and power conversion efficiency from 4.74% to 5.98% over an active area of 0.203 cm 2 . These results demonstrate that thermally engineered ZnTe is a viable undoped interface material for improving the performance of CdTe-based photovoltaics.
Related
- Flow-Induced Structuring of Polypropylene-Based Composites for Improved Mechanical and Thermal Performance
- Reversible control of thermal conductivity via electric field-driven domain engineering in barium titanate ceramics
- Bandgap engineering of CuGaS2–CuInS2 heterostructures for efficient thin-film photovoltaics
- Emergence of Glass-like Thermal Transport through Anion-Engineering in Complex Silver Gallium Germanium Chalcogenides
- Nano-Based Advanced Thermoelectric Design: Materials Engineering and Thermal Management Applications
BibTeX
@article{sharmin2026engineering,
title = {{Engineering ZnTe thin films by thermal control for bandgap tuning and improved CdTe solar cell performance}},
author = {Afrina Sharmin and Munira Sultana and Nusrat Zahan and Sharmin Jahan and Muhammad Shahriar Bashar},
journal = {Results in Surfaces and Interfaces},
year = {2026},
month = nov,
doi = {10.1016/j.rsurfi.2026.101037},
url = {https://doi.org/10.1016/j.rsurfi.2026.101037},
note = {CC BY},
}
RIS
TY - JOUR
TI - Engineering ZnTe thin films by thermal control for bandgap tuning and improved CdTe solar cell performance
AU - Afrina Sharmin
AU - Munira Sultana
AU - Nusrat Zahan
AU - Sharmin Jahan
AU - Muhammad Shahriar Bashar
PY - 2026
DA - 2026/11/08
JO - Results in Surfaces and Interfaces
DO - 10.1016/j.rsurfi.2026.101037
UR - https://doi.org/10.1016/j.rsurfi.2026.101037
AB - The study discusses a thorough experimental analysis on RF-sputtered ZnTe thin films prepared with different substrate temperatures in the range of room temperature up to 300 °C at a constant pressure of 5 mTorr and RF power of 30 W. Substrate temperature was established as a thermal design variable controlling the transition of the deposited thin film from Te-rich amorphous to polycrystalline ZnTe film. All films were maintained at a thickness of approximately 85-90 nm. Raman spectroscopy of the 300 °C film confirmed four characteristic vibrational peaks at 121, 142, 210, and 420 cm −1 , with a Zn/Te ratio of 45:55, close to the ideal stoichiometry. Increasing substrate temperature progressively improved crystallinity, enhanced p -type electrical conductivity with a bulk carrier concentration of 2.49 × 10 15 cm −3 , and tuned the direct optical bandgap from 3.04 eV (RT) to 3.39 eV (300 °C), accompanied by a reduction in Urbach energy to 0.58 eV and peak carrier mobility of 2.31 × 10 3 cm 2 V −1 s −1 . The film at 300 °C was determined to be the optimized thermal design point and was used as an interface layer in a CdTe solar cell architecture. Device characterization under illumination revealed that the ZnTe interlayer improved the V oc from 0.538 V to 0.546 V, fill factor from 30.47% to 33.20% and power conversion efficiency from 4.74% to 5.98% over an active area of 0.203 cm 2 . These results demonstrate that thermally engineered ZnTe is a viable undoped interface material for improving the performance of CdTe-based photovoltaics.
SN - 2666-8459
ER -