Moisture-dependent strength and microstructural response of clay stabilized with unsaturated polyester resin
Abstract
This study examines how initial water content influences the strength and microstructural response of a low-plasticity clay stabilized with unsaturated polyester resin (UPR). Clay specimens were prepared at two initial water contents, 0.5 LL and LL, and treated with 0–20% UPR. Unconfined compressive strength (UCS) tests were performed after 14 days of curing, and selected specimens were examined using SEM–EDX, XRD and FTIR. The UCS response depended strongly on initial water content. At 0.5LL, UCS increased with UPR content and reached 9.88 MPa at 20% UPR. At LL, UCS reached a maximum of 5.52 MPa at 10% UPR and then decreased at higher dosages. SEM–EDX observations indicated polymer-rich domains and a more integrated fabric in the 0.5LL specimens, whereas the LL specimens showed a more heterogeneous structure. XRD patterns showed no distinct new crystalline reaction products, and FTIR confirmed a polyester-related ester carbonyl response near 1720 cm⁻ ¹ . These results indicate that initial water content strongly influences the efficiency of UPR stabilization in the tested clay–polymer system by affecting the continuity and effectiveness of polymer-associated binding.
Related
- Numerical predictions for the behaviour of brick masonry with unsaturated polyester mortar: influence of the damage
- Photocrosslinking of an original biobased and semi-aromatic unsaturated polyester by combined thiol-ene and cycloaddition routes
- Thermal, Thermomechanical, and Fire Behaviour of Casein-Modified Unsaturated Polyester Resin Biocomposites
- Microwave-Assisted Degradation of Unsaturated Polyester Resin into HDPE-Modified Aerogels for Oil Adsorption and Oil/Water Separation.
- Strength-permeability-disintegration evolution and microstructural coupling mechanisms of oil-contaminated silty sand at natural moisture content
BibTeX
@article{yurtcan2026moisturedependent,
title = {{Moisture-dependent strength and microstructural response of clay stabilized with unsaturated polyester resin}},
author = {Uğur Eren Yurtcan},
journal = {Scientific Reports},
year = {2026},
month = oct,
doi = {10.1038/s41598-026-77420-w},
url = {https://www.nature.com/articles/s41598-026-77420-w},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Moisture-dependent strength and microstructural response of clay stabilized with unsaturated polyester resin
AU - Uğur Eren Yurtcan
PY - 2026
DA - 2026/10/21
JO - Scientific Reports
DO - 10.1038/s41598-026-77420-w
UR - https://www.nature.com/articles/s41598-026-77420-w
AB - This study examines how initial water content influences the strength and microstructural response of a low-plasticity clay stabilized with unsaturated polyester resin (UPR). Clay specimens were prepared at two initial water contents, 0.5 LL and LL, and treated with 0–20% UPR. Unconfined compressive strength (UCS) tests were performed after 14 days of curing, and selected specimens were examined using SEM–EDX, XRD and FTIR. The UCS response depended strongly on initial water content. At 0.5LL, UCS increased with UPR content and reached 9.88 MPa at 20% UPR. At LL, UCS reached a maximum of 5.52 MPa at 10% UPR and then decreased at higher dosages. SEM–EDX observations indicated polymer-rich domains and a more integrated fabric in the 0.5LL specimens, whereas the LL specimens showed a more heterogeneous structure. XRD patterns showed no distinct new crystalline reaction products, and FTIR confirmed a polyester-related ester carbonyl response near 1720 cm⁻ ¹ . These results indicate that initial water content strongly influences the efficiency of UPR stabilization in the tested clay–polymer system by affecting the continuity and effectiveness of polymer-associated binding.
SN - 2045-2322
ER -