Microstructural evolution of single-grain-like TiO2 microspheres prepared through spray drying and multi-step sintering
Abstract
The preparation of TiO2 microspheres by spray drying followed by controlled sintering was investigated. Starting from commercial rutile TiO2 nanoparticles dispersed in water, spherical microspheres with broad size distributions were produced by adjusting key spray-drying parameters, including solid concentration, gas flow, and suspension composition. The results showed that controlling the spray-drying conditions and the subsequent sintering cycle influenced the resulting microsphere size and morphology, grain evolution, and porosity. A tailored multi-step sintering approach was used to control the microstructural evolution of individual TiO2 microspheres while limiting inter-microsphere coalescence. SEM and three-dimensional nano-tomography revealed pronounced grain growth and progressive pore elimination during sintering. The grain size increased from approximately 2–5 µm at 1200 °C to 20–40 µm at 1400 °C, while ex situ nano-tomography showed a decrease in pore volume fraction from 15.9% to 1.3% over the same temperature range. In situ nano-holotomography further confirmed the progressive reduction in the connected pore network during heating. Overall, sintering at 1400 °C provided the best compromise between densification, grain growth, microsphere isolation, and preservation of the spherical morphology.
Related
- Copper smelting slag valorization in waste-derived clay ceramics: sintering behavior, microstructural evolution, engineering performance, and leaching behavior
- Multi-magnetic regulation of hollow CoNi microspheres via morphological evolution for ultrahigh electromagnetic wave absorption
- Texture and microstructural evolution in an Al-6061 alloy processed by high-pressure torsion
- Submicron CsPbBr₃ crystallites prepared through in situ moisture-driven decomposition of Cs₄PbBr₆ microcrystals
- Slip casting and stress-controlled co-sintering of a complex ceramic Al₂O₃–ZrO₂/Al₂O₃ bi-material component through bevelled interface design for electromagnetic applications
BibTeX
@article{kassas2026microstructural,
title = {{Microstructural evolution of single-grain-like TiO2 microspheres prepared through spray drying and multi-step sintering}},
author = {Ahmad Kassas and U-Chan Chung and Nicolas Penin and Julien Lesseur and Dominique Bernard and Catherine Elissalde and Mario Maglione},
journal = {Ceramics},
year = {2026},
month = oct,
doi = {10.3390/ceramics9090096},
url = {https://u-bordeaux.hal.science/hal-05788542v1},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Microstructural evolution of single-grain-like TiO2 microspheres prepared through spray drying and multi-step sintering
AU - Ahmad Kassas
AU - U-Chan Chung
AU - Nicolas Penin
AU - Julien Lesseur
AU - Dominique Bernard
AU - Catherine Elissalde
AU - Mario Maglione
PY - 2026
DA - 2026/10/09
JO - Ceramics
DO - 10.3390/ceramics9090096
UR - https://u-bordeaux.hal.science/hal-05788542v1
AB - The preparation of TiO2 microspheres by spray drying followed by controlled sintering was investigated. Starting from commercial rutile TiO2 nanoparticles dispersed in water, spherical microspheres with broad size distributions were produced by adjusting key spray-drying parameters, including solid concentration, gas flow, and suspension composition. The results showed that controlling the spray-drying conditions and the subsequent sintering cycle influenced the resulting microsphere size and morphology, grain evolution, and porosity. A tailored multi-step sintering approach was used to control the microstructural evolution of individual TiO2 microspheres while limiting inter-microsphere coalescence. SEM and three-dimensional nano-tomography revealed pronounced grain growth and progressive pore elimination during sintering. The grain size increased from approximately 2–5 µm at 1200 °C to 20–40 µm at 1400 °C, while ex situ nano-tomography showed a decrease in pore volume fraction from 15.9% to 1.3% over the same temperature range. In situ nano-holotomography further confirmed the progressive reduction in the connected pore network during heating. Overall, sintering at 1400 °C provided the best compromise between densification, grain growth, microsphere isolation, and preservation of the spherical morphology.
SN - 2571-6131
ER -