Polysulfone mixed matrix membranes embedded with sub-25 nm NH2-MIL-101(Cr) for enhanced divalent salt separation and permeability
- 1Department of Chemistry, Faculty of Science, Umm Al-Qura University Makkah Saudi Arabia +00201002535379
- 2Suez University, Faculty of Science, Chemistry Department 43518 Suez Egypt
Abstract
High-performance nanofiltration (NF) membranes are essential for sustainable water treatment but are often limited by the permeability-fouling trade-off. In this study, highly crystalline sub-25 nm NH2-MIL-101(Cr) nanoparticles (19–21 nm), possessing a high BET surface area (1700.18 m2 g−1) and permanent pores (2.04 nm), were hydrothermally synthesized and incorporated into polysulfone (PSF) mixed matrix membranes via phase inversion. The uniform distribution of hydrophilic NH2 groups enhanced membrane hydrophilicity, reducing the water contact angle from 76.2 ± 2° to 56.1 ± 2° at the optimum loading of 0.75 wt%. At 5 bar using a 2000 ppm feed solution, the optimized membrane achieved a water flux of 15.3 kg m−2 h−1, representing a 2.3-fold increase over pristine PSF, while maintaining high rejection of MgSO4 (86.5%) and CaSO4 (96.2%) through combined steric hindrance and Donnan exclusion mechanisms. Flux increased linearly with pressure up to 17.8 kg m−2 h−1 at 7.0 bar. Organic fouling tests with 10 ppm humic acid demonstrated excellent antifouling performance, with flux recovery ratios of 83.2% and 68.5% after the first and second alkaline cleaning cycles, respectively. These findings demonstrate that the PSF/NH2-MIL-101(Cr) mixed matrix membrane effectively overcomes the permeability-fouling trade-off, offering a promising platform for high-performance and long-term desalination applications.
Related
- Effect of a Sulfonated Poly(ether sulfone) Additive on the Bubble Point-Permeability Trade-Off of Polyethersulfone Microfiltration Membranes Prepared by Roll-to-Roll Vapor-Induced Phase Separation.
- Extended evaluation of activated carbon-embedded glucomannan membranes for the adsorption of structurally and charge-distinct dyes.
- Zwitterionic poly (amino acid methacrylate) brushes functionalized dendritic mesoporous silica nanoparticles in layer-by-layer assembled membranes for selective Ion separation
- Learning the Path to Ion Separation: A Proof-of-Concept for Machine Learning-Assisted Inverse Design (MLAID) of Nanofiltration Membranes
- Hybrid ceramic membranes for sustainable wastewater treatment: Low-Cost materials, hybrid separation mechanisms, and applications
BibTeX
@article{alshareef2026polysulfone,
title = {{Polysulfone mixed matrix membranes embedded with sub-25 nm NH2-MIL-101(Cr) for enhanced divalent salt separation and permeability}},
author = {Mubark Alshareef and Ahmed Alharbi and Mohamed S. Fahmi},
journal = {RSC advances},
year = {2026},
month = oct,
doi = {10.1039/d6ra07963f},
url = {https://europepmc.org/article/PMC/PMC13662755},
note = {CC BY},
}
RIS
TY - JOUR
TI - Polysulfone mixed matrix membranes embedded with sub-25 nm NH2-MIL-101(Cr) for enhanced divalent salt separation and permeability
AU - Mubark Alshareef
AU - Ahmed Alharbi
AU - Mohamed S. Fahmi
PY - 2026
DA - 2026/10/14
JO - RSC advances
DO - 10.1039/d6ra07963f
UR - https://europepmc.org/article/PMC/PMC13662755
AB - High-performance nanofiltration (NF) membranes are essential for sustainable water treatment but are often limited by the permeability-fouling trade-off. In this study, highly crystalline sub-25 nm NH2-MIL-101(Cr) nanoparticles (19–21 nm), possessing a high BET surface area (1700.18 m2 g−1) and permanent pores (2.04 nm), were hydrothermally synthesized and incorporated into polysulfone (PSF) mixed matrix membranes via phase inversion. The uniform distribution of hydrophilic NH2 groups enhanced membrane hydrophilicity, reducing the water contact angle from 76.2 ± 2° to 56.1 ± 2° at the optimum loading of 0.75 wt%. At 5 bar using a 2000 ppm feed solution, the optimized membrane achieved a water flux of 15.3 kg m−2 h−1, representing a 2.3-fold increase over pristine PSF, while maintaining high rejection of MgSO4 (86.5%) and CaSO4 (96.2%) through combined steric hindrance and Donnan exclusion mechanisms. Flux increased linearly with pressure up to 17.8 kg m−2 h−1 at 7.0 bar. Organic fouling tests with 10 ppm humic acid demonstrated excellent antifouling performance, with flux recovery ratios of 83.2% and 68.5% after the first and second alkaline cleaning cycles, respectively. These findings demonstrate that the PSF/NH2-MIL-101(Cr) mixed matrix membrane effectively overcomes the permeability-fouling trade-off, offering a promising platform for high-performance and long-term desalination applications.
SN - 2046-2069
ER -