In Situ Polyimide Modified Polymethylsilsesquioxane Aerogels for Thermal Insulation.
- 1School of Chemistry and Chemical Engineering, Qilu Normal University, Jinan 250200, China.
Abstract
The inherent brittleness of silica aerogels severely limits their practical application in thermal protection. To address this issue, polymethylsilsesquioxane (PMSQ) wet gels were fabricated via an aqueous sol-gel method, and polyimide (PI) was introduced through in situ polymerization to construct an inorganic-organic continuous framework with PI in situ bridging and interfacial coating, thus successfully preparing the Si/PI composite aerogel. This composite achieves synergistic enhancements in mechanical, thermal insulation, hydrophobic and flame-retardant properties. The flexible PI network effectively alleviates stress concentration, and the compressive modulus of the composite aerogels increased with the PI content, reaching 7.52 MPa for Si/PI-80 and 23.78 MPa for Si/PI-100. The thermal conductivity stays below 0.036 W·m⁻¹·K⁻¹ with favorable low thermal conduction stability. The Si-CH₃ groups in PMSQ provide excellent hydrophobicity with a maximum water contact angle of 145.6°. Meanwhile, the char-forming effect of PI at high temperatures counteracts the negative impact of methyl groups on flame retardancy, endowing the aerogel with self-extinguishing behavior and high thermal stability. This work offers a novel strategy for designing high-strength multifunctional silica-based aerogels, which exhibit promising application prospects in aerospace, building energy conservation and high-end thermal protection.
Related
- An overview of aerogels as advanced thermal insulation materials
- Origami-inspired folded-interlocked nanofiber aerogels for thermal insulation
- Multi-configuration synergistic modulation of MXene/poly-Schiff-base/Fe3O4 aerogels with enhanced microwave absorption, thermal insulation, and flame retardancy
- Chain-End Reactivity and Anisotropic Electronic Softening Define Candidate Design Targets in BPDA/4,4′-ODA Polyimide Insulation
- Investigation on the Degradation Mechanisms and Mechanical Property Evolution of 3D-SiO2-Fiber-Reinforced Polyimide Composites After Thermal Aging
BibTeX
@article{zhu2026situ,
title = {{In Situ Polyimide Modified Polymethylsilsesquioxane Aerogels for Thermal Insulation.}},
author = {Ziqi Zhu and Junyong Chen and Defang Pan and Guanghui Wu},
journal = {Gels (Basel, Switzerland)},
year = {2026},
month = oct,
doi = {10.3390/gels12100898},
url = {https://europepmc.org/article/MED/42929932},
note = {CC BY},
}
RIS
TY - JOUR
TI - In Situ Polyimide Modified Polymethylsilsesquioxane Aerogels for Thermal Insulation.
AU - Ziqi Zhu
AU - Junyong Chen
AU - Defang Pan
AU - Guanghui Wu
PY - 2026
DA - 2026/10/04
JO - Gels (Basel, Switzerland)
DO - 10.3390/gels12100898
UR - https://europepmc.org/article/MED/42929932
AB - The inherent brittleness of silica aerogels severely limits their practical application in thermal protection. To address this issue, polymethylsilsesquioxane (PMSQ) wet gels were fabricated via an aqueous sol-gel method, and polyimide (PI) was introduced through in situ polymerization to construct an inorganic-organic continuous framework with PI in situ bridging and interfacial coating, thus successfully preparing the Si/PI composite aerogel. This composite achieves synergistic enhancements in mechanical, thermal insulation, hydrophobic and flame-retardant properties. The flexible PI network effectively alleviates stress concentration, and the compressive modulus of the composite aerogels increased with the PI content, reaching 7.52 MPa for Si/PI-80 and 23.78 MPa for Si/PI-100. The thermal conductivity stays below 0.036 W·m⁻¹·K⁻¹ with favorable low thermal conduction stability. The Si-CH₃ groups in PMSQ provide excellent hydrophobicity with a maximum water contact angle of 145.6°. Meanwhile, the char-forming effect of PI at high temperatures counteracts the negative impact of methyl groups on flame retardancy, endowing the aerogel with self-extinguishing behavior and high thermal stability. This work offers a novel strategy for designing high-strength multifunctional silica-based aerogels, which exhibit promising application prospects in aerospace, building energy conservation and high-end thermal protection.
SN - 2310-2861
ER -