Structure–Performance Interplay and Mechanical Degradation Modes in Lithium Cobalt Oxide Cathodes: Implications for Flexible Lithium-Ion Battery Design
- 1Materials Science and Engineering, Fulton Schools of Engineering, Arizona State University, Tempe, AZ 85287, USA
- 2Chemical Engineering, Fulton Schools of Engineering, Arizona State University, Tempe, AZ 85287, USA
Abstract
Lithium cobalt oxide (LCO) remains the industry-standard cathode for lithium-ion batteries in consumer electronics, but its mechanical reliability under repeated deformation—a critical requirement for flexible and wearable devices—has not been systematically investigated. Here, as-manufactured LCO electrodes are subjected to repeated bending (up to 3000 cycles) at diameters of 100, 50, and 25 mm, followed by post-bending electrochemical, microstructure, and electrical characterization. Bending-induced degradation mechanisms are found to be strongly impacted by the LCO particle size. Coarse-particle electrodes undergo pronounced particle detachment and interfacial failure, medium-particle electrodes exhibit mixed damage modes, and fine-particle electrodes primarily exhibit delamination but retain strong composite cohesion, displaying the highest mechanical durability and electrochemical stability. Even after 3000 bending cycles at a 50 mm diameter, Fine-LCO electrodes retain 88.6% of their initial capacity (123 mAh g−1) at a 2 C rate, whereas other electrodes exhibit capacity losses of up to 97%. Electrode and interface resistances increase with bending severity, but these changes do not fully explain performance loss, underscoring the importance of complementary characterization techniques for elucidating failure mechanisms. These findings identify particle size control as a practical strategy for improving conventional LCO electrodes for flexible battery applications.
Related
- The complementary-competitive interplay of consumer information search and experience sharing: Implications for targeted advertising and firm performance
- Composition–Structure–Property Relationships in PLA-nHA-Mg Hybrid Biocomposites: Effect of Ceramic–Metallic Reinforcement Ratio on Mechanical and Physicochemical Performance
- Electrochemical Metastability of Au–Pd Alloy Nanoparticles: Interplay between Alloying, Surface Structure, and Halide-Induced Dissolution
- Overlooked Roles of Oxygen in PFAS Degradation by UV/Sulfite: Mechanistic Insights and Engineering Implications
- Interplay between Thermal Denaturation and Dynamic Covalent Chemistry Generates High-Performance Recyclable Protein Plastics.
BibTeX
@article{kim2026structureperformance,
title = {{Structure–Performance Interplay and Mechanical Degradation Modes in Lithium Cobalt Oxide Cathodes: Implications for Flexible Lithium-Ion Battery Design}},
author = {Kyungbae Kim and Roberto Martinez and Candace K. Chan},
journal = {Batteries},
year = {2026},
month = oct,
doi = {10.3390/batteries12100400},
url = {https://www.mdpi.com/2313-0105/12/10/400},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Structure–Performance Interplay and Mechanical Degradation Modes in Lithium Cobalt Oxide Cathodes: Implications for Flexible Lithium-Ion Battery Design
AU - Kyungbae Kim
AU - Roberto Martinez
AU - Candace K. Chan
PY - 2026
DA - 2026/10/05
JO - Batteries
DO - 10.3390/batteries12100400
UR - https://www.mdpi.com/2313-0105/12/10/400
AB - Lithium cobalt oxide (LCO) remains the industry-standard cathode for lithium-ion batteries in consumer electronics, but its mechanical reliability under repeated deformation—a critical requirement for flexible and wearable devices—has not been systematically investigated. Here, as-manufactured LCO electrodes are subjected to repeated bending (up to 3000 cycles) at diameters of 100, 50, and 25 mm, followed by post-bending electrochemical, microstructure, and electrical characterization. Bending-induced degradation mechanisms are found to be strongly impacted by the LCO particle size. Coarse-particle electrodes undergo pronounced particle detachment and interfacial failure, medium-particle electrodes exhibit mixed damage modes, and fine-particle electrodes primarily exhibit delamination but retain strong composite cohesion, displaying the highest mechanical durability and electrochemical stability. Even after 3000 bending cycles at a 50 mm diameter, Fine-LCO electrodes retain 88.6% of their initial capacity (123 mAh g−1) at a 2 C rate, whereas other electrodes exhibit capacity losses of up to 97%. Electrode and interface resistances increase with bending severity, but these changes do not fully explain performance loss, underscoring the importance of complementary characterization techniques for elucidating failure mechanisms. These findings identify particle size control as a practical strategy for improving conventional LCO electrodes for flexible battery applications.
SN - 2313-0105
ER -