Hydrogen Compatibility of Commercial Silicone Elastomer Seals: Multiscale Mechanical and Surface Characterization Following High-Pressure Hydrogen Exposure
- 1School of Aerospace and Mechanical Engineering, University of Oklahoma, Norman, OK 73019, USA
Abstract
Commercial silicone O-rings were exposed to hydrogen pressures up to 7000 psi for 192 h and evaluated using mechanical, data-driven, and microstructural characterization. ASTM D1414-based O-ring tensile testing was complemented by multivariate and functional analyses, while surface evolution was quantified using SEM-based image analysis and spatial statistics. Inclusion of an unexposed 0 psi mechanical control revealed a non-monotonic exposure-associated response. Several hydrogen-exposed groups exhibited greater ultimate elongation, tensile toughness, and structural loading work than the unexposed control, whereas these quantities decreased at 7000 psi relative to selected lower-pressure exposed groups. Welch ANOVA identified significant overall group effects for tensile strength, ultimate elongation, toughness, and structural loading work. The normalized tensile-curve shapes and several stiffness-related descriptors showed smaller relative differences than the failure-related properties. These results demonstrate that hydrogen exposure was associated with changes in deformability and failure response, but the tensile data alone do not establish the molecular mechanism responsible for these changes. Quantitative SEM analysis revealed pressure-associated differences in localized morphology and spatial organization, including a tendency toward reduced dark-feature number density and variation in the magnitude and length scale of feature clustering among the analyzed conditions, without evidence of catastrophic surface degradation in the examined SEM fields. Overall, the investigated silicone exhibited non-monotonic exposure-associated changes in mechanical response together with localized pressure-associated surface evolution, without evidence of catastrophic surface degradation in the analyzed SEM fields. These findings provide comparative post-exposure material-response data for commercial silicone O-rings under high-pressure hydrogen conditions.
Related
- Influences of TiO₂ and SiO₂ nanofillers on the mechanical performance of a maxillofacial silicone elastomer after two years of outdoor tropical weathering: An in vitro study
- Comparative Analysis of Starch-Based Films Functionalized with Bixa orellana Fruit and Leaf Extracts: A Multiscale Structural, Morphological, and Optical Characterization
- Degradation Behavior of NBR Seals Exposed to Halogenated Olefins under Coupled Thermal and Mechanical Loads: A Multiscale Experimental and Computational Study
- Electrochemical Characterization and DRT-Guided ECM Modeling of Commercial Sodium-Ion 18650 Cells
- Mechanical Prediction of Shale Oil Reservoirs Based on Micromechanical Characterization, Machine Learning, and Upscaling Model
BibTeX
@article{subedi2026hydrogen,
title = {{Hydrogen Compatibility of Commercial Silicone Elastomer Seals: Multiscale Mechanical and Surface Characterization Following High-Pressure Hydrogen Exposure}},
author = {Nitesh Subedi and Alfredo Becerril Corral and Md. Ariful Islam and Md. Monjur Hossain Bhuiyan and Zahed Siddique},
journal = {Polymers},
year = {2026},
month = nov,
doi = {10.3390/polym18212733},
url = {https://www.mdpi.com/2073-4360/18/21/2733},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Hydrogen Compatibility of Commercial Silicone Elastomer Seals: Multiscale Mechanical and Surface Characterization Following High-Pressure Hydrogen Exposure
AU - Nitesh Subedi
AU - Alfredo Becerril Corral
AU - Md. Ariful Islam
AU - Md. Monjur Hossain Bhuiyan
AU - Zahed Siddique
PY - 2026
DA - 2026/11/03
JO - Polymers
DO - 10.3390/polym18212733
UR - https://www.mdpi.com/2073-4360/18/21/2733
AB - Commercial silicone O-rings were exposed to hydrogen pressures up to 7000 psi for 192 h and evaluated using mechanical, data-driven, and microstructural characterization. ASTM D1414-based O-ring tensile testing was complemented by multivariate and functional analyses, while surface evolution was quantified using SEM-based image analysis and spatial statistics. Inclusion of an unexposed 0 psi mechanical control revealed a non-monotonic exposure-associated response. Several hydrogen-exposed groups exhibited greater ultimate elongation, tensile toughness, and structural loading work than the unexposed control, whereas these quantities decreased at 7000 psi relative to selected lower-pressure exposed groups. Welch ANOVA identified significant overall group effects for tensile strength, ultimate elongation, toughness, and structural loading work. The normalized tensile-curve shapes and several stiffness-related descriptors showed smaller relative differences than the failure-related properties. These results demonstrate that hydrogen exposure was associated with changes in deformability and failure response, but the tensile data alone do not establish the molecular mechanism responsible for these changes. Quantitative SEM analysis revealed pressure-associated differences in localized morphology and spatial organization, including a tendency toward reduced dark-feature number density and variation in the magnitude and length scale of feature clustering among the analyzed conditions, without evidence of catastrophic surface degradation in the examined SEM fields. Overall, the investigated silicone exhibited non-monotonic exposure-associated changes in mechanical response together with localized pressure-associated surface evolution, without evidence of catastrophic surface degradation in the analyzed SEM fields. These findings provide comparative post-exposure material-response data for commercial silicone O-rings under high-pressure hydrogen conditions.
SN - 2073-4360
ER -