Reconstruction of Acoustic Echoes and Their Effect on Brillouin Oscillations in Nanoscale Characterization of Supported Thin Films by Ultrafast Photoacoustics
- 1Joint Institute for High Temperatures of the Russian Academy of Sciences, Izhorskaya st. 13 Bd.2, 125412 Moscow, Russia
Abstract
The paper presents an experimental and theoretical analysis of the effects accompanying the non-contact, non-destructive nanoscale characterization of thin-film metal–dielectric structures through the substrate, using high-amplitude picosecond acoustic pulses generated by an ultrafast laser. Time-resolved reflectivity changes ΔR(t)/R0 at 793 nm are measured in the picosecond time domain using an all-optical pump-probe setup with balanced, phase-sensitive detection tuned to 0.5 kHz. For a glass-supported nanoscale nickel film, the measurements at the glass–film interface are carried out at absorbed laser fluences ranging from 1.7 to 10.3 mJ/cm2, generating peak pressures of up to several gigapascals. The ΔR(t)/R0 signal is dominated by the resulting Brillouin oscillations at a frequency of fBO = 1/TBO = 21.5 ± 0.1 GHz within the substrate, which undergo amplitude-phase modulation due to the superposition of the individual Brillouin oscillations from the acoustic pulses leaking into the substrate after reverberating in the film. Through post-processing, the obscured ΔR(t)/R0 signal of the acoustic pulses reverberating in the film at fecho = 1/Techo = 39.1 ± 0.2 GHz is reconstructed, showing excellent agreement with the reference signal directly measured at the air–film interface. It is shown that, unlike sufficiently thick submicron films, which exhibit no amplitude-phase modulation by reverberating acoustic pulses during the first several hundred picoseconds (Techo >> TBO), nanoscale films—where Techo ≈ TBO/2—cause a significant reduction in the resulting amplitude of the Brillouin oscillations in the substrate, which reaches its minimum due to destructive interference.
Related
- Dual-point-groups engineering enable multi-ultrahigh-Q resonances via Brillouin zone folding in tetramer metasurfaces
- Reconfigurable Nanoscale Material Display
- Nanoscale sensing of spatial correlations in nonequilibrium current noise
- A high-sensitivity resistance bridge for nanoscale thermal microscopy
- Ligand-Length Asymmetry Controls Nanoscale Heat Flow in Gold Janus Nanorods
BibTeX
@article{romashevskiy2026reconstruction,
title = {{Reconstruction of Acoustic Echoes and Their Effect on Brillouin Oscillations in Nanoscale Characterization of Supported Thin Films by Ultrafast Photoacoustics}},
author = {Sergey A. Romashevskiy},
journal = {Nanomaterials},
year = {2026},
month = oct,
doi = {10.3390/nano16201307},
url = {https://www.mdpi.com/2079-4991/16/20/1307},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Reconstruction of Acoustic Echoes and Their Effect on Brillouin Oscillations in Nanoscale Characterization of Supported Thin Films by Ultrafast Photoacoustics
AU - Sergey A. Romashevskiy
PY - 2026
DA - 2026/10/16
JO - Nanomaterials
DO - 10.3390/nano16201307
UR - https://www.mdpi.com/2079-4991/16/20/1307
AB - The paper presents an experimental and theoretical analysis of the effects accompanying the non-contact, non-destructive nanoscale characterization of thin-film metal–dielectric structures through the substrate, using high-amplitude picosecond acoustic pulses generated by an ultrafast laser. Time-resolved reflectivity changes ΔR(t)/R0 at 793 nm are measured in the picosecond time domain using an all-optical pump-probe setup with balanced, phase-sensitive detection tuned to 0.5 kHz. For a glass-supported nanoscale nickel film, the measurements at the glass–film interface are carried out at absorbed laser fluences ranging from 1.7 to 10.3 mJ/cm2, generating peak pressures of up to several gigapascals. The ΔR(t)/R0 signal is dominated by the resulting Brillouin oscillations at a frequency of fBO = 1/TBO = 21.5 ± 0.1 GHz within the substrate, which undergo amplitude-phase modulation due to the superposition of the individual Brillouin oscillations from the acoustic pulses leaking into the substrate after reverberating in the film. Through post-processing, the obscured ΔR(t)/R0 signal of the acoustic pulses reverberating in the film at fecho = 1/Techo = 39.1 ± 0.2 GHz is reconstructed, showing excellent agreement with the reference signal directly measured at the air–film interface. It is shown that, unlike sufficiently thick submicron films, which exhibit no amplitude-phase modulation by reverberating acoustic pulses during the first several hundred picoseconds (Techo >> TBO), nanoscale films—where Techo ≈ TBO/2—cause a significant reduction in the resulting amplitude of the Brillouin oscillations in the substrate, which reaches its minimum due to destructive interference.
SN - 2079-4991
ER -