Rheological Control of Microsphere Expansion and Cellular Stabilization in Styrene–Butadiene–Styrene Foams
- 1Polymer Materials Engineering Department, Faculty of Engineering, Yalova University, 77100 Yalova, Turkey
- 2Polyshield Engineering Consultancy and R&D Co., 77100 Yalova, Turkey
Abstract
Lightweight elastomeric foams for footwear, sealing and damping applications require substantial density reduction without loss of cellular stability, yet the role of matrix rheology in expandable-microsphere foaming of oil-extended thermoplastic elastomers remains insufficiently understood. Herein, styrene–butadiene–styrene (SBS) foams were prepared with 1–3 phr thermally expandable microspheres, 10–30 phr additional processing oil and three nominal densities (0.80, 0.65 and 0.45 g cm−3). Increasing oil content reduced matrix elastic and flow resistance by approximately 2–3-fold and increased the mean pore size from 25.2 to 49.6 µm under the intermediate-density condition. Under the lowest-density condition, however, excessive softening reduced cellular stability, raising the pore-size coefficient of variation to 49.7% for LD-30-3. Combined optical microscopy and dielectric measurements showed that larger pores at comparable density did not necessarily correspond to a higher bulk void fraction, while the permittivity response was consistent with a predominantly discrete closed-cell structure. Greater pore expansion did not coincide with maximum mechanical performance: the highest mean toughness (11.50 MJ m−3) was obtained for HD-10-3. Cyclic testing showed that increasing oil content reduced load-bearing capacity but nearly doubled conditioned damping (from approximately 3–4% to 6–7%). Overall, matrix rheological resistance can be used to balance microsphere expansion, cellular retention and function-specific performance in lightweight SBS foams.
Related
- E-Waste Acrylonitrile–Butadiene–Styrene (ABS) Upcycling via Low-Dose Electron Beam Irradiation (EBI) and Halloysite Nanotubes (HNTs): A Circular Approach
- The structure of gauche-1,3-butadiene: Further insights from the centimeter-wave, millimeter-wave, and far-infrared high resolution spectra
- Experimental and Theoretical Evaluation of Notch Strength in MEX-Printed Acrylonitrile Butadiene Styrene Under Symmetrical Three-Point Bending
- Magnetron Sputtering of Conformal Tungsten and Copper Coatings onto Glass Microsphere Powder via Agitation
- Unraveling Two Nonlinear Rheological Peaks in Filled Rubber: Chain-Arm Retraction and Bound-Rubber Dynamics
BibTeX
@article{cinar2026rheological,
title = {{Rheological Control of Microsphere Expansion and Cellular Stabilization in Styrene–Butadiene–Styrene Foams}},
author = {Ahmet Hakan Cinar and Zeynep Keskin and Furkan Sarisoy and Gökçe Yilmaz and Zuhal Yurtbasi and Emine Kasgoz and Alper Kasgoz},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18212696},
url = {https://www.mdpi.com/2073-4360/18/21/2696},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Rheological Control of Microsphere Expansion and Cellular Stabilization in Styrene–Butadiene–Styrene Foams
AU - Ahmet Hakan Cinar
AU - Zeynep Keskin
AU - Furkan Sarisoy
AU - Gökçe Yilmaz
AU - Zuhal Yurtbasi
AU - Emine Kasgoz
AU - Alper Kasgoz
PY - 2026
DA - 2026/10/31
JO - Polymers
DO - 10.3390/polym18212696
UR - https://www.mdpi.com/2073-4360/18/21/2696
AB - Lightweight elastomeric foams for footwear, sealing and damping applications require substantial density reduction without loss of cellular stability, yet the role of matrix rheology in expandable-microsphere foaming of oil-extended thermoplastic elastomers remains insufficiently understood. Herein, styrene–butadiene–styrene (SBS) foams were prepared with 1–3 phr thermally expandable microspheres, 10–30 phr additional processing oil and three nominal densities (0.80, 0.65 and 0.45 g cm−3). Increasing oil content reduced matrix elastic and flow resistance by approximately 2–3-fold and increased the mean pore size from 25.2 to 49.6 µm under the intermediate-density condition. Under the lowest-density condition, however, excessive softening reduced cellular stability, raising the pore-size coefficient of variation to 49.7% for LD-30-3. Combined optical microscopy and dielectric measurements showed that larger pores at comparable density did not necessarily correspond to a higher bulk void fraction, while the permittivity response was consistent with a predominantly discrete closed-cell structure. Greater pore expansion did not coincide with maximum mechanical performance: the highest mean toughness (11.50 MJ m−3) was obtained for HD-10-3. Cyclic testing showed that increasing oil content reduced load-bearing capacity but nearly doubled conditioned damping (from approximately 3–4% to 6–7%). Overall, matrix rheological resistance can be used to balance microsphere expansion, cellular retention and function-specific performance in lightweight SBS foams.
SN - 2073-4360
ER -