Mechanical and microstructural performance of concrete containing household waste ash and silica fume after exposure to 250°C
- 1Department of Civil and Environmental Engineering, College of Engineering, King Faisal University, Al Ahsa, Saudi Arabia
- 2Department of Civil Engineering, University of Engineering and Technology (UET) Mardan, Pakistan
Abstract
The increasing demand for sustainable concrete has encouraged the utilization of waste materials. This study investigates the combined effect of household waste ash (HWA) as a partial replacement of fine aggregate (0 to 20%) and silica fume (SF) as a cement replacement (10%). The mechanical, physical, and microstructural properties of concrete were evaluated after exposure to 250 °C for 220 minutes. Concrete workability, density, water absorption, compressive strength, splitting tensile strength, ultrasonic pulse velocity (UPV), SEM and EDX analysis were used to determine the influence of HWA. The results indicate that HWA reduced the concrete workability due to the physical properties of HWA (porous and rough texture). However, all mixes maintained acceptable workability (slump greater than 50 mm). Mechanical performance improved at optimum replacement levels. The 10% HWA increased compressive strength from 39.4 MPa to 42.5 MPa (7.8%). The maximum splitting tensile strength of 3.81 MPa (7.6% increase) was achieved at 15% HWA. SEM analysis indicates that 10-15% HWA enhanced mix densification and improved the interfacial transition zone (ITZ) through filler effects. However, excessive replacement (20% HWA) resulted in a less compact microstructure. The findings conclude that 10 to 15% HWA provides an optimum balance and produces concrete with adequate mechanical strength, a refined microstructure, and acceptable thermal stability after exposure to 250 °C.
Related
- Combined Use of Sodium Bentonite and Recycled Aggregates in Concrete: Microstructural Characterization and Mechanical Performance
- Effect of quarry dust particle sizes on the mechanical and microstructural properties of concrete
- Evaluating the effectiveness of coal bottom ash on the mechanical durability and microstructural characteristics of lightweight cellular concrete
- Waste-to-resource geopolymer technology: mechanical, durability, and microstructural performance of red Mud–fly ash-stabilized black cotton soil
- Mechanical performance of steel, basalt and polyamide fiber-reinforced ultra-high-performance concrete evaluated by experiments and SHAP-based machine learning
BibTeX
@article{ahmad2026mechanical,
title = {{Mechanical and microstructural performance of concrete containing household waste ash and silica fume after exposure to 250°C}},
author = {Jawad Ahmad and Abdulmoez Al Ismaeel and Muhammad Sheraz},
journal = {Science Progress},
year = {2026},
month = sep,
doi = {10.1177/00368504261488716},
url = {https://doi.org/10.1177/00368504261488716},
note = {CC BY-NC 4.0},
}
RIS
TY - JOUR
TI - Mechanical and microstructural performance of concrete containing household waste ash and silica fume after exposure to 250°C
AU - Jawad Ahmad
AU - Abdulmoez Al Ismaeel
AU - Muhammad Sheraz
PY - 2026
DA - 2026/09/18
JO - Science Progress
DO - 10.1177/00368504261488716
UR - https://doi.org/10.1177/00368504261488716
AB - The increasing demand for sustainable concrete has encouraged the utilization of waste materials. This study investigates the combined effect of household waste ash (HWA) as a partial replacement of fine aggregate (0 to 20%) and silica fume (SF) as a cement replacement (10%). The mechanical, physical, and microstructural properties of concrete were evaluated after exposure to 250 °C for 220 minutes. Concrete workability, density, water absorption, compressive strength, splitting tensile strength, ultrasonic pulse velocity (UPV), SEM and EDX analysis were used to determine the influence of HWA. The results indicate that HWA reduced the concrete workability due to the physical properties of HWA (porous and rough texture). However, all mixes maintained acceptable workability (slump greater than 50 mm). Mechanical performance improved at optimum replacement levels. The 10% HWA increased compressive strength from 39.4 MPa to 42.5 MPa (7.8%). The maximum splitting tensile strength of 3.81 MPa (7.6% increase) was achieved at 15% HWA. SEM analysis indicates that 10-15% HWA enhanced mix densification and improved the interfacial transition zone (ITZ) through filler effects. However, excessive replacement (20% HWA) resulted in a less compact microstructure. The findings conclude that 10 to 15% HWA provides an optimum balance and produces concrete with adequate mechanical strength, a refined microstructure, and acceptable thermal stability after exposure to 250 °C.
SN - 0036-8504
SN - 2047-7163
ER -