Morphology and Dynamics of Self-interstitial Clusters in Irradiated Nickel
Abstract
Self-interstitial atom (SIA) clustering is a key early step in radiation damage evolution in face-centered cubic (FCC) metals, governing defect transport, recombination, and the long-term microstructural response of irradiated alloys. We combine molecular dynamics (MD) simulations and high-speed (>1000 frames/s) in situ transmission electron microscopy (TEM) to investigate the structure, energetics, and migration dynamics of SIA clusters in FCC Ni. MD simulations show that interstitials initially form disordered dumbbell clusters that evolve into either sessile Frank loops or glissile perfect (prismatic) loops; the latter progressively reorganize into compact ordered configurations with increasing mobility. Direct construction of both loop types over a wide size range, validated against MD-relaxed structures, shows that perfect loops are thermodynamically favored over Frank loops for cluster sizes N greater than or equal to 14, where N is the number of SIAs, with the energetic advantage increasing with cluster size. Nevertheless, substantial kinetic barriers allow Frank loops to persist as metastable defects. For perfect loops, diffusion coefficients computed over N = 16 to 400 reveal a nearly size-independent migration barrier of approximately 0.02 eV, while the diffusion prefactor decreases approximately as N^(-0.54). Trajectory analysis reveals a non-rigid, row-wise relay mechanism in which the number of participating atoms increases systematically with loop size, accounting for much of the observed prefactor scaling. Sub-millisecond in situ TEM observations reveal intermittent loop motion at velocities higher than previously observed but still several orders of magnitude below the intrinsic mobilities predicted by MD, indicating migration through a heterogeneous energy landscape of mobile and pinned states.
Related
- Atmospheric dynamics and variability of periodically irradiated tidally locked planets
- Early oxidation and fast carbon incorporation in nickel nanoparticles: A ReaxFF molecular dynamics study
- Euclid: Quick Data Release (Q1) -- Exploring the detailed visual morphology of galaxies in clusters
- Stability and current-driven dynamics of mixed-topology bimeron clusters
- Few-Body Decay Dynamics in Colloidal CsPbI3 Quantum-Dot Clusters
BibTeX
@misc{annamareddy2026morphology,
title = {{Morphology and Dynamics of Self-interstitial Clusters in Irradiated Nickel}},
author = {Ajay Annamareddy and Ibrahim Momohjimoh and Hangyu Li and Kevin G. Field and Paul M. Voyles and Dane Morgan},
howpublished = {arXiv},
year = {2026},
month = sep,
doi = {10.48550/arxiv.2609.01879},
eprint = {2609.01879},
archivePrefix = {arXiv},
url = {https://arxiv.org/abs/2609.01879},
note = {CC BY 4.0},
}
RIS
TY - UNPB
TI - Morphology and Dynamics of Self-interstitial Clusters in Irradiated Nickel
AU - Ajay Annamareddy
AU - Ibrahim Momohjimoh
AU - Hangyu Li
AU - Kevin G. Field
AU - Paul M. Voyles
AU - Dane Morgan
PY - 2026
DA - 2026/09/01
PB - arXiv
DO - 10.48550/arxiv.2609.01879
UR - https://arxiv.org/abs/2609.01879
AB - Self-interstitial atom (SIA) clustering is a key early step in radiation damage evolution in face-centered cubic (FCC) metals, governing defect transport, recombination, and the long-term microstructural response of irradiated alloys. We combine molecular dynamics (MD) simulations and high-speed (>1000 frames/s) in situ transmission electron microscopy (TEM) to investigate the structure, energetics, and migration dynamics of SIA clusters in FCC Ni. MD simulations show that interstitials initially form disordered dumbbell clusters that evolve into either sessile Frank loops or glissile perfect (prismatic) loops; the latter progressively reorganize into compact ordered configurations with increasing mobility. Direct construction of both loop types over a wide size range, validated against MD-relaxed structures, shows that perfect loops are thermodynamically favored over Frank loops for cluster sizes N greater than or equal to 14, where N is the number of SIAs, with the energetic advantage increasing with cluster size. Nevertheless, substantial kinetic barriers allow Frank loops to persist as metastable defects. For perfect loops, diffusion coefficients computed over N = 16 to 400 reveal a nearly size-independent migration barrier of approximately 0.02 eV, while the diffusion prefactor decreases approximately as N^(-0.54). Trajectory analysis reveals a non-rigid, row-wise relay mechanism in which the number of participating atoms increases systematically with loop size, accounting for much of the observed prefactor scaling. Sub-millisecond in situ TEM observations reveal intermittent loop motion at velocities higher than previously observed but still several orders of magnitude below the intrinsic mobilities predicted by MD, indicating migration through a heterogeneous energy landscape of mobile and pinned states.
ER -