Surfactant-Free Microemulsion as Template for Stöber Silica Nanoparticle Synthesis
- 1Universität Regensburg , , ,
- 2Lehrstuhl für Physikalische Chemie II und Institut für Physikalische Chemie, RWTH Aachen , ,
Abstract
Surfactant-free microemulsions (SFMEs) have emerged as promising structured reaction media for the synthesis of inorganic nanoparticles. Recent reports suggested that the ternary water (H2O)/ethanol (EtOH)/tetraethyl orthosilicate (TEOS) system forms SFME structures capable of directing silica particle formation through a self-templating mechanism. Here, we systematically investigate this hypothesis and evaluate the influence of SFME structuring on Stöber silica nanoparticle synthesis. Ternary and pseudoternary phase diagrams of H2O/EtOH/TEOS and H2O/EtOH/(oil + TEOS) systems were established and characterized by dynamic light scattering (DLS), small- and wide-angle X-ray scattering (SWAXS), and transmission electron microscopy (TEM). The H2O/EtOH/TEOS system was found to remain molecularly dispersed throughout the investigated monophasic region and showed no evidence of SFME aggregate formation. Consequently, silica particle formation in this system follows conventional Stöber-type kinetics rather than a self-templating mechanism. Nevertheless, synthesis at high water contents and low ammonia concentrations produced highly monodisperse silica nanoparticles in the low-nanometer size range and enabled controlled particle growth through regrowth steps. In contrast, genuine SFME systems containing toluene or 1-octanol exhibited pronounced mesoscale structuring in the pre-Ouzo and bicontinuous regions, which strongly affected nucleation and growth behavior. Time-resolved DLS measurements revealed induction periods and growth regimes characteristic of compartmentalized reaction environments, resulting in particle sizes ranging from a few nanometers to several hundred nanometers, depending on microstructure and oil composition. The results demonstrate that SFME structures do not template particle formation in the H2O/EtOH/TEOS system but can substantially modify Stöber kinetics when a genuine mesoscale organization is present. A mechanistic model is proposed in which diffusion of hydrolyzed silica species across the SFME interphase governs nucleation and growth, establishing interfacial mass transport as a key parameter for controlling silica nanoparticle formation in structured solvents.
Related
- Dendritic Mesoporous Silica Nanoparticle-Based Co-Delivery of a Repellent and an Insecticide for Management of the Asian Citrus Psyllid
- Design meets simplicity: employing anhydrous precursors in microwave synthesis of NaGdF₄:Yb³⁺,Tm³⁺ upconverting nanoparticles and their deposition inside mesoporous titania or silica thin films through spin-coating
- Innovative AuAg bimetallic nanoparticle synthesis using food waste materials: its biological applications and photocatalytic degradation potentials
- Microbial Pyrolysis for the Sustainable Synthesis of Nanoparticle-Embedded Carbon Electrocatalysts
- Surfactant-free electrochemical synthesis of layered Ag/Au bimetallic nanostructures as SERS platforms with DFT insights into their interfacial charge transfer mechanism.
BibTeX
@article{rodig2026surfactantfree,
title = {{Surfactant-Free Microemulsion as Template for Stöber Silica Nanoparticle Synthesis}},
author = {Bastian Rödig and Lena Schmauser and Patrick Denk and Werner Kunz},
journal = {ACS Omega},
year = {2026},
month = oct,
doi = {10.1021/acsomega.6c08994},
url = {https://pubs.acs.org/acsodf/article/11/42/65735/5449777/Surfactant-Free-Microemulsion-as-Template-for-Sto},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Surfactant-Free Microemulsion as Template for Stöber Silica Nanoparticle Synthesis
AU - Bastian Rödig
AU - Lena Schmauser
AU - Patrick Denk
AU - Werner Kunz
PY - 2026
DA - 2026/10/13
JO - ACS Omega
DO - 10.1021/acsomega.6c08994
UR - https://pubs.acs.org/acsodf/article/11/42/65735/5449777/Surfactant-Free-Microemulsion-as-Template-for-Sto
AB - Surfactant-free microemulsions (SFMEs) have emerged as promising structured reaction media for the synthesis of inorganic nanoparticles. Recent reports suggested that the ternary water (H2O)/ethanol (EtOH)/tetraethyl orthosilicate (TEOS) system forms SFME structures capable of directing silica particle formation through a self-templating mechanism. Here, we systematically investigate this hypothesis and evaluate the influence of SFME structuring on Stöber silica nanoparticle synthesis. Ternary and pseudoternary phase diagrams of H2O/EtOH/TEOS and H2O/EtOH/(oil + TEOS) systems were established and characterized by dynamic light scattering (DLS), small- and wide-angle X-ray scattering (SWAXS), and transmission electron microscopy (TEM). The H2O/EtOH/TEOS system was found to remain molecularly dispersed throughout the investigated monophasic region and showed no evidence of SFME aggregate formation. Consequently, silica particle formation in this system follows conventional Stöber-type kinetics rather than a self-templating mechanism. Nevertheless, synthesis at high water contents and low ammonia concentrations produced highly monodisperse silica nanoparticles in the low-nanometer size range and enabled controlled particle growth through regrowth steps. In contrast, genuine SFME systems containing toluene or 1-octanol exhibited pronounced mesoscale structuring in the pre-Ouzo and bicontinuous regions, which strongly affected nucleation and growth behavior. Time-resolved DLS measurements revealed induction periods and growth regimes characteristic of compartmentalized reaction environments, resulting in particle sizes ranging from a few nanometers to several hundred nanometers, depending on microstructure and oil composition. The results demonstrate that SFME structures do not template particle formation in the H2O/EtOH/TEOS system but can substantially modify Stöber kinetics when a genuine mesoscale organization is present. A mechanistic model is proposed in which diffusion of hydrolyzed silica species across the SFME interphase governs nucleation and growth, establishing interfacial mass transport as a key parameter for controlling silica nanoparticle formation in structured solvents.
SN - 2470-1343
ER -