Study on the Chlorine Resistance of HDPE Pipe to Chlorinated Seawater
- 1China Nuclear Power Engineering Co., Ltd., Shengzhen 518124, China
- 2Sino-French Institute of Nuclear Engineering and Technology, Sun Yat-Sen University, Zhuhai 519082, China
- 3Suzhou Nuclear Power Research Institute Co., Ltd., Suzhou 215004, China
Abstract
High-density polyethylene (HDPE) pipes are widely used for seawater transportation. However, residual chlorine introduced for disinfection purposes can induce oxidative degradation and accelerate material failure. Existing investigations predominantly focus on HDPE aging in chlorinated freshwater, while the degradation mechanism of HDPE subjected to chlorinated seawater remains poorly documented. In this paper, chlorine-resistance tests for HDPE pipes were performed following the ASTM F2263 standard at 90 °C using real seawater with 0.2 ppm free residual chlorine. Micro-morphology, elemental distribution, and tensile properties were characterized by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), and uniaxial tensile tests. The chlorine-resistance test results revealed that HDPE pipes eventually failed in a brittle-fracture mode after long-term exposure to chlorinated seawater. Numerous axial surface-initiated microcracks formed on the pipe inner wall, while EDS line scan demonstrated that chloride ions hardly diffused into the bulk polymer matrix. Reducing hoop stress by 18% only extended failure lifetime by approximately 6%, indicating a weak linear correlation between hoop stress and failure time under the present chemo-mechanical coupling condition. This study provides experimental references for the safety evaluation of HDPE pipes serving in chlorinated seawater environments.
Related
- Confining chlorine in the cation solvation sheaths towards stable and sustainable seawater electrolysis
- Internal conversion in functionalized poly-chlorinated trityl radicals can be tuned by a characteristic high-frequency mode
- Chlorinated polyethylene nanocomposites using PCL/clay nanohybrid masterbatches
- Enhanced X-ray shielding performance of HDPE–Sb₂O₃ composites in the diagnostic dental X-ray energy range
- "Effect of modified montmorillonite on properties of chlorinated butyl rubber/polypropylene thermoplastic vulcanizates"
BibTeX
@article{cheng2026study,
title = {{Study on the Chlorine Resistance of HDPE Pipe to Chlorinated Seawater}},
author = {Chao Cheng and Yongjing Li and Jinpeng Xiao and Huan Sheng Lai and Fangjie Shi},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18202572},
url = {https://www.mdpi.com/2073-4360/18/20/2572},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Study on the Chlorine Resistance of HDPE Pipe to Chlorinated Seawater
AU - Chao Cheng
AU - Yongjing Li
AU - Jinpeng Xiao
AU - Huan Sheng Lai
AU - Fangjie Shi
PY - 2026
DA - 2026/10/01
JO - Polymers
DO - 10.3390/polym18202572
UR - https://www.mdpi.com/2073-4360/18/20/2572
AB - High-density polyethylene (HDPE) pipes are widely used for seawater transportation. However, residual chlorine introduced for disinfection purposes can induce oxidative degradation and accelerate material failure. Existing investigations predominantly focus on HDPE aging in chlorinated freshwater, while the degradation mechanism of HDPE subjected to chlorinated seawater remains poorly documented. In this paper, chlorine-resistance tests for HDPE pipes were performed following the ASTM F2263 standard at 90 °C using real seawater with 0.2 ppm free residual chlorine. Micro-morphology, elemental distribution, and tensile properties were characterized by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), and uniaxial tensile tests. The chlorine-resistance test results revealed that HDPE pipes eventually failed in a brittle-fracture mode after long-term exposure to chlorinated seawater. Numerous axial surface-initiated microcracks formed on the pipe inner wall, while EDS line scan demonstrated that chloride ions hardly diffused into the bulk polymer matrix. Reducing hoop stress by 18% only extended failure lifetime by approximately 6%, indicating a weak linear correlation between hoop stress and failure time under the present chemo-mechanical coupling condition. This study provides experimental references for the safety evaluation of HDPE pipes serving in chlorinated seawater environments.
SN - 2073-4360
ER -