Fabrication and Performance of Thermally Triggered Active Fire-Extinguishing Patches Based on Perfluorohexanone Microcapsule-Modified Epoxy Resin
- 1School of Civil Engineering, Hebei University of Engineering, Handan 056000, China
- 2Department of Mechanical and Aerospace Engineering, The Hong Kong University of Science and Technology, Clear Water Bay, Kowloon, Hong Kong, China
- 3School of Economics and Management, Yanshan University, Qinghuangdao 066004, China
Abstract
To address the challenges of timely detection and local suppression of incipient fires, as well as the inherent limitations of traditional flame-retardant materials that primarily rely on passive thermal insulation or combustion retardation, this study developed thermally responsive microcapsules with perfluorohexanone as the core material and melamine–urea–formaldehyde (MUF) resin as the shell. These microcapsules were incorporated into an epoxy resin matrix to fabricate active fire-extinguishing patches. The morphology, chemical structure, thermal stability, thermally triggered release behavior, and fire-extinguishing performance of the microcapsules and the composite patches were systematically characterized by microscopic observation, FTIR, XPS, TGA particle size analysis, and combustion tests. The results showed that the prepared microcapsules exhibited a nearly spherical morphology with a median particle size (D50) of 143.94 μm and an encapsulation efficiency of 87.78%. After heating at 60 °C for 24 h, the mass loss was 5.88%, and after sealed storage at room temperature for 360 days, the mass loss was only 1.8%, indicating satisfactory thermal stability and storage stability. When the microcapsules were compounded with epoxy resin, the self-extinguishing time of the resulting patches decreased with increasing microcapsule content, reaching a minimum of 4.81 s. Mechanism analysis suggested that the fire-extinguishing effect of the composite system originated predominantly from gas-phase flame inhibition by the released perfluorohexanone, possibly synergized with a condensed-phase barrier effect derived from the charring epoxy matrix upon heating. This work provides experimental evidence for the application of perfluorohexanone-based active fire-extinguishing composites in proactive fire protection.
Related
- Scalable Fabrication of Lightweight, Thermally Insulating and Ablation-Resistant SiC/SiOC Hybrid Aerogel Composites Reinforced with High-Porosity Needle-Punched Quartz Fiber Felts
- Diatomite-Templated Fabrication of Porous N, S-Co-Doped Carbon as High-Performance Catalyst for Oxygen Reduction
- Post-Fabrication Deprotection of Semiconducting Polymers for High-Performance Organic Electrochemical Transistors.
- Developing renewable polysaccharide-based bioplastic films using pectin derived from agricultural cocoa husk byproducts: fabrication, characterization, and performance assessment
- Infrared Photothermal Heterodyne Imaging in Thermally Thick Medium for Thermo-optic Property Characterizations
BibTeX
@article{tian2026fabrication,
title = {{Fabrication and Performance of Thermally Triggered Active Fire-Extinguishing Patches Based on Perfluorohexanone Microcapsule-Modified Epoxy Resin}},
author = {Zihou Tian and Le Yang and Songdi Zhang and Xiaoqian Wang and Xinteng Li and Jinliang An},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18212640},
url = {https://www.mdpi.com/2073-4360/18/21/2640},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Fabrication and Performance of Thermally Triggered Active Fire-Extinguishing Patches Based on Perfluorohexanone Microcapsule-Modified Epoxy Resin
AU - Zihou Tian
AU - Le Yang
AU - Songdi Zhang
AU - Xiaoqian Wang
AU - Xinteng Li
AU - Jinliang An
PY - 2026
DA - 2026/10/25
JO - Polymers
DO - 10.3390/polym18212640
UR - https://www.mdpi.com/2073-4360/18/21/2640
AB - To address the challenges of timely detection and local suppression of incipient fires, as well as the inherent limitations of traditional flame-retardant materials that primarily rely on passive thermal insulation or combustion retardation, this study developed thermally responsive microcapsules with perfluorohexanone as the core material and melamine–urea–formaldehyde (MUF) resin as the shell. These microcapsules were incorporated into an epoxy resin matrix to fabricate active fire-extinguishing patches. The morphology, chemical structure, thermal stability, thermally triggered release behavior, and fire-extinguishing performance of the microcapsules and the composite patches were systematically characterized by microscopic observation, FTIR, XPS, TGA particle size analysis, and combustion tests. The results showed that the prepared microcapsules exhibited a nearly spherical morphology with a median particle size (D50) of 143.94 μm and an encapsulation efficiency of 87.78%. After heating at 60 °C for 24 h, the mass loss was 5.88%, and after sealed storage at room temperature for 360 days, the mass loss was only 1.8%, indicating satisfactory thermal stability and storage stability. When the microcapsules were compounded with epoxy resin, the self-extinguishing time of the resulting patches decreased with increasing microcapsule content, reaching a minimum of 4.81 s. Mechanism analysis suggested that the fire-extinguishing effect of the composite system originated predominantly from gas-phase flame inhibition by the released perfluorohexanone, possibly synergized with a condensed-phase barrier effect derived from the charring epoxy matrix upon heating. This work provides experimental evidence for the application of perfluorohexanone-based active fire-extinguishing composites in proactive fire protection.
SN - 2073-4360
ER -