Electrodeposited Pd/TiO2 Nanotube Arrays with Size-Controlled Pd for High-Performance UV and Visible-Light Photocatalytic Water Remediation
Abstract
Environmental contamination by persistent industrial dyes such as Amido Black demands highly efficient photocatalysts for advanced water treatment. Structural, chemical, and optical strategies based on TiO2 nanotube engineering are widely explored for this purpose. In this work, highly ordered TiO2 nanotube arrays were fabricated by electrochemical anodization and subsequently decorated with Pd nanoparticles via potentiostatic electrodeposition (10–300 s), enabling precise control of Pd nanoparticle size and loading. The resulting materials were systematically characterized by SEM, TEM, XRD, XPS, UV–vis DRS, and PL spectroscopy, and their properties were correlated with the photocatalytic degradation of Amido Black under both UV and visible light irradiation. The study reveals a clear size-dependent duality in the role of Pd. For intermediate Pd nanoparticles (≈9 nm, 20 s), Pd behaves predominantly as an electron sink, forming an efficient Schottky junction with anatase TiO2 that markedly suppresses charge carrier recombination. This configuration yields ≈ 97% Amido Black removal after 120 min of UV irradiation, with an apparent rate constant about three times higher than that of bare TiO2 nanotubes. In contrast, for ultra-small Pd nanoparticles (≈6 nm, 10 s), interfacial defect states sensitize TiO2 to visible light, enabling ≈ 65% degradation after 270 min and a rate constant roughly four times higher than that of undecorated nanotubes under visible illumination. At long deposition times (≥150 s), Pd agglomeration leads to enhanced photoluminescence and markedly reduced photocatalytic activity, indicating increased recombination and less effective utilization of photogenerated charges. This provides a practical design rule to rationally tailor Pd–TiO2 nanotube photocatalysts for targeted UV or visible light applications in dye removal and broader environmental remediation scenarios
Related
- Photocatalytic Performance of TiO2-Based Nanomaterials for Water Remediation
- Polymer Brush-Mediated Surface-Initiated Polycondensation Enables sp2C-COF Thin Films with Controlled Crystallinity and High Photocatalytic Performance
- Adsorption and Photocatalytic Activity of Covalent Organic Frameworks for Environmental Remediation: A Review of Density Functional Theory Studies
- Oxygen Defects and Photocatalytic Activity of Bi2O3/TiO2 Nanotube-Based Catalysts
- Multifunctional Alginate–TiO2/SiO2 Hydrogel–Ceramic Composites for Photocatalytic Soil Remediation and Impedance-Based Diagnostics: A Critical Review and Conceptual Framework
BibTeX
@article{mehdaoui2026electrodeposited,
title = {{Electrodeposited Pd/TiO2 Nanotube Arrays with Size-Controlled Pd for High-Performance UV and Visible-Light Photocatalytic Water Remediation}},
author = {Ayda Mehdaoui and Syrine Sassi and Rabia Benabderrahmane Zaghouani and Hafedh Dhiflaoui and Lotfi Khezami and Amal Bouich and Farid Fadhillah and Aymen Amine Assadi and Jie Zhang and Anouar Hajjaji and Bernabé Mari Soucase},
journal = {Catalysts},
year = {2026},
month = oct,
doi = {10.3390/catal16040350},
url = {https://hal.science/hal-05834898v1},
note = {CC BY},
}
RIS
TY - JOUR
TI - Electrodeposited Pd/TiO2 Nanotube Arrays with Size-Controlled Pd for High-Performance UV and Visible-Light Photocatalytic Water Remediation
AU - Ayda Mehdaoui
AU - Syrine Sassi
AU - Rabia Benabderrahmane Zaghouani
AU - Hafedh Dhiflaoui
AU - Lotfi Khezami
AU - Amal Bouich
AU - Farid Fadhillah
AU - Aymen Amine Assadi
AU - Jie Zhang
AU - Anouar Hajjaji
AU - Bernabé Mari Soucase
PY - 2026
DA - 2026/10/22
JO - Catalysts
DO - 10.3390/catal16040350
UR - https://hal.science/hal-05834898v1
AB - Environmental contamination by persistent industrial dyes such as Amido Black demands highly efficient photocatalysts for advanced water treatment. Structural, chemical, and optical strategies based on TiO2 nanotube engineering are widely explored for this purpose. In this work, highly ordered TiO2 nanotube arrays were fabricated by electrochemical anodization and subsequently decorated with Pd nanoparticles via potentiostatic electrodeposition (10–300 s), enabling precise control of Pd nanoparticle size and loading. The resulting materials were systematically characterized by SEM, TEM, XRD, XPS, UV–vis DRS, and PL spectroscopy, and their properties were correlated with the photocatalytic degradation of Amido Black under both UV and visible light irradiation. The study reveals a clear size-dependent duality in the role of Pd. For intermediate Pd nanoparticles (≈9 nm, 20 s), Pd behaves predominantly as an electron sink, forming an efficient Schottky junction with anatase TiO2 that markedly suppresses charge carrier recombination. This configuration yields ≈ 97% Amido Black removal after 120 min of UV irradiation, with an apparent rate constant about three times higher than that of bare TiO2 nanotubes. In contrast, for ultra-small Pd nanoparticles (≈6 nm, 10 s), interfacial defect states sensitize TiO2 to visible light, enabling ≈ 65% degradation after 270 min and a rate constant roughly four times higher than that of undecorated nanotubes under visible illumination. At long deposition times (≥150 s), Pd agglomeration leads to enhanced photoluminescence and markedly reduced photocatalytic activity, indicating increased recombination and less effective utilization of photogenerated charges. This provides a practical design rule to rationally tailor Pd–TiO2 nanotube photocatalysts for targeted UV or visible light applications in dye removal and broader environmental remediation scenarios