Gd3+-Driven Microstructure Regulation of Tm3+, Yb3+: GdxBi2−xWO6 for High-Sensitivity Temperature Sensing and Magnetism
- 1School of Physics and Electronic Engineering, Xinjiang Normal University, Urumqi 830054, China
- 2Xinjiang Key Laboratory for Luminescence Minerals and Optical Functional Materials, Xinjiang Normal University, Urumqi 830054, China
Abstract
Tm3+, Yb3+: GdxBi2−xWO6 series upconversion luminescent materials were synthesized via a solid-state method. Calculations and XRD analysis reveal that Gd3+ in the lattice exhibits both substitutional and interstitial doping. Compared with the NaYF4 matrix, the Bi2WO6 material doped with Gd3+ has a lower Debye temperature (392.45 K), and the maximum phonon energy is low; thus, the probability of nonradiative transitions decreases. SEM images and EDS results reveal that the powder particle size ranges from 0.5 to 3 μm and that the elements are evenly distributed on the surface. The diffuse reflectance absorption spectra indicate that moderate Tm3+, Yb3+ and Gd3+ doping shifts the absorption band of the material towards longer wavelengths and decreases the band gaps. Under 980 nm laser excitation and a Gd3+ doping concentration of x = 0.2, the emission intensities of Tm3+ at 476 nm, 683 nm, 703 nm, and 804 nm increase by 1.8, 1.24, 1.35, and 81.9 times, respectively. Calculations reveal that these emissions in the range of 450 to 850 nm originate from three-photon or two-photon absorption. Gd3+ codoping can prolong the lifetime of the Tm3+ energy levels. When this sample was excited at 980 nm (518 mW), the temperature was characterized by FIR703nm/476nm from 298 K to 573 K, and the obtained maximum relative sensitivity was 3.4907 K−1 (298 K). The minimum temperature resolution was 0.0083 K (298 K). Compared with that of the undoped Gd3+ sample, the temperature sensitivity of the Gd3+-codoped sample increased by 92.35 times. Under an external magnetic field of 20 kOe and a temperature of 300 K, the magnetization of the sample doped with Gd3+ increased fourfold to 0.08174 emu/g. This material has potential applications in temperature sensing and magnetic resonance imaging.
Related
- Enabling the High-Volume Utilization of Iron-Rich Sewage Sludge Ash in Cement: The Role of Curing Temperature in Microstructure and Performance Enhancement
- Effect of pyrolysis temperature on the microstructure and thermal conductivity of polymer-derived monolithic and porous SiC ceramics
- Microstructure and high-temperature oxidation behaviour of HVOF and plasma sprayed Ni–Cr-based ceramic coatings on SA516 boiler steel
- High Fidelity Stochastic Electrode Microstructure Generation for Low Temperature Electrochemical Systems
- Hard carbon anodes for sodium-ion batteries: from mechanistic reconciliation, precursor-tailored microstructure regulation to industrial scale-up
BibTeX
@article{feng2026gd3driven,
title = {{Gd3+-Driven Microstructure Regulation of Tm3+, Yb3+: GdxBi2−xWO6 for High-Sensitivity Temperature Sensing and Magnetism}},
author = {Xin Feng and Linxiang Wang and Jiachen Shi and Mengliang Jiang and Munire Maimaiti and Yan Zhang and Yue Bai},
journal = {Molecules (Basel, Switzerland)},
year = {2026},
month = oct,
doi = {10.3390/molecules31193557},
url = {https://europepmc.org/article/PMC/PMC13667120},
note = {CC BY},
}
RIS
TY - JOUR
TI - Gd3+-Driven Microstructure Regulation of Tm3+, Yb3+: GdxBi2−xWO6 for High-Sensitivity Temperature Sensing and Magnetism
AU - Xin Feng
AU - Linxiang Wang
AU - Jiachen Shi
AU - Mengliang Jiang
AU - Munire Maimaiti
AU - Yan Zhang
AU - Yue Bai
PY - 2026
DA - 2026/10/01
JO - Molecules (Basel, Switzerland)
DO - 10.3390/molecules31193557
UR - https://europepmc.org/article/PMC/PMC13667120
AB - Tm3+, Yb3+: GdxBi2−xWO6 series upconversion luminescent materials were synthesized via a solid-state method. Calculations and XRD analysis reveal that Gd3+ in the lattice exhibits both substitutional and interstitial doping. Compared with the NaYF4 matrix, the Bi2WO6 material doped with Gd3+ has a lower Debye temperature (392.45 K), and the maximum phonon energy is low; thus, the probability of nonradiative transitions decreases. SEM images and EDS results reveal that the powder particle size ranges from 0.5 to 3 μm and that the elements are evenly distributed on the surface. The diffuse reflectance absorption spectra indicate that moderate Tm3+, Yb3+ and Gd3+ doping shifts the absorption band of the material towards longer wavelengths and decreases the band gaps. Under 980 nm laser excitation and a Gd3+ doping concentration of x = 0.2, the emission intensities of Tm3+ at 476 nm, 683 nm, 703 nm, and 804 nm increase by 1.8, 1.24, 1.35, and 81.9 times, respectively. Calculations reveal that these emissions in the range of 450 to 850 nm originate from three-photon or two-photon absorption. Gd3+ codoping can prolong the lifetime of the Tm3+ energy levels. When this sample was excited at 980 nm (518 mW), the temperature was characterized by FIR703nm/476nm from 298 K to 573 K, and the obtained maximum relative sensitivity was 3.4907 K−1 (298 K). The minimum temperature resolution was 0.0083 K (298 K). Compared with that of the undoped Gd3+ sample, the temperature sensitivity of the Gd3+-codoped sample increased by 92.35 times. Under an external magnetic field of 20 kOe and a temperature of 300 K, the magnetization of the sample doped with Gd3+ increased fourfold to 0.08174 emu/g. This material has potential applications in temperature sensing and magnetic resonance imaging.
SN - 1420-3049
ER -