Insight into the effects of the cathode operating potential on the ageing mechanisms of PEMFC single cells’ active layers
Abstract
This study aims to unveil the influence of the cell voltage value on the degradation rate of PEMFC single cell durably operated at constant cell voltages (0.6-0.85 V) under H2/Air, with minimal intermediate characterisations to limit the impact of voltage cycling. In these potentiostatic test conditions, no major corrosion of the carbon support of the Pt/C catalyst occurs. Whereas the cathode ECSA losses are rather similar whatever the test conditions, the cathodes have different fates depending on whether the ageing is performed at low or high cell voltage. Low cathode potential (cell voltage) prevents Pt-oxides formation (hence Pt passivation) and minors Pt potential-induced dissolution but favours Pt-redeposition: Oswald ripening is the main process of ECSA loss. High cell voltage enables larger Pt passivation by surface oxides, mitigating both Pt dissolution and redeposition/reduction, hence significantly lowering Oswald ripening; these conditions enhance the formation of carbon surface groups, leading to Pt crystallites migration into agglomerates and related ECSA loss. These carbon surface groups are only minorly oxidised into CO2, because Pt-assisted corrosion is unlikely for Pt-oxides. The ORR performance remains high after low potential ageing (the ECSA loss is counterbalanced by the positive Pt nanoparticles-size-effect) and degrades faster after high potential ageing (the ECSA loss is accompanied by rather irreversible Pt-oxides formation after high-potential holds, which results in very depreciated apparent ORR kinetics). One cannot exclude that the different cell voltages experiences lead to different water content of the active layers, this effect probably being second-order compared to that of the potential.
Related
- Synthesis of Fused Biimidazole-Containing Polymers and Their Application as High-Potential Organic Cathode Materials for Lithium-Ion Batteries
- Direct regeneration mechanisms of spent lithium iron phosphate cathode materials for sustainable lithium ion battery recycling
- Ageing and CEI formation mechanisms in porous carbon positive electrode in sodium-ion capacitors
- A Mini-Review on Thalidomide: Chemistry, Mechanisms of Action, Therapeutic Potential and Anti-Angiogenic Properties in Multiple Myeloma
- Antibacterial Plant Secondary Metabolites: Mechanisms of Action, Pharmacokinetics, Safety, and Translational Potential
BibTeX
@article{riasse2026insight,
title = {{Insight into the effects of the cathode operating potential on the ageing mechanisms of PEMFC single cells’ active layers}},
author = {Raphaël Riasse and Laetitia Dubau and Julien Durst and Gaël Maranzana and Marian Chatenet},
journal = {Electrochimica Acta},
year = {2026},
month = oct,
doi = {10.1016/j.electacta.2026.149473},
url = {https://univ-grenoble-alpes.hal.science/hal-05766719v1},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Insight into the effects of the cathode operating potential on the ageing mechanisms of PEMFC single cells’ active layers
AU - Raphaël Riasse
AU - Laetitia Dubau
AU - Julien Durst
AU - Gaël Maranzana
AU - Marian Chatenet
PY - 2026
DA - 2026/10/20
JO - Electrochimica Acta
DO - 10.1016/j.electacta.2026.149473
UR - https://univ-grenoble-alpes.hal.science/hal-05766719v1
AB - This study aims to unveil the influence of the cell voltage value on the degradation rate of PEMFC single cell durably operated at constant cell voltages (0.6-0.85 V) under H2/Air, with minimal intermediate characterisations to limit the impact of voltage cycling. In these potentiostatic test conditions, no major corrosion of the carbon support of the Pt/C catalyst occurs. Whereas the cathode ECSA losses are rather similar whatever the test conditions, the cathodes have different fates depending on whether the ageing is performed at low or high cell voltage. Low cathode potential (cell voltage) prevents Pt-oxides formation (hence Pt passivation) and minors Pt potential-induced dissolution but favours Pt-redeposition: Oswald ripening is the main process of ECSA loss. High cell voltage enables larger Pt passivation by surface oxides, mitigating both Pt dissolution and redeposition/reduction, hence significantly lowering Oswald ripening; these conditions enhance the formation of carbon surface groups, leading to Pt crystallites migration into agglomerates and related ECSA loss. These carbon surface groups are only minorly oxidised into CO2, because Pt-assisted corrosion is unlikely for Pt-oxides. The ORR performance remains high after low potential ageing (the ECSA loss is counterbalanced by the positive Pt nanoparticles-size-effect) and degrades faster after high potential ageing (the ECSA loss is accompanied by rather irreversible Pt-oxides formation after high-potential holds, which results in very depreciated apparent ORR kinetics). One cannot exclude that the different cell voltages experiences lead to different water content of the active layers, this effect probably being second-order compared to that of the potential.
SN - 0013-4686
ER -