Influences of N2 flow rate on the superconducting properties and dimensionality of epitaxial TiN thin films
Abstract
TiN thin films have received great attention in the field of superconducting quantum computing due to their low loss characteristics derived from stable chemical and thermal properties, as well as excellent electrical conductivity. In this study, TiN thin films with a thickness of 35 nm were epitaxially grown on MgO substrates using the DC reactive magnetron sputtering technique. The crystal structure, film thickness, and surface morphology of the thin films were characterized. The films exhibit a very flat surface with a root mean square roughness of only a few tenths of a nanometer. The influences of nitrogen (N2) flow rate on the surface morphology, superconducting transition temperature (Tc), residual resistivity ratio (RRR), normal-state resistivity (ρn), upper critical field, and superconducting dimensionality were investigated systematically. The experimental results show that the TiN film deposited with a N2 flow rate of 1.5 sccm exhibits optimal performance, including the highest Tc (4.93 K), the largest RRR, the lowest ρn, and the lowest slope of the out-of-film upper critical field near Tc. Moreover, it is found that the background vacuum inside the growth chamber has a significant impact on the superconducting properties of TiN films, and the degradation of vacuum degree can lead to the decrease of Tc. The upper critical field reveals a significant anisotropic feature. Importantly, the in-film upper critical field data demonstrates that the optimization of sample quality leads to deviation from two-dimensional superconducting behavior, which provides a new perspective on the influencing factors of superconducting dimensionality beyond the thickness of films. The present results provide useful references for a comprehensive understanding of the relationship between growth parameters and the superconducting properties of thin films.
Versions
Related
- Links between La N4,5-edge RIXS probed A-site covalency, structural parameters and superconducting properties in optimally doped La1.84M0.16CuO4 (M = Ca, Sr, Ba) epitaxial films and the La2CuO4 host lattice
- TLS loss in superconducting resonators on epitaxial hBN thin films
- Orientation selection and superconducting properties of epitaxial Al on ferromagnetic semiconductor (In,Fe)As
- Tailoring the properties of YBa2Cu3O7−δ thin films by 30-keV He+ irradiation: An enabling route to superconducting device nanopatterning
- Effect of oxygen plasma treatment on the structural and superconducting properties of atomic-layer-deposited NbN thin films
BibTeX
@misc{chen2026influences,
title = {{Influences of $N_2$ flow rate on the superconducting properties and dimensionality of epitaxial TiN thin films}},
author = {Shilong Chen and Yuchuan Liu and Yihui Sun and Xiaoni Wang and Wei Peng and Yu Wu and Gang Mu and Zhirong Lin},
howpublished = {arXiv},
year = {2026},
month = oct,
doi = {10.48550/arxiv.2610.38250},
eprint = {2610.38250},
archivePrefix = {arXiv},
url = {https://arxiv.org/abs/2610.38250},
note = {CC BY 4.0},
}
RIS
TY - UNPB
TI - Influences of N_2 flow rate on the superconducting properties and dimensionality of epitaxial TiN thin films
AU - Shilong Chen
AU - Yuchuan Liu
AU - Yihui Sun
AU - Xiaoni Wang
AU - Wei Peng
AU - Yu Wu
AU - Gang Mu
AU - Zhirong Lin
PY - 2026
DA - 2026/10/28
PB - arXiv
DO - 10.48550/arxiv.2610.38250
UR - https://arxiv.org/abs/2610.38250
AB - TiN thin films have received great attention in the field of superconducting quantum computing due to their low loss characteristics derived from stable chemical and thermal properties, as well as excellent electrical conductivity. In this study, TiN thin films with a thickness of 35 nm were epitaxially grown on MgO substrates using the DC reactive magnetron sputtering technique. The crystal structure, film thickness, and surface morphology of the thin films were characterized. The films exhibit a very flat surface with a root mean square roughness of only a few tenths of a nanometer. The influences of nitrogen (N_2) flow rate on the surface morphology, superconducting transition temperature (T_c), residual resistivity ratio (RRR), normal-state resistivity (ρ_n), upper critical field, and superconducting dimensionality were investigated systematically. The experimental results show that the TiN film deposited with a N_2 flow rate of 1.5 sccm exhibits optimal performance, including the highest T_c (4.93 K), the largest RRR, the lowest ρ_n, and the lowest slope of the out-of-film upper critical field near Tc. Moreover, it is found that the background vacuum inside the growth chamber has a significant impact on the superconducting properties of TiN films, and the degradation of vacuum degree can lead to the decrease of T_c. The upper critical field reveals a significant anisotropic feature. Importantly, the in-film upper critical field data demonstrates that the optimization of sample quality leads to deviation from two-dimensional superconducting behavior, which provides a new perspective on the influencing factors of superconducting dimensionality beyond the thickness of films. The present results provide useful references for a comprehensive understanding of the relationship between growth parameters and the superconducting properties of thin films.
ER -