Effect of Acrylic Emulsion on Drying Shrinkage, Mechanical Properties, and Hydration Behavior of UHPC Matrix.
- 1School of Future Transportation, Guangzhou Maritime University, Guangzhou 510725, China.
- 2School of Civil Engineering and Transportation, Foshan University, Foshan 528200, China.
Abstract
Significant drying shrinkage and early-age cracking have remained critical constraints to the broader application of ultra-high performance concrete (UHPC). This study attempted to address these limitations through the addition of acrylic emulsion (AE), and the influence of its content (0-10 wt.%) on the setting time, mechanical properties, drying shrinkage, hydration behavior, and microstructure of UHPC matrix was systematically investigated. The results show that AE addition delayed setting and early hydration, substantially reducing cumulative heat release and thereby lowering the risk of thermal cracking. AE incorporation reduced compressive strength, and this adverse effect became more pronounced at higher dosages. In contrast, the formation of intertwining polymer films within the hydration products provided effective pore-filling and "micro-fibre" effects, which enhanced flexural strength development and alleviated drying shrinkage that originates principally from moisture loss within the C-S-H gel. At an optimal dosage of 5 wt.%, AE reduced the 14-day and 90-day drying shrinkage of UHPC matrix by 28% and 25%, respectively, while increasing the 90-day flexural strength by approximately 3%. However, a further increase in the dosage deteriorated overall performance, primarily because excessive polymer promoted agglomeration and introduced more air bubbles. These findings provide a theoretical foundation for designing low-shrinkage, low-heat-release UHPC tailored for large-volume engineering structures.
Related
- Internal Curing Effect of Pre-Wetted Coal Gangue Powder on Hydration and Shrinkage Behavior of Cement–Fly Ash Composite Materials
- Enhanced mechanical properties and reduced polymerization shrinkage in a light-cured flowable dental nanocomposite via incorporation of silane-functionalized ScYSZ nanoparticles
- Thermally Activated Shrinkage of Heat-Shrinkable Fibers and Its Influence on Drying Shrinkage and Mechanical Properties of Cement Mortar
- Multifunctional Properties of Novel X2FeH5 Hydrides (X = Ca, Mg, Ba): A First-Principles Study of Hydrogen Storage, Electronic, Optical, and Mechanical Behavior
- Effects of hydrothermal aging on the wear behavior, mechanical properties, and microstructure of a multilayered zirconia
BibTeX
@article{fan2026effect,
title = {{Effect of Acrylic Emulsion on Drying Shrinkage, Mechanical Properties, and Hydration Behavior of UHPC Matrix.}},
author = {Jie Fan and Sijie Deng and Gengying Li and Yong Yu},
journal = {Gels (Basel, Switzerland)},
year = {2026},
month = oct,
doi = {10.3390/gels12100926},
url = {https://europepmc.org/article/MED/42929960},
note = {CC BY},
}
RIS
TY - JOUR
TI - Effect of Acrylic Emulsion on Drying Shrinkage, Mechanical Properties, and Hydration Behavior of UHPC Matrix.
AU - Jie Fan
AU - Sijie Deng
AU - Gengying Li
AU - Yong Yu
PY - 2026
DA - 2026/10/15
JO - Gels (Basel, Switzerland)
DO - 10.3390/gels12100926
UR - https://europepmc.org/article/MED/42929960
AB - Significant drying shrinkage and early-age cracking have remained critical constraints to the broader application of ultra-high performance concrete (UHPC). This study attempted to address these limitations through the addition of acrylic emulsion (AE), and the influence of its content (0-10 wt.%) on the setting time, mechanical properties, drying shrinkage, hydration behavior, and microstructure of UHPC matrix was systematically investigated. The results show that AE addition delayed setting and early hydration, substantially reducing cumulative heat release and thereby lowering the risk of thermal cracking. AE incorporation reduced compressive strength, and this adverse effect became more pronounced at higher dosages. In contrast, the formation of intertwining polymer films within the hydration products provided effective pore-filling and "micro-fibre" effects, which enhanced flexural strength development and alleviated drying shrinkage that originates principally from moisture loss within the C-S-H gel. At an optimal dosage of 5 wt.%, AE reduced the 14-day and 90-day drying shrinkage of UHPC matrix by 28% and 25%, respectively, while increasing the 90-day flexural strength by approximately 3%. However, a further increase in the dosage deteriorated overall performance, primarily because excessive polymer promoted agglomeration and introduced more air bubbles. These findings provide a theoretical foundation for designing low-shrinkage, low-heat-release UHPC tailored for large-volume engineering structures.
SN - 2310-2861
ER -