Ultrarobust, Rapidly Recoverable Superhydrophobic Coatings with Self-Similar Micro/Nanostructures and Reinforced Interface for Aluminum Alloy Protection
- 1Chinese Research Academy of Environmental Sciences , , ,
- 2Beijing University of Technology , , ,
- 3University of Cambridge , , ,
Abstract
In the field of aluminum alloy protection, constructing durable superhydrophobic coatings through a simple strategy is always a great challenge. Here, we report a functional coating with high mechanical robustness and superhydrophobic recoverability, composed of 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane (PTES) bonded octyltrimethoxysilane-functionalized titanium dioxide nanoparticles (OTMS-TiO2 NPs) and high-viscosity epoxy resin (EP). The coating combines a hierarchical micro/nanostructure, an EP adhesive interface, and a surface enriched with fluorinated and alkyl functionalities. The synergy between the hierarchical roughness and the low-polarity surface chemistry enables excellent water repellency. After 100 cycles of sandpaper abrasion or tape peeling, the coating retained its superhydrophobic water repellency, with WCA values remaining above 160°. The newly exposed surfaces preserved sufficient hierarchical roughness and low-surface-energy components to sustain superhydrophobic. Even after continuous water flow impact or stirred sand-slurry abrasion for 48 h, the superhydrophobicity of the coating does not show significant degradation (WCA > 150°). In addition, the coating shows great stability in strong acidic (pH = 2) or strong alkaline (pH = 12) environments. More importantly, when the coating encounters mechanical damage, corrosion by 36.5 wt % HCl, or complete contamination by industrial oil/paint, its superhydrophobic properties can be quickly restored through a simple sandpaper rubbing treatment. This easily prepared superhydrophobic coating with both recoverability and excellent robustness provides new technical support for protecting aluminum alloy.
Related
- Fabrication of superhydrophobic and superoleophilic copper oxide nanostructures without organic modifiers for oil–water separation
- Biofabricated CuO Nanoparticle Reinforced Bamboo Fiber Coatings for Photocatalytic Antimicrobial and Superhydrophobic Biomedical Textile Applications
- Superhydrophobic Porous Coordination Polymer-Confined Co3O4 Nanoparticles: A Sustainable Strategy for Electrochemical Water Splitting
- Superhydrophobic-Like Complete Rebound of Impacting Water Droplets on a Smooth Oleic- Acid-Coated Phenyl-Silica Surface
- A Durable Hierarchical ZnO/Epoxy Superhydrophobic Coating for Dual-Mode Drag Reduction of Surface and Underwater Vehicles
BibTeX
@article{chen2026ultrarobust,
title = {{Ultrarobust, Rapidly Recoverable Superhydrophobic Coatings with Self-Similar Micro/Nanostructures and Reinforced Interface for Aluminum Alloy Protection}},
author = {Jing Chen and Fujia Wang and Xinxin Xiao and Xiaohan Jia and Xiaowei Wang and Sha Chen},
journal = {ACS Omega},
year = {2026},
month = oct,
doi = {10.1021/acsomega.6c07237},
url = {https://pubs.acs.org/acsodf/article/11/41/63441/5446656/Ultrarobust-Rapidly-Recoverable-Superhydrophobic},
note = {CC BY-NC-ND 4.0},
}
RIS
TY - JOUR
TI - Ultrarobust, Rapidly Recoverable Superhydrophobic Coatings with Self-Similar Micro/Nanostructures and Reinforced Interface for Aluminum Alloy Protection
AU - Jing Chen
AU - Fujia Wang
AU - Xinxin Xiao
AU - Xiaohan Jia
AU - Xiaowei Wang
AU - Sha Chen
PY - 2026
DA - 2026/10/08
JO - ACS Omega
DO - 10.1021/acsomega.6c07237
UR - https://pubs.acs.org/acsodf/article/11/41/63441/5446656/Ultrarobust-Rapidly-Recoverable-Superhydrophobic
AB - In the field of aluminum alloy protection, constructing durable superhydrophobic coatings through a simple strategy is always a great challenge. Here, we report a functional coating with high mechanical robustness and superhydrophobic recoverability, composed of 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane (PTES) bonded octyltrimethoxysilane-functionalized titanium dioxide nanoparticles (OTMS-TiO2 NPs) and high-viscosity epoxy resin (EP). The coating combines a hierarchical micro/nanostructure, an EP adhesive interface, and a surface enriched with fluorinated and alkyl functionalities. The synergy between the hierarchical roughness and the low-polarity surface chemistry enables excellent water repellency. After 100 cycles of sandpaper abrasion or tape peeling, the coating retained its superhydrophobic water repellency, with WCA values remaining above 160°. The newly exposed surfaces preserved sufficient hierarchical roughness and low-surface-energy components to sustain superhydrophobic. Even after continuous water flow impact or stirred sand-slurry abrasion for 48 h, the superhydrophobicity of the coating does not show significant degradation (WCA > 150°). In addition, the coating shows great stability in strong acidic (pH = 2) or strong alkaline (pH = 12) environments. More importantly, when the coating encounters mechanical damage, corrosion by 36.5 wt % HCl, or complete contamination by industrial oil/paint, its superhydrophobic properties can be quickly restored through a simple sandpaper rubbing treatment. This easily prepared superhydrophobic coating with both recoverability and excellent robustness provides new technical support for protecting aluminum alloy.
SN - 2470-1343
ER -