Mechanical and morphological properties of cellulose biocomposites

Abstract

Natural biocomposites offer promising alternatives to petroleum-based composites thanks to their biocompatibility, sustainability, and low environmental impact. However, they must also demonstrate competitive mechanical properties and adaptability to manufacturing processes. To this end, we developed cellulosic biocomposites using plasticized cellulose acetate (PCA) reinforced with cellulosic fibers at loadings from 30 to 50 wt%. Mechanical properties were determined with tensile, bending, and impact tests and interfacial bonding was analyzed using scanning electron microscopy (SEM). Results showed that the adhesion of 50 wt% cellulose fibers increased the Young's modulus of the biocomposites by 300 % and the tensile strength by 12 %. Flexural properties also improved: the flexural modulus increased from 1.52 GPa to 5 GPa for PCA at maximum fiber loading, and from 43.3 MPa to 54 MPa for flexural strength. However, the elongation at break decreased with increasing cellulose content, from 13.5 % to 0.8 %, along with a 74 % decrease in impact strength. SEM results revealed good fiber dispersion, interfacial adhesion, porosity, and fiber pullout. These results underscore the potential for cellulose biocomposites as eco-friendly alternatives for high-value utilizations, including electronic and dielectric applications.

Natural CaCO₃ improves the moisture resistance and mechanical performance of hemp-starch biocomposites: A multi-objective optimization study
Sameh Balti, Chadi Maalouf, Tala Moussa +7
Case Studies in Construction Materials25 Sep 2026Peer-reviewedCC BY 4.0Full textEnvironmental science & pollution General physicsHAL
The Interfacial Effect of Structural Optimization of Sugar Palm and Woven Carbon Fiber Reinforced Epoxy Composites on Mechanical, Thermal, Fire Resistance, and Morphological Performance
Mohammed Huzaifa Mulla, Mohd Nurazzi Norizan, Mohamad Haafiz Mohamad Kassim +5
Journal of Natural Fibers25 Jul 2026Peer-reviewedCC BY 4.0Full textEnvironmental science & pollutionHAL
Impact of S-metolachlor, atrazine and their metabolites on the morphological, structural and functional properties of the intestinal barrier
Nolwenn Dubois, Aurélie Loussouarn, Maxime Mahé +3
Ecotoxicology and Environmental Safety28 Oct 2026Peer-reviewedCC BY 4.0Full textGeneral biology Environmental science & pollutionHAL
Research on the mechanical properties of loess solidified via enzyme induced calcium carbonate precipitation (EICP)
Siwei Chen, Jia Liu, Gang Li +1
Scientific Reports12 Oct 2026Peer-reviewedCC BY-NC-ND 4.0Full textEnvironmental science & pollutionCrossref
Study on the mechanical properties and resistance to wetting–drying cycles of red clay stabilized by enzyme-induced carbonate precipitation (EICP)
Xiaolong Xu, Zhongyuan Chen, Jianping Wei +3
Scientific Reports26 Oct 2026Peer-reviewedCC BY-NC-ND 4.0Full textEnvironmental science & pollutionCrossref

Cite

BibTeX RIS

BibTeX

@article{khouaja2026mechanical,
  title = {{Mechanical and morphological properties of cellulose biocomposites}},
  author = {Asma Khouaja and Ahmed Koubaa and Hachmi Ben Daly},
  journal = {Chemosphere},
  year = {2026},
  month = oct,
  doi = {10.1016/j.chemosphere.2025.144415},
  url = {https://hal.science/hal-05795994v1},
  note = {CC BY},
}

RIS

TY  - JOUR
TI  - Mechanical and morphological properties of cellulose biocomposites
AU  - Asma Khouaja
AU  - Ahmed Koubaa
AU  - Hachmi Ben Daly
PY  - 2026
DA  - 2026/10/12
JO  - Chemosphere
DO  - 10.1016/j.chemosphere.2025.144415
UR  - https://hal.science/hal-05795994v1
AB  - Natural biocomposites offer promising alternatives to petroleum-based composites thanks to their biocompatibility, sustainability, and low environmental impact. However, they must also demonstrate competitive mechanical properties and adaptability to manufacturing processes. To this end, we developed cellulosic biocomposites using plasticized cellulose acetate (PCA) reinforced with cellulosic fibers at loadings from 30 to 50 wt%. Mechanical properties were determined with tensile, bending, and impact tests and interfacial bonding was analyzed using scanning electron microscopy (SEM). Results showed that the adhesion of 50 wt% cellulose fibers increased the Young's modulus of the biocomposites by 300 % and the tensile strength by 12 %. Flexural properties also improved: the flexural modulus increased from 1.52 GPa to 5 GPa for PCA at maximum fiber loading, and from 43.3 MPa to 54 MPa for flexural strength. However, the elongation at break decreased with increasing cellulose content, from 13.5 % to 0.8 %, along with a 74 % decrease in impact strength. SEM results revealed good fiber dispersion, interfacial adhesion, porosity, and fiber pullout. These results underscore the potential for cellulose biocomposites as eco-friendly alternatives for high-value utilizations, including electronic and dielectric applications.
SN  - 0045-6535
SN  - 1879-1298
ER  -

Abstract

Related

Cite