Investigation on the Degradation Mechanisms and Mechanical Property Evolution of 3D-SiO2-Fiber-Reinforced Polyimide Composites After Thermal Aging
- 1Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha 410073, China
Abstract
Understanding the thermal aging behavior of SiO2f/PI composites is crucial for ensuring their reliability and longevity in high-temperature aerospace applications. In this study, the thermal aging behavior of three-dimensional quartz-fiber-reinforced polyimide (3D-SiO2f/PI) composites was investigated. The composites were fabricated through a modified prepreg compression molding (PCM) method, including a vacuum-assisted impregnation process followed by thermal compression molding. Long-term thermal aging was carried out to evaluate the high-temperature aging resistance. The flexural properties were tested with a three-point bending test method. The micromechanical characterization was performed though nanoindentation. Interfacial properties were evaluated through single-fiber push-in tests, and the interfacial shear strength (IFSS) was calculated. The thermal aging experiment results revealed that the composites maintained excellent long-term thermal stability. The PI matrix showed no detectable oxidation or thermal degradation of after 100 h aging at 350 °C, yet no significant porosity or cracks were observed for the composite. However, further prolonged thermal exposure led to significant mechanical property degradation. The flexural strength retention rates dropped to below 15% after 300 h at 350 °C or 100 h at 400 °C aging. On the other hand, 350 °C isothermal aging for 300 h led to a progressive decrease in IFSS from 128.6 MPa to near-zero. The degradation mechanism was primarily attributed to two factors: increased porosity due to thermal decomposition of the PI matrix and significant deterioration of fiber–matrix interfacial bonding strength. These findings provide critical insights into the durability prediction and failure mechanisms of 3D-SiO2f/PI composites in high-temperature usage environments.
Related
- Comparative study of chemical treatments on the mechanical and moisture absorption behavior of coccinia indica fiber-reinforced epoxy composites
- Failure investigation and degradation study of long term hydrothermally stressed PVC reinforced with ZnO nanocomposites for cable insulation applications
- Investigation of the effect of gamma radiation on the mechanical properties of nanoclay-reinforced composite plates
- PLA nanocomposites reinforced with green synthesized AgNPs: its physico-mechanical investigation
- Dynamic Interactions and Deformation Mechanisms in Nanocutting of Carbon Nanotube Reinforced Ni-Based Composites
BibTeX
@article{yang2026investigation,
title = {{Investigation on the Degradation Mechanisms and Mechanical Property Evolution of 3D-SiO2-Fiber-Reinforced Polyimide Composites After Thermal Aging}},
author = {Minglong Yang and Yadan Wu and Jiahao He and Qiujin Gu and Haitao Liu},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18202556},
url = {https://www.mdpi.com/2073-4360/18/20/2556},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Investigation on the Degradation Mechanisms and Mechanical Property Evolution of 3D-SiO2-Fiber-Reinforced Polyimide Composites After Thermal Aging
AU - Minglong Yang
AU - Yadan Wu
AU - Jiahao He
AU - Qiujin Gu
AU - Haitao Liu
PY - 2026
DA - 2026/10/17
JO - Polymers
DO - 10.3390/polym18202556
UR - https://www.mdpi.com/2073-4360/18/20/2556
AB - Understanding the thermal aging behavior of SiO2f/PI composites is crucial for ensuring their reliability and longevity in high-temperature aerospace applications. In this study, the thermal aging behavior of three-dimensional quartz-fiber-reinforced polyimide (3D-SiO2f/PI) composites was investigated. The composites were fabricated through a modified prepreg compression molding (PCM) method, including a vacuum-assisted impregnation process followed by thermal compression molding. Long-term thermal aging was carried out to evaluate the high-temperature aging resistance. The flexural properties were tested with a three-point bending test method. The micromechanical characterization was performed though nanoindentation. Interfacial properties were evaluated through single-fiber push-in tests, and the interfacial shear strength (IFSS) was calculated. The thermal aging experiment results revealed that the composites maintained excellent long-term thermal stability. The PI matrix showed no detectable oxidation or thermal degradation of after 100 h aging at 350 °C, yet no significant porosity or cracks were observed for the composite. However, further prolonged thermal exposure led to significant mechanical property degradation. The flexural strength retention rates dropped to below 15% after 300 h at 350 °C or 100 h at 400 °C aging. On the other hand, 350 °C isothermal aging for 300 h led to a progressive decrease in IFSS from 128.6 MPa to near-zero. The degradation mechanism was primarily attributed to two factors: increased porosity due to thermal decomposition of the PI matrix and significant deterioration of fiber–matrix interfacial bonding strength. These findings provide critical insights into the durability prediction and failure mechanisms of 3D-SiO2f/PI composites in high-temperature usage environments.
SN - 2073-4360
ER -