Flow-Rate-Controlled Agglomeration and Ambient Oxide Phase Characteristics of Spark-Ablated Copper Nanoparticles
- 1Novel Materials Development Laboratory, SAFIR (Sorbonne Abu Dhabi for Innovation and Research Institute), Sorbonne University Abu Dhabi, Abu Dhabi P.O. Box 38044, United Arab Emirates
- 2Plateforme MACLE-CVL (Microscopies, Imageries et Ressources Analytiques en Région Centre-Val de Loire), UAR 2590 (Unité d’Appui et de Recherche), 1b, Rue de la Férollerie, 45071 Orléans Cedex 2, France
- 3GREMAN (Groupe de Recherche en Matériaux, Microélectronique, Acoustique, Nanotechnologies), UMR (Unité Mixte de Recherche) 7347–CNRS (Centre National de la Recherche Scientifique), IUT de Blois, University of Tours, 15 Rue de la Chocolaterie, 41029 Blois, France
Abstract
Spark ablation is an attractive gas-phase route for producing ligand-free metal nanoparticles, yet control over agglomeration and phase evolution during deposition remains challenging. The influence of carrier gas flow rate and deposition time on the agglomerate morphology, size distribution, and oxidation behavior of copper nanoparticles deposited onto silicon and glass substrates is investigated. Copper nanoparticles were generated by spark discharge and transported by nitrogen (N2) carrier gas under flow rates ranging from 0.5 to 3.5 L min−1 prior to deposition onto silicon substrates for 2 h and 5 h. Scanning electron microscopy reveals a transition from compact, isotropic agglomerates at low flow rates to elongated, chain-like structures at higher flow rates, indicating a shift from coalescence- and restructuring-favored conditions toward increasingly kinetically constrained aggregation. Transmission electron microscopy reveals predominantly spherical nanoparticles with a lognormal size distribution centered at approximately 10 nm, consistent with gas-phase nucleation and coalescence. Structural and spectroscopic analyses suggest CuO as the dominant oxide phase with minor Cu2O contributions, with Raman spectroscopy providing the primary evidence due to limitations in high-resolution TEM analysis from substrate effects and peak overlap. These findings show that carrier-gas flow rate systematically influences agglomerate structure under the investigated conditions, while oxidation may occur both during aerosol transport and following ambient exposure; the present measurements do not allow the relative contributions of these processes to be quantitatively separated.
Related
- Biocomposite Microparticles Incorporating Ibuprofen and ZnO Nanoparticles for Controlled Drug Delivery and Antimicrobial Therapy
- Controlled Aggregation of Citrate-Stabilized Gold Nanoparticles into Long-Lived Metastable Clusters.
- Controlled Decoration of Electrochemically Exfoliated Graphene with Gold Nanoparticles for Electrocatalysis and Sensing
- Controlled Pt doping of silica-supported Ni nanoparticles through surface organometallic chemistry on metals: application as catalysts for selective hydrogenation reactions
- pH-controlled reversible assembly of magnetic and plasmonic nanoparticles on gold nanorods
BibTeX
@article{elrifai2026flowratecontrolled,
title = {{Flow-Rate-Controlled Agglomeration and Ambient Oxide Phase Characteristics of Spark-Ablated Copper Nanoparticles}},
author = {Joumana El-Rifai and Eliane Bsaibess and Diaa Mereib and Corinne Bouillet and Mustapha Zaghrioui},
journal = {Nanomaterials (Basel, Switzerland)},
year = {2026},
month = oct,
doi = {10.3390/nano16191270},
url = {https://europepmc.org/article/PMC/PMC13667034},
note = {CC BY},
}
RIS
TY - JOUR
TI - Flow-Rate-Controlled Agglomeration and Ambient Oxide Phase Characteristics of Spark-Ablated Copper Nanoparticles
AU - Joumana El-Rifai
AU - Eliane Bsaibess
AU - Diaa Mereib
AU - Corinne Bouillet
AU - Mustapha Zaghrioui
PY - 2026
DA - 2026/10/01
JO - Nanomaterials (Basel, Switzerland)
DO - 10.3390/nano16191270
UR - https://europepmc.org/article/PMC/PMC13667034
AB - Spark ablation is an attractive gas-phase route for producing ligand-free metal nanoparticles, yet control over agglomeration and phase evolution during deposition remains challenging. The influence of carrier gas flow rate and deposition time on the agglomerate morphology, size distribution, and oxidation behavior of copper nanoparticles deposited onto silicon and glass substrates is investigated. Copper nanoparticles were generated by spark discharge and transported by nitrogen (N2) carrier gas under flow rates ranging from 0.5 to 3.5 L min−1 prior to deposition onto silicon substrates for 2 h and 5 h. Scanning electron microscopy reveals a transition from compact, isotropic agglomerates at low flow rates to elongated, chain-like structures at higher flow rates, indicating a shift from coalescence- and restructuring-favored conditions toward increasingly kinetically constrained aggregation. Transmission electron microscopy reveals predominantly spherical nanoparticles with a lognormal size distribution centered at approximately 10 nm, consistent with gas-phase nucleation and coalescence. Structural and spectroscopic analyses suggest CuO as the dominant oxide phase with minor Cu2O contributions, with Raman spectroscopy providing the primary evidence due to limitations in high-resolution TEM analysis from substrate effects and peak overlap. These findings show that carrier-gas flow rate systematically influences agglomerate structure under the investigated conditions, while oxidation may occur both during aerosol transport and following ambient exposure; the present measurements do not allow the relative contributions of these processes to be quantitatively separated.