Energy-dependent underwater abrasion behavior of sustainable lightweight concrete incorporating agro-waste aggregates and natural fibers under rotational hydraulic conditions
Abstract
Lightweight aggregate concrete has become a popular material in hydraulic engineering and coastal and offshore engineering, and understanding its durability under underwater rotational abrasion is critical. Comparative studies on the abrasion resistance of several agricultural waste aggregates under high-energy underwater conditions have been conducted for the production of sustainable concrete; however, such studies are still scarce, especially considering the combined effects of rotational speed, abrasion time, aggregate properties, and properties of the interfacial transition zone between the aggregate and cement matrix. This study aims to fill this research gap by comparing conventional concrete with lightweight aggregate concrete using coconut shell, expanded clay aggregate, oil palm shell, and areca nut shell aggregates with natural fibers (hemp, jute, and coir) under underwater rotational abrasion. Abrasion tests were conducted at 1200 rpm and 1600 rpm to investigate the influence of exposure time, abrasion energy, and aggregate nature on the abrasion resistance. Findings indicated that the Abrasion loss increased linearly with exposure time, confirming cumulative mechanical erosion. After 6 h at 1600 rpm, weight loss increased from 461.93 g for conventional concrete to 549.44–698.91 g for lightweight concretes. Wear rate ranged from 23.35–38.80 g/h (1200 rpm) and 55.42–116.49 g/h (1600 rpm), while weight loss ratio varied between 1.78 and 2.60. Among lightweight mixtures, palm oil shell-hemp fiber exhibited the lowest speed sensitivity and the most stable abrasion performance under severe underwater conditions.
Related
- A lightweight underwater biological object detector with enhanced cross-scale feature interaction
- Mechanical performance and water penetration resistance of two-stage concrete incorporating recycled aggregates from demolition waste
- PAUNet: A Lightweight Network for Real-Time Underwater Image Enhancement.
- A Lightweight Channel-Frequency Joint Attention Network for Underwater Ship-Radiated Noise Separation.
- Editorial Note: Predicting corporate management performance using AI: Incorporating CEO strategy insights from sustainable management reports
BibTeX
@article{kumar2026energydependent,
title = {{Energy-dependent underwater abrasion behavior of sustainable lightweight concrete incorporating agro-waste aggregates and natural fibers under rotational hydraulic conditions}},
author = {A. Hemanth Kumar and K. Karthikeyan and G. Murali},
journal = {Scientific Reports},
year = {2026},
month = oct,
doi = {10.1038/s41598-026-72514-x},
url = {https://www.nature.com/articles/s41598-026-72514-x},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Energy-dependent underwater abrasion behavior of sustainable lightweight concrete incorporating agro-waste aggregates and natural fibers under rotational hydraulic conditions
AU - A. Hemanth Kumar
AU - K. Karthikeyan
AU - G. Murali
PY - 2026
DA - 2026/10/11
JO - Scientific Reports
DO - 10.1038/s41598-026-72514-x
UR - https://www.nature.com/articles/s41598-026-72514-x
AB - Lightweight aggregate concrete has become a popular material in hydraulic engineering and coastal and offshore engineering, and understanding its durability under underwater rotational abrasion is critical. Comparative studies on the abrasion resistance of several agricultural waste aggregates under high-energy underwater conditions have been conducted for the production of sustainable concrete; however, such studies are still scarce, especially considering the combined effects of rotational speed, abrasion time, aggregate properties, and properties of the interfacial transition zone between the aggregate and cement matrix. This study aims to fill this research gap by comparing conventional concrete with lightweight aggregate concrete using coconut shell, expanded clay aggregate, oil palm shell, and areca nut shell aggregates with natural fibers (hemp, jute, and coir) under underwater rotational abrasion. Abrasion tests were conducted at 1200 rpm and 1600 rpm to investigate the influence of exposure time, abrasion energy, and aggregate nature on the abrasion resistance. Findings indicated that the Abrasion loss increased linearly with exposure time, confirming cumulative mechanical erosion. After 6 h at 1600 rpm, weight loss increased from 461.93 g for conventional concrete to 549.44–698.91 g for lightweight concretes. Wear rate ranged from 23.35–38.80 g/h (1200 rpm) and 55.42–116.49 g/h (1600 rpm), while weight loss ratio varied between 1.78 and 2.60. Among lightweight mixtures, palm oil shell-hemp fiber exhibited the lowest speed sensitivity and the most stable abrasion performance under severe underwater conditions.
SN - 2045-2322
ER -