Evolution of Pigments in Artificially Aged Polyethylene Plastics: A Raman Study
Abstract
The degradation mechanisms of polymers under UV exposure and the evolution of additives are a major concern due to their potential toxicity to humans and the environment. Vibrational spectroscopies are commonly used for the analysis of these processes. Raman spectroscopy offers a key advantage by detecting both organic and inorganic compounds with enhanced sensitivity through resonance, while infrared spectroscopy is less sensitive to low‐concentration additives. This paper highlights a new qualitative method, based on Raman spectroscopy, for the investigation of the degradation path of plastics additives, in particular pigments. The limitations and advantages are discussed in detail, with a focus on Raman‐resonant amplification of the spectral signature. Applied to commercial polyethylene containing either inorganic (titanium dioxide) or organic (PR254) pigments, this approach was validated by two artificial aging configurations. Dry and humid UVA exposure was performed during 3, 7, 15, 30, 60, and 120 days. Raman spectroscopy provides access to the study of aged surface samples, where degradation occurred. More severe degradation of the polymer matrix was observed under humid conditions compared to dry exposition. The observed relative reduction in the Raman signature of pigments indicates either the release or degradation (bond breaking or oxidation) of the pigments. Examination of the aged Raman spectra revealed no significant difference between dry and humid UVA aging, suggesting that UVA radiation was the predominant. Our study demonstrates the value of resonance Raman spectroscopy in investigating the degradation processes of plastics in the environment.
Related
- Application of indigenous bacterial strains isolated from plastics-contaminated sites in high-density polyethylene degradation
- Editorial: Biodegradation of plastics and their additives
- SCREEN-LCA: Ex-ante prioritization of bio-based pathways for chemicals and plastics under a climate-mitigation objective
- Hydrogen gas (H₂) artificially generated during soil-gas sampling - Technical report
- From mercury to plastics: Earth system science and governance strategies
BibTeX
@article{dewyspelaere2026evolution,
title = {{Evolution of Pigments in Artificially Aged Polyethylene Plastics: A Raman Study}},
author = {Lucie Dewyspelaere and Lénaïk Belec and Isabelle Martin and Véronique Madigou and Olivia Gérigny and Alexandre Merlen},
journal = {Journal of Raman Spectroscopy},
year = {2026},
month = oct,
doi = {10.1002/jrs.70219},
url = {https://hal.science/hal-05836392v1},
note = {CC BY-NC-ND},
}
RIS
TY - JOUR
TI - Evolution of Pigments in Artificially Aged Polyethylene Plastics: A Raman Study
AU - Lucie Dewyspelaere
AU - Lénaïk Belec
AU - Isabelle Martin
AU - Véronique Madigou
AU - Olivia Gérigny
AU - Alexandre Merlen
PY - 2026
DA - 2026/10/21
JO - Journal of Raman Spectroscopy
DO - 10.1002/jrs.70219
UR - https://hal.science/hal-05836392v1
AB - The degradation mechanisms of polymers under UV exposure and the evolution of additives are a major concern due to their potential toxicity to humans and the environment. Vibrational spectroscopies are commonly used for the analysis of these processes. Raman spectroscopy offers a key advantage by detecting both organic and inorganic compounds with enhanced sensitivity through resonance, while infrared spectroscopy is less sensitive to low‐concentration additives. This paper highlights a new qualitative method, based on Raman spectroscopy, for the investigation of the degradation path of plastics additives, in particular pigments. The limitations and advantages are discussed in detail, with a focus on Raman‐resonant amplification of the spectral signature. Applied to commercial polyethylene containing either inorganic (titanium dioxide) or organic (PR254) pigments, this approach was validated by two artificial aging configurations. Dry and humid UVA exposure was performed during 3, 7, 15, 30, 60, and 120 days. Raman spectroscopy provides access to the study of aged surface samples, where degradation occurred. More severe degradation of the polymer matrix was observed under humid conditions compared to dry exposition. The observed relative reduction in the Raman signature of pigments indicates either the release or degradation (bond breaking or oxidation) of the pigments. Examination of the aged Raman spectra revealed no significant difference between dry and humid UVA aging, suggesting that UVA radiation was the predominant. Our study demonstrates the value of resonance Raman spectroscopy in investigating the degradation processes of plastics in the environment.
SN - 0377-0486
SN - 1097-4555
ER -