Surface morphology, printing accuracy and flexural strength of 3D-printed zirconia posts with longitudinal microgrooves.
5 affiliations
- 1Stomatological Hospital of Xiamen Medical Colledge, Xiamen, Fujian, China.
- 2Xiamen Key Laboratory of Stomatological Disease Diagnosis and Disease Diagnosis and Treatment, Xiamen, Fujian, China.
- 3Second community health service center, Jinshan Street, Cangshan district, Fuzhou, Fujian, China.
- 4Stomatological Hospital of Xiamen Medical Colledge, Xiamen, Fujian, China. [email protected].
- 5Xiamen Key Laboratory of Stomatological Disease Diagnosis and Disease Diagnosis and Treatment, Xiamen, Fujian, China. [email protected].
Abstract
Background
Postcore restoration is essential for compromised teeth. Zirconia is a promising material due to its esthetics, strength, and radiopacity. Additive manufacturing, particularly advanced customized jetting (ACJ) technology, enables the fabrication of complex microstructures on zirconia surfaces to potentially enhance resin bonding. However, before bonding tests, it is necessary to establish the printability, accuracy, and baseline mechanical properties of such microstructured posts.Methods
A commercial fiber post was scanned and used as a template to design zirconia posts with 4, 8, 16, and 32 longitudinal microgrooves (MZ4, MZ8, MZ16, MZ32). Posts were fabricated via ACJ 3D printing. Surface morphology and roughness were evaluated via laser scanning confocal microscopy (LSCM). Microstructural surfaces were observed via scanning electron microscopy (SEM). Printing accuracy was assessed by boundary dimension and coefficient of variation (CV) of microgroove width. Flexural strength was determined via three-point bending test (ISO 6872:2024). Data were analyzed using Welch's ANOVA (α=0.05).Results
LSCM and SEM revealed regular, intact microgrooves in MZ4, MZ8, and MZ16, while MZ32 exhibited structural collapse. Surface roughness increased significantly from MZ4 to MZ16. Boundary dimensions of MZ4-MZ16 showed no significant differences, whereas MZ32 deviated significantly (P<0.01). CV values for MZ4, MZ8, and MZ16 were 10.30±3.38%, 12.99±4.44%, and 11.03±0.72%, respectively, with no significant intergroup differences (P=0.862). Flexural strengths for MZ4, MZ8, MZ16, MZ32, and the fiber post control were 605.32±27.48, 466.28±20.51, 414.28±33.69, 367.36±21.28, and 471.53±22.95 MPa, respectively. Welch's ANOVA revealed a significant difference (P=0.045), with a monotonic decreasing trend in strength as groove density increased. Significant difference was found only between MZ4 and MZ32 (P=0.037), while no significant differences were detected among other groups (P>0.05).Conclusion
Within the limitations of this study, ACJ printing can reliably fabricate zirconia posts with up to 16 microgrooves without compromising accuracy or flexural strength. MZ16, which provided the highest surface roughness without significant loss of strength or accuracy, may be considered as a candidate for future adhesion studies. Further investigations-including bond strength testing, mechanical aging, and fatigue evaluation-are warranted.
Related
- A Systematic Review of 3D-Printing in Spine Surgery: Applications, Accuracy, and Outcomes
- Quantitative Morphology of Stump Sprouts Reveals a Common Growth Axis and a Reproducible Basal Longitudinal Cavity in an Ornamental Cherry
- Accuracy of transfer learning in predicting peri-implantitis onset from intraoral radiograph: A multi-center longitudinal retrospective study.
- Experimental characterization and scaling of flexural rigidity in sewn multilayer structures
- Constraining Lithospheric Delamination on Venus with Flexural Topography and Trench Geometry
BibTeX
@article{lin2026surface,
title = {{Surface morphology, printing accuracy and flexural strength of 3D-printed zirconia posts with longitudinal microgrooves.}},
author = {Pingting Lin and Qi Jiang and Lu Yin},
journal = {BMC oral health},
year = {2026},
month = aug,
doi = {10.1186/s12903-026-09244-z},
url = {https://europepmc.org/article/MED/42968074},
note = {CC BY-NC-ND},
}
RIS
TY - JOUR
TI - Surface morphology, printing accuracy and flexural strength of 3D-printed zirconia posts with longitudinal microgrooves.
AU - Pingting Lin
AU - Qi Jiang
AU - Lu Yin
PY - 2026
DA - 2026/08/05
JO - BMC oral health
DO - 10.1186/s12903-026-09244-z
UR - https://europepmc.org/article/MED/42968074
AB - Background Postcore restoration is essential for compromised teeth. Zirconia is a promising material due to its esthetics, strength, and radiopacity. Additive manufacturing, particularly advanced customized jetting (ACJ) technology, enables the fabrication of complex microstructures on zirconia surfaces to potentially enhance resin bonding. However, before bonding tests, it is necessary to establish the printability, accuracy, and baseline mechanical properties of such microstructured posts.Methods A commercial fiber post was scanned and used as a template to design zirconia posts with 4, 8, 16, and 32 longitudinal microgrooves (MZ4, MZ8, MZ16, MZ32). Posts were fabricated via ACJ 3D printing. Surface morphology and roughness were evaluated via laser scanning confocal microscopy (LSCM). Microstructural surfaces were observed via scanning electron microscopy (SEM). Printing accuracy was assessed by boundary dimension and coefficient of variation (CV) of microgroove width. Flexural strength was determined via three-point bending test (ISO 6872:2024). Data were analyzed using Welch's ANOVA (α=0.05).Results LSCM and SEM revealed regular, intact microgrooves in MZ4, MZ8, and MZ16, while MZ32 exhibited structural collapse. Surface roughness increased significantly from MZ4 to MZ16. Boundary dimensions of MZ4-MZ16 showed no significant differences, whereas MZ32 deviated significantly (P<0.01). CV values for MZ4, MZ8, and MZ16 were 10.30±3.38%, 12.99±4.44%, and 11.03±0.72%, respectively, with no significant intergroup differences (P=0.862). Flexural strengths for MZ4, MZ8, MZ16, MZ32, and the fiber post control were 605.32±27.48, 466.28±20.51, 414.28±33.69, 367.36±21.28, and 471.53±22.95 MPa, respectively. Welch's ANOVA revealed a significant difference (P=0.045), with a monotonic decreasing trend in strength as groove density increased. Significant difference was found only between MZ4 and MZ32 (P=0.037), while no significant differences were detected among other groups (P>0.05).Conclusion Within the limitations of this study, ACJ printing can reliably fabricate zirconia posts with up to 16 microgrooves without compromising accuracy or flexural strength. MZ16, which provided the highest surface roughness without significant loss of strength or accuracy, may be considered as a candidate for future adhesion studies. Further investigations-including bond strength testing, mechanical aging, and fatigue evaluation-are warranted.