Nonequilibrium Hydrogen/Argon Plasma for a Swift Reduction of Cobalt Oxalate into Metal: Utilization of Radiofrequency and Microwave Plasma Reactors
Abstract
Cobalt is a critical material for energy storage, catalysis, and advanced alloys, yet its recovery from end-of-life products with precursors such as cobalt oxalate remains limited even when cobalt resources are depleting. This study investigates the rapid reduction of cobalt oxalate dihydrate (Co(C2O4)·2H2O) to metallic cobalt using low-pressure nonequilibrium hydrogen and argon (H2/Ar) plasma in two reactor configurations: radiofrequency (RF, 40 MHz) and microwave (MW, 2.45 GHz). Experiments were conducted at transmitted powers of 550 and up to 800 W, with gas flow rates of 120 to 200 sccm with variable H2/Ar ratios and pressures ranging from 40 to 200 Pa. Under optimized conditions, complete reduction occurred in 5 min for the RF reactor. The MW reactor demonstrated superior performance that was attributed to higher power density and localized discharge, enabling full reduction within 2 min. Gas temperatures were estimated using optical emission spectroscopy, reaching temperatures of 700 to 1000 K, while the phase transformation and microstructural evolution of cobalt were confirmed through X-ray diffraction and scanning electron microscopy indicating the formation of 1 µm granulometry α-cobalt powder. Thermodynamic discussion indicates that plasma activation significantly enhances reaction kinetics, overcoming the limitations of conventional thermal reduction. These findings highlight cobalt oxalate dihydrate as a promising feed for cobalt secondary sourcing and nonequilibrium plasma as a promising route for fast cobalt recovery, with potential applications in battery recycling and advanced metallurgical processes.
Related
- Microwave-irradiated ultrafast synthesis of NiSnPdPtRh high-entropy alloy nanorods for high-efficiency electrocatalytic hydrogen evolution reaction
- Hierarchical nature of hydrogen-based direct reduction of iron oxides
- Puppet Strings of Hydrogen Plasma Reduction of Iron Ores: The Impact of Process Parameters on Plasma Properties and Reduction Kinetics
- Concomitant Production and Transfer of Hydrogen for Efficient In Situ Reduction of C–C and C–O Unsaturated Substrates by Pt/TiO2 Photocatalyst in Ethanol
- Role of water in hydrogen-based iron oxide reduction: effects on pore evolution and gas transport
BibTeX
@article{guillemin2026nonequilibrium,
title = {{Nonequilibrium Hydrogen/Argon Plasma for a Swift Reduction of Cobalt Oxalate into Metal: Utilization of Radiofrequency and Microwave Plasma Reactors}},
author = {Antonin Guillemin and Morvan Gaudin and Gabriel Morand and Sylviane Chevreux and Frederic Rousseau and Cédric Guyon},
journal = {ACS Sustainable Chemistry \& Engineering},
year = {2026},
month = oct,
doi = {10.1021/acssuschemeng.6c07125},
url = {https://hal.science/hal-05801326v1},
note = {CC BY-NC-ND 4.0},
}
RIS
TY - JOUR
TI - Nonequilibrium Hydrogen/Argon Plasma for a Swift Reduction of Cobalt Oxalate into Metal: Utilization of Radiofrequency and Microwave Plasma Reactors
AU - Antonin Guillemin
AU - Morvan Gaudin
AU - Gabriel Morand
AU - Sylviane Chevreux
AU - Frederic Rousseau
AU - Cédric Guyon
PY - 2026
DA - 2026/10/15
JO - ACS Sustainable Chemistry & Engineering
DO - 10.1021/acssuschemeng.6c07125
UR - https://hal.science/hal-05801326v1
AB - Cobalt is a critical material for energy storage, catalysis, and advanced alloys, yet its recovery from end-of-life products with precursors such as cobalt oxalate remains limited even when cobalt resources are depleting. This study investigates the rapid reduction of cobalt oxalate dihydrate (Co(C2O4)·2H2O) to metallic cobalt using low-pressure nonequilibrium hydrogen and argon (H2/Ar) plasma in two reactor configurations: radiofrequency (RF, 40 MHz) and microwave (MW, 2.45 GHz). Experiments were conducted at transmitted powers of 550 and up to 800 W, with gas flow rates of 120 to 200 sccm with variable H2/Ar ratios and pressures ranging from 40 to 200 Pa. Under optimized conditions, complete reduction occurred in 5 min for the RF reactor. The MW reactor demonstrated superior performance that was attributed to higher power density and localized discharge, enabling full reduction within 2 min. Gas temperatures were estimated using optical emission spectroscopy, reaching temperatures of 700 to 1000 K, while the phase transformation and microstructural evolution of cobalt were confirmed through X-ray diffraction and scanning electron microscopy indicating the formation of 1 µm granulometry α-cobalt powder. Thermodynamic discussion indicates that plasma activation significantly enhances reaction kinetics, overcoming the limitations of conventional thermal reduction. These findings highlight cobalt oxalate dihydrate as a promising feed for cobalt secondary sourcing and nonequilibrium plasma as a promising route for fast cobalt recovery, with potential applications in battery recycling and advanced metallurgical processes.
SN - 2168-0485
SN - 2168-0485
ER -