4D Printing of Magneto‐Active Soft Elastomers via Efficient Active Mixing Direct Ink Writing
Abstract
4D printing relies on the 3D printing of materials that respond to various stimuli after printing. Among these, magneto‐active elastomers readily react to magnetic fields, particularly at high magnetic particle loadings. For soft silicones with high particle contents, direct ink writing (DIW) is the most appropriate printing technique. However, a major challenge remains, especially for very‐short‐pot‐life silicones: crosslinking starts once the base is mixed with the curing agent. Hence, a helical mixer with large blades operating at low speed within a large chamber is introduced for the first time in active mixing DIW to specifically address high‐particle‐content, short‐pot‐life silicones. This method offers a steady and efficient mixing of the two silicone components, both loaded with magnetic particles and a rheology modifier, just before extrusion, leading to consistent filament extrusion with even particle distribution in addition to extended printing times without further additives or elaborate control systems. A framework is presented for selecting print parameters, where only the extruder speed needs to be adjusted when switching between inks having different particle contents. The impact of printing strategy on mechanical properties is assessed, and magneto‐active structures that can find applications in tunable actuators, soft robotics, deployable structures, and surface morphing are demonstrated.
Related
- Effect of chirality on active elastomers and solids in three dimensions
- Phase-Matched Chirps for Energy-Efficient Excitation of Magneto-Mechanical Resonators
- Diversity-Aware Batch-Mode Active Learning for Efficient Sampling in Data-Driven Constitutive Modeling
- Survival Analysis of Fatigue Lifetime in Aged Elastomers Using Weibull and Cox Regression Models
- Electromechanical Domain Wall Propagation in Dielectric Elastomers: An Exact Geometric Resolution via Conformal Mapping
BibTeX
@article{selvam2026printing,
title = {{4D Printing of Magneto‐Active Soft Elastomers via Efficient Active Mixing Direct Ink Writing}},
author = {Vignesh Selvam and Kostas Danas and Laurence Bodelot},
journal = {Advanced Materials Technologies},
year = {2026},
month = aug,
doi = {10.1002/admt.71264},
url = {https://polytechnique.hal.science/hal-05756202v1},
note = {CC BY-NC-ND 4.0},
}
RIS
TY - JOUR
TI - 4D Printing of Magneto‐Active Soft Elastomers via Efficient Active Mixing Direct Ink Writing
AU - Vignesh Selvam
AU - Kostas Danas
AU - Laurence Bodelot
PY - 2026
DA - 2026/08/24
JO - Advanced Materials Technologies
DO - 10.1002/admt.71264
UR - https://polytechnique.hal.science/hal-05756202v1
AB - 4D printing relies on the 3D printing of materials that respond to various stimuli after printing. Among these, magneto‐active elastomers readily react to magnetic fields, particularly at high magnetic particle loadings. For soft silicones with high particle contents, direct ink writing (DIW) is the most appropriate printing technique. However, a major challenge remains, especially for very‐short‐pot‐life silicones: crosslinking starts once the base is mixed with the curing agent. Hence, a helical mixer with large blades operating at low speed within a large chamber is introduced for the first time in active mixing DIW to specifically address high‐particle‐content, short‐pot‐life silicones. This method offers a steady and efficient mixing of the two silicone components, both loaded with magnetic particles and a rheology modifier, just before extrusion, leading to consistent filament extrusion with even particle distribution in addition to extended printing times without further additives or elaborate control systems. A framework is presented for selecting print parameters, where only the extruder speed needs to be adjusted when switching between inks having different particle contents. The impact of printing strategy on mechanical properties is assessed, and magneto‐active structures that can find applications in tunable actuators, soft robotics, deployable structures, and surface morphing are demonstrated.
SN - 2365-709X
ER -