Influence of Low TiO2 Nanoparticle Loading on Electrospun sPEEK Fiber Morphology and Chemistry and on the Tensile Properties of Corresponding Solution-Cast Membranes
4 affiliations
- 1Departamento de Ciencias de la Energía y Mecánica, Universidad de las Fuerzas Armadas ESPE, Sangolquí 171103, Ecuador
- 2Centro de Nanociencia y Nanotecnología, Universidad de las Fuerzas Armadas ESPE, Sangolquí 171103, Ecuador
- 3Department of Mechanical Engineering, Universidad San Francisco de Quito USFQ, Quito 170901, Ecuador
- 4School of Engineering and Sciences, Tecnologico de Monterrey, Monterrey 64849, Mexico
Abstract
Polymer matrix composites (PMCs) have garnered importance due to their unique combination of mechanical, thermal, and functional properties. However, their performance depends on overcoming challenges related to dispersion, bonding, and processing. Electrospinning is an advanced technique for producing nanofiber or microfiber PMCs. One of the key challenges in electrospun PMCs is the uniform dispersion of reinforcement materials like TiO2 nanoparticles within the polymer matrix. A Taguchi orthogonal design (L16) was used to evaluate the effects of needle-to-collector distance, applied voltage, and flow rate on mean fiber diameter and deposition quality. Scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FT-IR) were used to characterize electrospun neat sulfonated poly(ether ether ketone) (sPEEK) and sPEEK/TiO2 fibers, whereas tensile tests were performed on solution-cast membranes prepared from the corresponding formulations. The lowest observed run mean diameter was 204.6695 nm at 8 kV, 1.25 mL h−1, and a needle-to-collector distance of 12 cm; this run was also selected for deposition quality. Neat sPEEK membranes exhibited a mean tensile strength of 35.3 MPa, a mean apparent tensile modulus of 476 MPa, and a mean elongation at fracture of 18%. Among the TiO2-containing formulations, increasing the TiO2 content from 0.04 to 0.10 wt.% was associated with higher mean apparent tensile modulus and tensile strength and lower mean elongation at fracture. The 0.10 wt.% formulation exhibited the highest mean apparent tensile modulus and tensile strength.
Related
- PEG as Transient Structuring Agent for Tuning Properties of Electrospun Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) Scaffolds
- Valorization of cotton waste into cellulose nanocrystals and their incorporation into electrospun poly (vinyl alcohol) nanofibrous membranes with enhanced thermal and structural properties
- Direct Integration of Electrospun Polycaprolactone Fibers with Polydimethylsiloxane: Influence of Elastomer Formulation on Fiber–Elastomer Adhesion
- Shaping Tumor Targeting: How Nanoparticle Morphology Influences Penetration and Accumulation in 3D Breast Cancer Models
- First-principles Investigation of Reconstructions for the Polar CoO (111) Surface and the Impact on Nanoparticle Morphology
BibTeX
@article{llumiquinga2026influence,
title = {{Influence of Low TiO2 Nanoparticle Loading on Electrospun sPEEK Fiber Morphology and Chemistry and on the Tensile Properties of Corresponding Solution-Cast Membranes}},
author = {Dayana Llumiquinga and Luis Criollo and Wilson Navas-Pinto and Germán Omar Barrionuevo and Jhon Luna-Jaén and Xavier Sánchez-Sánchez and Santiago D. Puma-Araujo},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18192410},
url = {https://europepmc.org/article/PMC/PMC13667181},
note = {CC BY},
}
RIS
TY - JOUR
TI - Influence of Low TiO2 Nanoparticle Loading on Electrospun sPEEK Fiber Morphology and Chemistry and on the Tensile Properties of Corresponding Solution-Cast Membranes
AU - Dayana Llumiquinga
AU - Luis Criollo
AU - Wilson Navas-Pinto
AU - Germán Omar Barrionuevo
AU - Jhon Luna-Jaén
AU - Xavier Sánchez-Sánchez
AU - Santiago D. Puma-Araujo
PY - 2026
DA - 2026/10/01
JO - Polymers
DO - 10.3390/polym18192410
UR - https://europepmc.org/article/PMC/PMC13667181
AB - Polymer matrix composites (PMCs) have garnered importance due to their unique combination of mechanical, thermal, and functional properties. However, their performance depends on overcoming challenges related to dispersion, bonding, and processing. Electrospinning is an advanced technique for producing nanofiber or microfiber PMCs. One of the key challenges in electrospun PMCs is the uniform dispersion of reinforcement materials like TiO2 nanoparticles within the polymer matrix. A Taguchi orthogonal design (L16) was used to evaluate the effects of needle-to-collector distance, applied voltage, and flow rate on mean fiber diameter and deposition quality. Scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FT-IR) were used to characterize electrospun neat sulfonated poly(ether ether ketone) (sPEEK) and sPEEK/TiO2 fibers, whereas tensile tests were performed on solution-cast membranes prepared from the corresponding formulations. The lowest observed run mean diameter was 204.6695 nm at 8 kV, 1.25 mL h−1, and a needle-to-collector distance of 12 cm; this run was also selected for deposition quality. Neat sPEEK membranes exhibited a mean tensile strength of 35.3 MPa, a mean apparent tensile modulus of 476 MPa, and a mean elongation at fracture of 18%. Among the TiO2-containing formulations, increasing the TiO2 content from 0.04 to 0.10 wt.% was associated with higher mean apparent tensile modulus and tensile strength and lower mean elongation at fracture. The 0.10 wt.% formulation exhibited the highest mean apparent tensile modulus and tensile strength.