Mechanical and Thermomechanical Performance Evaluation of CFRP Sandwich Structures with Additively Manufactured Composite Cores
- 1Composite Materials Laboratory for Aeronautical Field, Romanian Research & Development Institute for Gas Turbines—COMOTI, 220D Iuliu Maniu Av., 061126 Bucharest, Romania
- 2Mechanical Engineering, Mechatronics and Robotics Department, Mechanical Engineering Faculty, “Gheorghe Asachi” Technical University of Iasi, 700050 Iasi, Romania
Abstract
This study experimentally evaluates how various 3D-printed gyroid core materials influence the mechanical and thermo-mechanical performance of lightweight carbon-fiber-reinforced polymer (CFRP) sandwich structures. Three gyroid core configurations were considered: short-carbon-fiber-reinforced polyphthalamide (PPA-CF), continuous-carbon-fiber-reinforced nylon (ONYX-R), and nylon short-carbon-fiber-reinforced (ONYX), all combined with similar 0/90° carbon-fiber-reinforced polymer composite (CFRP) face sheets. The sandwich specimens were manufactured using a one-step co-curing process and characterized by flatwise compression, three-point bending, and dynamic mechanical analysis (DMA). The PPA-CF-CFRP sandwich configuration exhibited the highest flexural performance, with a maximum flexural stress of 148–156 MPa, approximately 39% higher than that of ONYX-R-CFRP, and the highest mean compression modulus of approximately 87 MPa. However, ONYX-R-CFRP achieved the highest mean compressive strength of 12.84 MPa, compared with 11.85 MPa for PPA-CF-CFRP. These findings indicate that the mechanical response depends on the loading mode and is influenced by the combined effects of the thermoplastic matrix, carbon-fiber reinforcement architecture, and the resulting structural characteristics of the printed gyroid cores. DMA revealed that the PPA-CF-CFRP sandwich achieved a storage modulus of ~9 GPa at 30 °C, outperforming the ONYX-R-CFRP configuration by approximately 70%. Conversely, ONYX-R-CFRP exhibited the highest damping capacity, with a maximum tan δ of approximately 0.16, about 60% higher than the PPA-CF-CFRP configuration. The ONYX-CFRP sandwich configuration displayed the lowest mechanical and thermo-mechanical performance, demonstrating that the stiffness, deformation capacity, damping response, and temperature-dependent mechanical behavior of these sandwich structures can be tailored through the selection of the additively manufactured core configuration.
Related
- Mechanical and Thermomechanical Response of Co-Cured QFRP Sandwich Structures with Additively Manufactured Fibre-Reinforced Gyroid Cores
- Mechanical Performance of Bio-Based Additively Manufactured Honeycomb Sandwich Panels: Experimental and Numerical Investigation
- Ultrasonic Energy Field-Induced Recrystallization-Driven Grain Refinement and Mechanical Property Enhancement in Ti5321G Alloy Manufactured via Laser Melting Deposition
- Influence of Post-Processing by Annealing on Additive Manufacturing Productivity and Mechanical Properties in Three-Point Bending of Additively Manufactured Specimens from PETG and Recycled PETG
- Cooperative Thiol-Amine System Enables Rapid Epoxy Curing with Balanced Thermomechanical Performance
BibTeX
@article{ciubotariu2026mechanical,
title = {{Mechanical and Thermomechanical Performance Evaluation of CFRP Sandwich Structures with Additively Manufactured Composite Cores}},
author = {Alexandru Ciubotariu and Teodor-Adrian Badea and Madalina Mustareata and Raluca Maier and Andrei Timonia and Vlad Buga and Laurentiu Petre and Ciprian Ionuț Morăraș and Viorel Goanță},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18202510},
url = {https://www.mdpi.com/2073-4360/18/20/2510},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Mechanical and Thermomechanical Performance Evaluation of CFRP Sandwich Structures with Additively Manufactured Composite Cores
AU - Alexandru Ciubotariu
AU - Teodor-Adrian Badea
AU - Madalina Mustareata
AU - Raluca Maier
AU - Andrei Timonia
AU - Vlad Buga
AU - Laurentiu Petre
AU - Ciprian Ionuț Morăraș
AU - Viorel Goanță
PY - 2026
DA - 2026/10/01
JO - Polymers
DO - 10.3390/polym18202510
UR - https://www.mdpi.com/2073-4360/18/20/2510
AB - This study experimentally evaluates how various 3D-printed gyroid core materials influence the mechanical and thermo-mechanical performance of lightweight carbon-fiber-reinforced polymer (CFRP) sandwich structures. Three gyroid core configurations were considered: short-carbon-fiber-reinforced polyphthalamide (PPA-CF), continuous-carbon-fiber-reinforced nylon (ONYX-R), and nylon short-carbon-fiber-reinforced (ONYX), all combined with similar 0/90° carbon-fiber-reinforced polymer composite (CFRP) face sheets. The sandwich specimens were manufactured using a one-step co-curing process and characterized by flatwise compression, three-point bending, and dynamic mechanical analysis (DMA). The PPA-CF-CFRP sandwich configuration exhibited the highest flexural performance, with a maximum flexural stress of 148–156 MPa, approximately 39% higher than that of ONYX-R-CFRP, and the highest mean compression modulus of approximately 87 MPa. However, ONYX-R-CFRP achieved the highest mean compressive strength of 12.84 MPa, compared with 11.85 MPa for PPA-CF-CFRP. These findings indicate that the mechanical response depends on the loading mode and is influenced by the combined effects of the thermoplastic matrix, carbon-fiber reinforcement architecture, and the resulting structural characteristics of the printed gyroid cores. DMA revealed that the PPA-CF-CFRP sandwich achieved a storage modulus of ~9 GPa at 30 °C, outperforming the ONYX-R-CFRP configuration by approximately 70%. Conversely, ONYX-R-CFRP exhibited the highest damping capacity, with a maximum tan δ of approximately 0.16, about 60% higher than the PPA-CF-CFRP configuration. The ONYX-CFRP sandwich configuration displayed the lowest mechanical and thermo-mechanical performance, demonstrating that the stiffness, deformation capacity, damping response, and temperature-dependent mechanical behavior of these sandwich structures can be tailored through the selection of the additively manufactured core configuration.
SN - 2073-4360
ER -