Synergistic Effect of Citrate and EDTA Electrolyte Additives Mixture on the Discharge Behavior of AZ31 Anode in Mg–Air Batteries
- 1Department of Mechanical Engineering, Sami Shamoon College of Engineering, Ashdod 77245, Israel
- 2Energy Engineering Unit, Ben-Gurion University of the Negev, Beer-Sheva 84105, Israel
Abstract
The performance of aqueous Mg–air batteries is determined by the interplay between magnesium dissolution, self-corrosion, and Mg(OH)2 surface passivation. Electrolyte additives that enhance one of these processes often compromise the others, making it difficult to simultaneously improve discharge voltage and operational stability. The effective regulation of this trade-off was investigated using two Mg-complexing ligands with complementary complexation properties. Citrate (CIT) and ethylenediaminetetraacetic acid (EDTA) were systematically investigated, individually and in combination, in a 3.5 wt% NaCl electrolyte under a discharge current density of 30 mA/cm2. Electrochemical characterization, hydrogen evolution measurements during discharge, discharge testing, post-discharge surface characterization, three-dimensional surface topography, and in situ visualization using the metal-ion indicator Eriochrome Black T (EBT) were employed to reveal the fundamental processes at the Mg anode–electrolyte interface that determine battery discharge behavior. The mixed electrolyte containing 0.15 M CIT and 0.15 M EDTA exhibited superior overall discharge performance, maintaining 804 mV after 35 h of discharge, compared with 584 mV for the EDTA electrolyte under identical conditions, whereas complete discharge occurred after only 16.5 h in the CIT electrolyte. Potentiodynamic polarization and electrochemical impedance spectroscopy revealed enhanced anodic dissolution together with the lowest film and charge-transfer resistances. Surface characterization confirmed increased magnesium dissolution and delayed Mg(OH)2 passivation, while hydrogen evolution measurements demonstrated that the improved discharge performance was accompanied by increased self-corrosion. In situ visualization using the metal-ion indicator EBT further revealed the evolution of Mg–ligand complexation, progressive EDTA depletion, and electrolyte pH during discharge. The combined experimental evidence supports a cooperative complexation mechanism, in which the presence of both CIT and EDTA in the electrolyte modulates the Mg anode–electrolyte interface and facilitates the preferential complexation of dissolved Mg ions in the bulk electrolyte. Their complementary functions coordinate magnesium dissolution with delayed surface passivation, thereby regulating the evolution of the anode/electrolyte interface and maintaining an electrochemically active anode throughout discharge.
Related
- How to Discover New Electrolyte Additives for Lithium Batteries: A Computational Roadmap
- Graphene-Confined Silicon and a Li6.5La3Zr1.5Ta0.5O12-Reinforced Plasticized Poly(ethylene oxide) Electrolyte Enable Contact-Stable Solid-State Lithium Batteries
- Computational Modeling of Electrolytes and the Solid–Electrolyte Interphase (SEI) in Li-Ion Batteries: A 30-Year Odyssey from DFT/MD/MC to AI–A Comprehensive Review
- Interfacial engineering in sulfide-based all-solid-state batteries: from cathode/anode interfaces to electrolyte modification
- Stable lithium/electrolyte interphase enabled by tailoring Li+ solvation structure and FEC additive in LiOTf/LiNO3 dual-salt sulfolane-based nonflammable electrolyte for lithium metal batteries
BibTeX
@article{bason2026synergistic,
title = {{Synergistic Effect of Citrate and EDTA Electrolyte Additives Mixture on the Discharge Behavior of AZ31 Anode in Mg–Air Batteries}},
author = {Shani Abtan Bason and Guy Ben Hamu},
journal = {Batteries},
year = {2026},
month = oct,
doi = {10.3390/batteries12100395},
url = {https://www.mdpi.com/2313-0105/12/10/395},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Synergistic Effect of Citrate and EDTA Electrolyte Additives Mixture on the Discharge Behavior of AZ31 Anode in Mg–Air Batteries
AU - Shani Abtan Bason
AU - Guy Ben Hamu
PY - 2026
DA - 2026/10/04
JO - Batteries
DO - 10.3390/batteries12100395
UR - https://www.mdpi.com/2313-0105/12/10/395
AB - The performance of aqueous Mg–air batteries is determined by the interplay between magnesium dissolution, self-corrosion, and Mg(OH)2 surface passivation. Electrolyte additives that enhance one of these processes often compromise the others, making it difficult to simultaneously improve discharge voltage and operational stability. The effective regulation of this trade-off was investigated using two Mg-complexing ligands with complementary complexation properties. Citrate (CIT) and ethylenediaminetetraacetic acid (EDTA) were systematically investigated, individually and in combination, in a 3.5 wt% NaCl electrolyte under a discharge current density of 30 mA/cm2. Electrochemical characterization, hydrogen evolution measurements during discharge, discharge testing, post-discharge surface characterization, three-dimensional surface topography, and in situ visualization using the metal-ion indicator Eriochrome Black T (EBT) were employed to reveal the fundamental processes at the Mg anode–electrolyte interface that determine battery discharge behavior. The mixed electrolyte containing 0.15 M CIT and 0.15 M EDTA exhibited superior overall discharge performance, maintaining 804 mV after 35 h of discharge, compared with 584 mV for the EDTA electrolyte under identical conditions, whereas complete discharge occurred after only 16.5 h in the CIT electrolyte. Potentiodynamic polarization and electrochemical impedance spectroscopy revealed enhanced anodic dissolution together with the lowest film and charge-transfer resistances. Surface characterization confirmed increased magnesium dissolution and delayed Mg(OH)2 passivation, while hydrogen evolution measurements demonstrated that the improved discharge performance was accompanied by increased self-corrosion. In situ visualization using the metal-ion indicator EBT further revealed the evolution of Mg–ligand complexation, progressive EDTA depletion, and electrolyte pH during discharge. The combined experimental evidence supports a cooperative complexation mechanism, in which the presence of both CIT and EDTA in the electrolyte modulates the Mg anode–electrolyte interface and facilitates the preferential complexation of dissolved Mg ions in the bulk electrolyte. Their complementary functions coordinate magnesium dissolution with delayed surface passivation, thereby regulating the evolution of the anode/electrolyte interface and maintaining an electrochemically active anode throughout discharge.
SN - 2313-0105
ER -