Unraveling the Role of Lignin Oligomers Functionality for the Synthesis of Nonisocyanate Polyurethanes
Abstract
Lignins are the main source of aromatic compounds in nature. Their depolymerization most often leads to oligomeric products, which lack proper valorization. In this study, two lignins (Kraft and organosolv) were subjected to two depolymerization methodologies, leading to a total of six lignin samples, which were characterized and functionalized to cyclocarbonate (CC) building blocks through a green and optimized one-pot procedure. The lignin oligomers obtained by depolymerization were compared to the raw lignins for the synthesis of safe and sustainable polyhydroxyurethane (PHU) thermosets by aminolysis with lignin contents between 28 and 34 wt%. The synthesized PHU materials displayed a wide range of mechanical properties and behaviors, with a tensile modulus ranging from 50 to 1400 kPa, and elongation at break ranging from 46% to 217%. While lignin depolymerization had a negligible effect on the polymerization kinetics, it led to softer and more flexible materials at equivalent lignin contents. Interestingly, it was found that the functionality of the lignin-CC building blocks is the main factor affecting the crosslinking density, and consequently the mechanical properties of the materials. Other factors such as the lignin type (e.g., Kraft vs. organosolv) and the depolymerization method (e.g., hydrothermal vs. reductive) did not have a strong influence on the final material properties. These different points establish a strong foundation for the understanding of "structure-properties" relationships in lignin-based materials, a key point toward the valorization of lignin into renewable, safe, and high-performance materials.
Related
- Feasibility Study of the Synthesis of Isocyanate-Free Polyurethanes from Catechin
- Scalable Room-Temperature Synthesis of Glass-like MOF Thin Films on Arbitrary Substrates with Versatile Functionality
- On the enzymatic synthesis of ketone-containing oligomers and their processing into sustainable crosslinked materials
- Terpene-Derived Carvyl Acetate Dicarbonate: A Novel Monomer for Biobased Nonisocyanate Poly(hydroxyurethane) Thermoplastics and Thermosets.
- Polymer Network Evolution Induced by Dual-Crosslinking Architectures in UV-Curable Waterborne Polyurethanes
BibTeX
@article{wybo2026unraveling,
title = {{Unraveling the Role of Lignin Oligomers Functionality for the Synthesis of Nonisocyanate Polyurethanes}},
author = {N. Wybo and H. Lilti and D. Laurenti and C. Geantet and A. Duval and L. Averous},
journal = {ChemSusChem},
year = {2026},
month = sep,
doi = {10.1002/cssc.70953},
url = {https://hal.science/hal-05741785v1},
note = {CC BY},
}
RIS
TY - JOUR
TI - Unraveling the Role of Lignin Oligomers Functionality for the Synthesis of Nonisocyanate Polyurethanes
AU - N. Wybo
AU - H. Lilti
AU - D. Laurenti
AU - C. Geantet
AU - A. Duval
AU - L. Averous
PY - 2026
DA - 2026/09/08
JO - ChemSusChem
DO - 10.1002/cssc.70953
UR - https://hal.science/hal-05741785v1
AB - Lignins are the main source of aromatic compounds in nature. Their depolymerization most often leads to oligomeric products, which lack proper valorization. In this study, two lignins (Kraft and organosolv) were subjected to two depolymerization methodologies, leading to a total of six lignin samples, which were characterized and functionalized to cyclocarbonate (CC) building blocks through a green and optimized one-pot procedure. The lignin oligomers obtained by depolymerization were compared to the raw lignins for the synthesis of safe and sustainable polyhydroxyurethane (PHU) thermosets by aminolysis with lignin contents between 28 and 34 wt%. The synthesized PHU materials displayed a wide range of mechanical properties and behaviors, with a tensile modulus ranging from 50 to 1400 kPa, and elongation at break ranging from 46% to 217%. While lignin depolymerization had a negligible effect on the polymerization kinetics, it led to softer and more flexible materials at equivalent lignin contents. Interestingly, it was found that the functionality of the lignin-CC building blocks is the main factor affecting the crosslinking density, and consequently the mechanical properties of the materials. Other factors such as the lignin type (e.g., Kraft vs. organosolv) and the depolymerization method (e.g., hydrothermal vs. reductive) did not have a strong influence on the final material properties. These different points establish a strong foundation for the understanding of "structure-properties" relationships in lignin-based materials, a key point toward the valorization of lignin into renewable, safe, and high-performance materials.
SN - 1864-5631
SN - 1864-564X
ER -