Exploring the thermal and mechanical performance of hybrid bio composites reinforced with agro waste fibers and Turbinella pyrum shell powder
Abstract
The use of sustainable natural fiber-reinforced polymer composites has attracted considerable attention mainly because they are environmentally friendly and can replace heavy components in engineering. The present work involves making hybrid epoxy composites reinforced with banana stem fiber (BSF), sugarcane bagasse fiber (SCF), and Turbinella pyrum shell (TPS) powder by the vacuum-assisted resin infusion technique. Nine composite samples (S1-S9) were made by changing fiber and TPS filler amounts to study the mechanical, thermal, moisture resistance, and morphological properties of the composites. The study found that the addition of the TPS filler might be the biggest reason for the composite’s better performance, which increased with filler content up to a maximum of 3 wt%. S6 showed the best tensile strength (20.0 MPa), tensile modulus (2.95 GPa), flexural strength (49.8 MPa), flexural modulus (4.48 GPa), and impact strength (8.1 kJ/m ² ); these properties were 332.9%, 136.0%, 255.7%, 250.0%, and approximately 523.1% better than the unfilled S1 formulation. S5, in contrast, has the highest compressive strength (9.40 MPa), compressive modulus (1.34 GPa), and minimum moisture absorption (1.95%), which indicates very good resistance to water. The composite formulation with the lowest weight and highest strength was selected, based on different performance criteria (mechanical, thermal, and moisture resistance), by multi-response optimization. It was revealed that S6 was the composite formulation showing the most balanced characteristics. Thermogravimetric studies showed that the composites with TPS filler have better thermal capability, and SEM imaging revealed discrepancies among composite samples for fibre pull-out, void presence, filler dispersion, and the nature of the crack. EDX analysis was used to detect the calcium carbonate (CaCO ₃ ) enriched material of the TPS filler, and its contribution towards the increase of composites’ stiffness and thermal resistance was acknowledged. These results portray the possibility of using TPS-filled hybrid epoxy composites as green products for lightweight structural and engineering applications.
Related
- Mechanical performance of natural fiber reinforced polymer composites with critical assessment of recent advances and future perspectives
- Mechanical performance and eco-efficiency of thermoplastic polyurethane composites reinforced with recycled tire rubber
- Overcoming the Performance Cliff at High Loadings: Enhanced Mechanical, Dielectric, and Rheological Properties of PBT Composites Reinforced with Flat Glass Fibers
- Comparative study of chemical treatments on the mechanical and moisture absorption behavior of coccinia indica fiber-reinforced epoxy composites
- From Reinforcement to Prediction: Mechanical Behavior and Modeling of CNT-Reinforced Cementitious Composites
BibTeX
@article{maniraj2026exploring,
title = {{Exploring the thermal and mechanical performance of hybrid bio composites reinforced with agro waste fibers and Turbinella pyrum shell powder}},
author = {J. Maniraj and A. Arunkumar and B. Deeban and S. Venkatesh and P. Baranitharan and Malinee Sriariyanun and U. Elaiyarasan and Mamaru Wutabachew Yeshachew},
journal = {Scientific Reports},
year = {2026},
month = oct,
doi = {10.1038/s41598-026-77514-5},
url = {https://www.nature.com/articles/s41598-026-77514-5},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Exploring the thermal and mechanical performance of hybrid bio composites reinforced with agro waste fibers and Turbinella pyrum shell powder
AU - J. Maniraj
AU - A. Arunkumar
AU - B. Deeban
AU - S. Venkatesh
AU - P. Baranitharan
AU - Malinee Sriariyanun
AU - U. Elaiyarasan
AU - Mamaru Wutabachew Yeshachew
PY - 2026
DA - 2026/10/24
JO - Scientific Reports
DO - 10.1038/s41598-026-77514-5
UR - https://www.nature.com/articles/s41598-026-77514-5
AB - The use of sustainable natural fiber-reinforced polymer composites has attracted considerable attention mainly because they are environmentally friendly and can replace heavy components in engineering. The present work involves making hybrid epoxy composites reinforced with banana stem fiber (BSF), sugarcane bagasse fiber (SCF), and Turbinella pyrum shell (TPS) powder by the vacuum-assisted resin infusion technique. Nine composite samples (S1-S9) were made by changing fiber and TPS filler amounts to study the mechanical, thermal, moisture resistance, and morphological properties of the composites. The study found that the addition of the TPS filler might be the biggest reason for the composite’s better performance, which increased with filler content up to a maximum of 3 wt%. S6 showed the best tensile strength (20.0 MPa), tensile modulus (2.95 GPa), flexural strength (49.8 MPa), flexural modulus (4.48 GPa), and impact strength (8.1 kJ/m ² ); these properties were 332.9%, 136.0%, 255.7%, 250.0%, and approximately 523.1% better than the unfilled S1 formulation. S5, in contrast, has the highest compressive strength (9.40 MPa), compressive modulus (1.34 GPa), and minimum moisture absorption (1.95%), which indicates very good resistance to water. The composite formulation with the lowest weight and highest strength was selected, based on different performance criteria (mechanical, thermal, and moisture resistance), by multi-response optimization. It was revealed that S6 was the composite formulation showing the most balanced characteristics. Thermogravimetric studies showed that the composites with TPS filler have better thermal capability, and SEM imaging revealed discrepancies among composite samples for fibre pull-out, void presence, filler dispersion, and the nature of the crack. EDX analysis was used to detect the calcium carbonate (CaCO ₃ ) enriched material of the TPS filler, and its contribution towards the increase of composites’ stiffness and thermal resistance was acknowledged. These results portray the possibility of using TPS-filled hybrid epoxy composites as green products for lightweight structural and engineering applications.
SN - 2045-2322
ER -