Mn-deficient Ni-Mn-Ga alloys: phase transitions, magnetic properties, and disappearance of martensitic transformation
Abstract
Composition gradients formed during directional solidification are generally considered undesirable in Ni-Mn-Ga magnetic shape-memory alloys. However, these gradients offer a highly effective platform for systematically investigating composition-property relationships under identical growth and heat-treatment conditions. To exploit this approach, one Mn-deficient and two near-stoichiometric Ni-Mn-Ga oligocrystals were grown by optical zone remelting and characterized by X-ray fluorescence mapping, optical microscopy, X-ray diffraction, low-field magnetic measurements, and vibrating-sample magnetometry. The ingots contained elongated grains and axial compositional gradients, primarily associated with the redistribution of Mn and Ga, whereas Ni remained relatively uniformly distributed. The martensitic and premartensitic transformation temperatures generally increased with increasing Mn content. Neither transformation was detected between 10 and 400 K in specimens containing 20.5-22.0 at.% Mn, all of which had e/a < 7.40. In contrast, both transformations were observed in the investigated specimens containing at least 22.1 at.% (e/a ≥ 7.46). This abrupt change may indicate a possible electron-concentration threshold for the occurrence of these transformations. Saturation magnetization increased with Mn content up to 25.8 at.%, reaching 96.9 A m2/kg at 10 K and 71.2 A m2/kg at 300 K. Post-growth annealing increased the transition temperatures and changed the low-field magnetic response. The results indicate that composition-gradient oligocrystals serve as an effective platform for investigating the relationships between composition, structure, and magnetic properties in Ni-Mn-Ga alloys with the same processing history.
Related
- Modelling the dynamics of the martensitic transformation in Ni2MnGa with machine-learning force-fields
- Dynamical Phase Transitions as Properties of the Stationary State: Analytic Results after Quantum Quenches in the Spin-1/2 XXZ Chain
- Transport properties and topological phase transitions for a Creutz-Su-Schrieffer-Heeger ladder
- Neutron disappearance and the LZ nuclear recoil event
- DM induced neutron disappearance as the origin of the LZ nuclear recoil event
BibTeX
@misc{moskvina2026mndeficient,
title = {{Mn-deficient Ni-Mn-Ga alloys: phase transitions, magnetic properties, and disappearance of martensitic transformation}},
author = {Valentina Moskvina and Jaroslav Čapek and Michal Rameš and Denys Musiienko and Petr Veřtát and Alexej Perevertov and Ladislav Straka and Oleg Heczko},
howpublished = {arXiv},
year = {2026},
month = oct,
doi = {10.48550/arxiv.2610.31206},
eprint = {2610.31206},
archivePrefix = {arXiv},
url = {https://arxiv.org/abs/2610.31206},
note = {CC BY 4.0},
}
RIS
TY - UNPB
TI - Mn-deficient Ni-Mn-Ga alloys: phase transitions, magnetic properties, and disappearance of martensitic transformation
AU - Valentina Moskvina
AU - Jaroslav Čapek
AU - Michal Rameš
AU - Denys Musiienko
AU - Petr Veřtát
AU - Alexej Perevertov
AU - Ladislav Straka
AU - Oleg Heczko
PY - 2026
DA - 2026/10/22
PB - arXiv
DO - 10.48550/arxiv.2610.31206
UR - https://arxiv.org/abs/2610.31206
AB - Composition gradients formed during directional solidification are generally considered undesirable in Ni-Mn-Ga magnetic shape-memory alloys. However, these gradients offer a highly effective platform for systematically investigating composition-property relationships under identical growth and heat-treatment conditions. To exploit this approach, one Mn-deficient and two near-stoichiometric Ni-Mn-Ga oligocrystals were grown by optical zone remelting and characterized by X-ray fluorescence mapping, optical microscopy, X-ray diffraction, low-field magnetic measurements, and vibrating-sample magnetometry. The ingots contained elongated grains and axial compositional gradients, primarily associated with the redistribution of Mn and Ga, whereas Ni remained relatively uniformly distributed. The martensitic and premartensitic transformation temperatures generally increased with increasing Mn content. Neither transformation was detected between 10 and 400 K in specimens containing 20.5-22.0 at.% Mn, all of which had e/a < 7.40. In contrast, both transformations were observed in the investigated specimens containing at least 22.1 at.% (e/a ≥ 7.46). This abrupt change may indicate a possible electron-concentration threshold for the occurrence of these transformations. Saturation magnetization increased with Mn content up to 25.8 at.%, reaching 96.9 A m^2/kg at 10 K and 71.2 A m^2/kg at 300 K. Post-growth annealing increased the transition temperatures and changed the low-field magnetic response. The results indicate that composition-gradient oligocrystals serve as an effective platform for investigating the relationships between composition, structure, and magnetic properties in Ni-Mn-Ga alloys with the same processing history.
ER -