Effect of Scrap Configuration on the Tensile and Flexural Properties of Grinding-Free Recycled CF/PA6 Composites
- 1Federal University of São Paulo (UNIFESP) , , 330 Talim St. , ,
- 2Federal University of São Carlos (UFSCar) , , Rod. Washington Luiz, Km 235 , ,
- 3Coordination of Applied Research and Technological Development (COPDT) , , 1758 Astronautas Avenue , ,
Abstract
The increasing demand for lightweight, high-performance materials in the automotive sector has driven the use of carbon fiber/polyamide 6 (CF/PA6) composites. This study proposes a grinding-free recycling route based on the reassembly of CF/PA6 composite cutouts into a controlled laminate configuration, followed by hot compression molding. Three configurations were investigated: S21 (two layers of 1 mm-thickness square cutouts), S13 (one layer of 3 mm-thickness square cutouts), and R21 (two layers of 1 mm-thickness rectangular cutouts), all containing 85 wt % CF/PA6 scraps and 15 wt % neat PA6 powder. The recycled laminates were characterized by ultrasonic inspection, differential scanning calorimetry (DSC), acid digestion for volumetric fraction determination, tensile and flexural testing, and field-emission gun scanning electron microscopy (FEG-SEM) analyses. Ultrasonic inspection and acid digestion showed that the S13 configuration exhibited the highest structural homogeneity and the lowest void content. In contrast, S21 and R21 presented higher void fractions, as confirmed by ultrasonic maps, acid digestion results, and FEG-SEM observations. Despite the higher void content, S21 achieved the highest tensile strength, probably due to the more efficient stress distribution throughout the laminate. Fractographic analyses revealed good fiber–matrix interfacial adhesion, as well as typical aspects observed in the fracture surfaces of thermoplastic polymeric composites, including plastic deformation, fiber pullout, and matrix-rich regions. Overall, the results demonstrate that the proposed grinding-free recycling approach enables the reuse of CF/PA6 waste in multilayer architectures in applications that do not require high structural performance.
Related
- Impeller Configuration and Agitation Speed Govern Lignin Dispersion and Resultant Properties of Natural Rubber Composites in Wet Mixing: A CFD Experimental Study
- Effect of a Pre‐Treatment on the Mechanical and Acoustic Properties of Recycled Ground Tire Rubber/Polyurethane Foam Composites
- Sustainable Graphene-Reinforced Geopolymer Composites Derived from Recycled Volcanic Ash: Matrix Optimization, Characterization, and Photoluminescent Proof-of-Concept
- Evaluating Measurement Bias in Flexural Modulus of Orthotropic UHMWPE Fiber/Nano-Epoxy Composites: A Finite Element Study
- Contamination tolerant poly(ethylene terephthalate) composites from recycled feedstocks and cellulosic waste
BibTeX
@article{nascimento2026effect,
title = {{Effect of Scrap Configuration on the Tensile and Flexural Properties of Grinding-Free Recycled CF/PA6 Composites}},
author = {Talita Melo do Nascimento and Larissa Stieven Montagna and Thiely Ferreira da Silva and Rieyssa Maria de Almeida Corrêa and Guilherme Ferreira de Melo Morgado and Juliano Marini and Camila Alves Escanio and Mirabel Cerqueira Rezende and Fabio Roberto Passador},
journal = {ACS Omega},
year = {2026},
month = oct,
doi = {10.1021/acsomega.6c08579},
url = {https://pubs.acs.org/acsodf/article/11/42/65716/5451155/Effect-of-Scrap-Configuration-on-the-Tensile-and},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Effect of Scrap Configuration on the Tensile and Flexural Properties of Grinding-Free Recycled CF/PA6 Composites
AU - Talita Melo do Nascimento
AU - Larissa Stieven Montagna
AU - Thiely Ferreira da Silva
AU - Rieyssa Maria de Almeida Corrêa
AU - Guilherme Ferreira de Melo Morgado
AU - Juliano Marini
AU - Camila Alves Escanio
AU - Mirabel Cerqueira Rezende
AU - Fabio Roberto Passador
PY - 2026
DA - 2026/10/14
JO - ACS Omega
DO - 10.1021/acsomega.6c08579
UR - https://pubs.acs.org/acsodf/article/11/42/65716/5451155/Effect-of-Scrap-Configuration-on-the-Tensile-and
AB - The increasing demand for lightweight, high-performance materials in the automotive sector has driven the use of carbon fiber/polyamide 6 (CF/PA6) composites. This study proposes a grinding-free recycling route based on the reassembly of CF/PA6 composite cutouts into a controlled laminate configuration, followed by hot compression molding. Three configurations were investigated: S21 (two layers of 1 mm-thickness square cutouts), S13 (one layer of 3 mm-thickness square cutouts), and R21 (two layers of 1 mm-thickness rectangular cutouts), all containing 85 wt % CF/PA6 scraps and 15 wt % neat PA6 powder. The recycled laminates were characterized by ultrasonic inspection, differential scanning calorimetry (DSC), acid digestion for volumetric fraction determination, tensile and flexural testing, and field-emission gun scanning electron microscopy (FEG-SEM) analyses. Ultrasonic inspection and acid digestion showed that the S13 configuration exhibited the highest structural homogeneity and the lowest void content. In contrast, S21 and R21 presented higher void fractions, as confirmed by ultrasonic maps, acid digestion results, and FEG-SEM observations. Despite the higher void content, S21 achieved the highest tensile strength, probably due to the more efficient stress distribution throughout the laminate. Fractographic analyses revealed good fiber–matrix interfacial adhesion, as well as typical aspects observed in the fracture surfaces of thermoplastic polymeric composites, including plastic deformation, fiber pullout, and matrix-rich regions. Overall, the results demonstrate that the proposed grinding-free recycling approach enables the reuse of CF/PA6 waste in multilayer architectures in applications that do not require high structural performance.
SN - 2470-1343
ER -