Enhancement of the corrosion protection performance of Ni coatings on steel substrates using HiPIMS pretreatment
Abstract
This paper adresses with the enhancement of corrosion resistance of steel substrates using High Power Impulse Magnetron Sputtering (HiPIMS) pretreatment before deposition of Nickel (Ni) coating by sputtering. Electrochemical measurements show that Ni exhibits a higher corrosion potential than steel. In this situation, slight imperfections in the Ni coating can cause severe anodic dissolution of the steel substrate in a corrosive environment. It is therefore necessary to optimize the steel surface preparation before depositing the Ni coating, as growth defects originate mainly from irregularities on the substrate surface (dust, polishing residues, impurities). In this work, we developed a HiPIMS pretreatment of the steel substrate. This latter is subjected to intense and homogeneous Ni ion bombardment using a Ni-Ar HiPIMS discharge and biasing the substrate at -600 V. We obtained an ultra-clean substrate surface and the formation of a Ni1-x Fex intermixed interface. Advantageously, the resulting modified surface provides an ideal template for the Ni layer to grow without open paths down to the substrate surface, resulting in corrosion resistance of the Ni-steel system for more than 1000 h in a salt spray bath, at room temperature.
Related
- Sustainable MOF-derived nanocomposites for advanced corrosion protection and mechanical performance: A comprehensive review of materials, mechanisms, and future directions
- Corrosion protection of XC70 mild steel by a Ni–Co/TiO₂ composite coating in an acidic chloride environment
- Sustainable corrosion inhibitor derived from Moroccan oil shale: calcium acetate for steel protection
- Investigation of mulberry leaf and olive pomace extracts as green corrosion inhibitors for carbon steel protection: Experimental evaluation and process optimization
- Critical and comparative evaluation of waterborne polymer resin based coatings for corrosion protection
BibTeX
@article{keraudy2026enhancement,
title = {{Enhancement of the corrosion protection performance of Ni coatings on steel substrates using HiPIMS pretreatment}},
author = {Julien Keraudy and Axel Ferrec and Duc Tuong Nguyen and Dimitri Boivin and Mireille Richard-Plouet and Vincent Fernandez and Neal Fairley and Jérémy Barbé and Pierre-Yves Jouan},
journal = {Vacuum},
year = {2026},
month = oct,
doi = {10.1016/j.vacuum.2026.115503},
url = {https://hal.science/hal-05753283v2},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Enhancement of the corrosion protection performance of Ni coatings on steel substrates using HiPIMS pretreatment
AU - Julien Keraudy
AU - Axel Ferrec
AU - Duc Tuong Nguyen
AU - Dimitri Boivin
AU - Mireille Richard-Plouet
AU - Vincent Fernandez
AU - Neal Fairley
AU - Jérémy Barbé
AU - Pierre-Yves Jouan
PY - 2026
DA - 2026/10/08
JO - Vacuum
DO - 10.1016/j.vacuum.2026.115503
UR - https://hal.science/hal-05753283v2
AB - This paper adresses with the enhancement of corrosion resistance of steel substrates using High Power Impulse Magnetron Sputtering (HiPIMS) pretreatment before deposition of Nickel (Ni) coating by sputtering. Electrochemical measurements show that Ni exhibits a higher corrosion potential than steel. In this situation, slight imperfections in the Ni coating can cause severe anodic dissolution of the steel substrate in a corrosive environment. It is therefore necessary to optimize the steel surface preparation before depositing the Ni coating, as growth defects originate mainly from irregularities on the substrate surface (dust, polishing residues, impurities). In this work, we developed a HiPIMS pretreatment of the steel substrate. This latter is subjected to intense and homogeneous Ni ion bombardment using a Ni-Ar HiPIMS discharge and biasing the substrate at -600 V. We obtained an ultra-clean substrate surface and the formation of a Ni1-x Fex intermixed interface. Advantageously, the resulting modified surface provides an ideal template for the Ni layer to grow without open paths down to the substrate surface, resulting in corrosion resistance of the Ni-steel system for more than 1000 h in a salt spray bath, at room temperature.
SN - 0042-207X
SN - 1879-2715
ER -