Effect of Al-Zn alloy wafer grain boundary diffusion on the magnetism and microstructure of sintered NdFeB magnets
Abstract
This study investigates Al-Zn grain boundary diffusion (GBD) treatment on sintered Nd-Fe-B magnets using Al80Zn20 alloy sheets as the diffusion source. The alloy sheets were placed at both ends of cylindrical samples and diffusion-annealed at 900∘C and 700∘C for 7 hours under vacuum (≤5×10−3 Pa), followed by tempering at 500∘C for 2 hours. Magnetic measurements show that coercivity increases from 951.5kA/m in the untreated sample to 1158.2kA/m at 900∘C (a gain of 206.7kA/m, 21.7\%) and to 1039.6kA/m at 700∘C (a gain of 88.1kA/m, 9.3\%), while remanence declines modestly from 1282mT to 1256mT after the high-temperature treatment. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffractometer (XRD) analyses reveal that the 900∘C treatment produces a thinner, more continuous grain boundary phase and a distinct core-shell structure around the main-phase grains. EDS mapping shows that Al preferentially enriches the shell region of the Nd2Fe14B grains, while Zn predominantly resides in the grain boundary phase, where it lowers the melting point of the intergranular phase and improves its fluidity. XRD shows no detectable secondary phases, while the combined XRD, EDS results, and lattice expansion are consistent with possible limited Al incorporation into the main-phase lattice. Verified by computational analysis, the coercivity enhancement is attributed to three synergistic factors: improved grain boundary decoupling, the formation of a high-anisotropy shell layer that strengthens domain-wall pinning, and the smoothing of grain edges to suppress reverse-domain nucleation.
Related
- Purely Electric-Field Control of Topological Magnetism in Two-Dimensional Magnets
- Fiber-Resolved Microstructure Quantification from Multi-Shell Diffusion MRI using Detection Transformers
- Imaging cellular-level brain microstructure with diffusion MRI
- General boundary conditions for the quasiclassical kinetic equations in the presence of magnetism and unconventional superconductivity
- A quantitative phase-field model for grain boundary trapping and diffusion of hydrogen
BibTeX
@misc{liu2026effect,
title = {{Effect of Al-Zn alloy wafer grain boundary diffusion on the magnetism and microstructure of sintered NdFeB magnets}},
author = {Xi Liu and Wenxi Fang and Ken Perlin},
howpublished = {arXiv},
year = {2026},
month = oct,
doi = {10.48550/arxiv.2607.21870},
eprint = {2607.21870},
archivePrefix = {arXiv},
url = {https://arxiv.org/abs/2607.21870},
note = {CC BY 4.0},
}
RIS
TY - UNPB
TI - Effect of Al-Zn alloy wafer grain boundary diffusion on the magnetism and microstructure of sintered NdFeB magnets
AU - Xi Liu
AU - Wenxi Fang
AU - Ken Perlin
PY - 2026
DA - 2026/10/11
PB - arXiv
DO - 10.48550/arxiv.2607.21870
UR - https://arxiv.org/abs/2607.21870
AB - This study investigates Al-Zn grain boundary diffusion (GBD) treatment on sintered Nd-Fe-B magnets using Al_80Zn_20 alloy sheets as the diffusion source. The alloy sheets were placed at both ends of cylindrical samples and diffusion-annealed at 900^∘C and 700^∘C for 7 hours under vacuum (≤5×10^−3 Pa), followed by tempering at 500^∘C for 2 hours. Magnetic measurements show that coercivity increases from 951.5kA/m in the untreated sample to 1158.2kA/m at 900^∘C (a gain of 206.7kA/m, 21.7\%) and to 1039.6kA/m at 700^∘C (a gain of 88.1kA/m, 9.3\%), while remanence declines modestly from 1282mT to 1256mT after the high-temperature treatment. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffractometer (XRD) analyses reveal that the 900^∘C treatment produces a thinner, more continuous grain boundary phase and a distinct core-shell structure around the main-phase grains. EDS mapping shows that Al preferentially enriches the shell region of the Nd_2Fe_14B grains, while Zn predominantly resides in the grain boundary phase, where it lowers the melting point of the intergranular phase and improves its fluidity. XRD shows no detectable secondary phases, while the combined XRD, EDS results, and lattice expansion are consistent with possible limited Al incorporation into the main-phase lattice. Verified by computational analysis, the coercivity enhancement is attributed to three synergistic factors: improved grain boundary decoupling, the formation of a high-anisotropy shell layer that strengthens domain-wall pinning, and the smoothing of grain edges to suppress reverse-domain nucleation.
ER -