Functionally Graded Polymer Lattice Structures Enabled by Multi-Material Fused Deposition Modeling: Current Progress, Challenges, and Future Perspectives
- 1Mechanical Engineering Department, Sakarya University, 54050 Sakarya, Turkey
Abstract
Functionally graded lattice (FGL) structures can decouple stiffness, strength and energy absorption. Multi-material fused deposition modeling (MM-FDM) is an accessible route to lattices that vary in composition and topology within one print. This review examines MM-FDM polymer FGLs through a PRISMA 2020-informed screening of 610 records. Of the 126 screened references, 65 primary studies meet all eligibility criteria and form the core evidence, and 20 are supporting studies. Four grading strategies were identified: material-based zoning, geometry-induced grading, combined material–geometry grading and process-induced grading, applied mainly to strut-based, triply periodic minimal surface (TPMS) and hybrid plate–TPMS architectures. Pairing rigid thermoplastics (PLA, ABS, PETG) with hyperelastic TPU increased specific energy absorption by up to two- to threefold over single-material lattices, but the gain over the rigid constituent alone was smaller and, in several quasi-static studies, negative; it depends on configuration, baseline and loading rate. Graded lattices collapse layer by layer, yet their energy gain over uniform lattices of equal mass is often modest. TPMS architectures are reported to reduce nodal stress concentrations. Most evidence remains at the specimen level. The main limitations are weak interfaces between incompatible polymers, process-induced defects, models that neglect manufacturing effects and the lack of standardized test protocols.
Related
- Reply to Cantwell Chater and Shahsavar: Clarifying PDB deposition records and local model interpretation in GlyT2 structures.
- Effect of Silver Deposition on the Material Characteristics and Photocatalytic Activity of Barium Titanates
- Functionalization of polycaprolactone scaffolds for tissue engineering: molecular cues, bioactive cell–material interfaces, and translational perspectives
- Hybrid Joining Technologies for Composites: Mechanisms, Performance, Challenges, and Perspectives
- Manufacturing of Hierarchical (Nano-)Composite Structures: Numerical and Experimental Perspectives
BibTeX
@article{usman2026functionally,
title = {{Functionally Graded Polymer Lattice Structures Enabled by Multi-Material Fused Deposition Modeling: Current Progress, Challenges, and Future Perspectives}},
author = {Abdullahi Idris Usman and Muhammet Muaz Yalçın},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18202483},
url = {https://www.mdpi.com/2073-4360/18/20/2483},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Functionally Graded Polymer Lattice Structures Enabled by Multi-Material Fused Deposition Modeling: Current Progress, Challenges, and Future Perspectives
AU - Abdullahi Idris Usman
AU - Muhammet Muaz Yalçın
PY - 2026
DA - 2026/10/11
JO - Polymers
DO - 10.3390/polym18202483
UR - https://www.mdpi.com/2073-4360/18/20/2483
AB - Functionally graded lattice (FGL) structures can decouple stiffness, strength and energy absorption. Multi-material fused deposition modeling (MM-FDM) is an accessible route to lattices that vary in composition and topology within one print. This review examines MM-FDM polymer FGLs through a PRISMA 2020-informed screening of 610 records. Of the 126 screened references, 65 primary studies meet all eligibility criteria and form the core evidence, and 20 are supporting studies. Four grading strategies were identified: material-based zoning, geometry-induced grading, combined material–geometry grading and process-induced grading, applied mainly to strut-based, triply periodic minimal surface (TPMS) and hybrid plate–TPMS architectures. Pairing rigid thermoplastics (PLA, ABS, PETG) with hyperelastic TPU increased specific energy absorption by up to two- to threefold over single-material lattices, but the gain over the rigid constituent alone was smaller and, in several quasi-static studies, negative; it depends on configuration, baseline and loading rate. Graded lattices collapse layer by layer, yet their energy gain over uniform lattices of equal mass is often modest. TPMS architectures are reported to reduce nodal stress concentrations. Most evidence remains at the specimen level. The main limitations are weak interfaces between incompatible polymers, process-induced defects, models that neglect manufacturing effects and the lack of standardized test protocols.
SN - 2073-4360
ER -