Exsolution-Engineered Ni-Based Titanate Perovskites for Dry Reforming of Methane: Activity-Stability Trade-Offs and Deactivation Mechanisms
- 1University of Padova , , Via F. Marzolo 1 , ,
- 2Elettra Sincrotrone Trieste S.C.p.A. , s.s. 14 Km 163.5, Basovizza , ,
Abstract
Syngas production via dry reforming of methane (DRM) represents a promising route for the valorization of carbon-based molecules, CH4 and CO2, in the emerging decarbonization era. However, the harsh operating conditions required by DRM demand highly active and robust catalysts to exploit this process for hydrogen production. In this context, the rational design of thermally stable catalysts with enhanced resistance to deactivation becomes essential. Herein, we focus on elucidating the structural and morphological evolution of Ni-, Ni–Co-, and Ni–Fe-doped titanates with a perovskite framework during guest cation incorporation and subsequent exsolution. Structural, compositional, and surface modifications were investigated by XRD, SEM, EDX, XAFS, N2 physisorption, and XPS. The catalytic performance of the exsolved materials was evaluated in DRM. The Ni-doped titanate (LSTNO-H) exhibited higher catalytic activity than Ni/γ-Al2O3 for CO2 conversion, reaching 80% conversion at 708 °C compared to 715 °C under short-term tests. However, the titanates still show room for improvement in long-term activity and durability. To elucidate the mechanisms governing catalyst deactivation, DRM tests were performed under diluted conditions, enabling a comparative assessment of structural and surface changes during reaction. Under such conditions, catalyst deactivation was mainly associated with nanoparticle sintering, with partial metal oxidation potentially contributing to activity loss, while no significant carbon deposition was detected. In contrast, the benchmark Ni/γ-Al2O3 catalyst showed carbon deposition, although no measurable deactivation occurred under the investigated conditions. Overall, this study highlights the potential of exsolution-based titanates for DRM while providing insights into the deactivation behavior of exsolved Ni under the investigated conditions.
Related
- Catalytic Steam Reforming of Methanol, Ethanol, and Glycerol for Hydrogen Production: A Critical Review of Reaction Chemistry, Catalyst Design, Performance Metrics, and Deactivation
- The Role of Manganese in CeNi1−xMnxO₃ Nano-Crystalline Perovskites for Dry Reforming of Methane to Produce Syngas
- Activation engineered Sr rich Ruddlesden–Popper oxides for robust SOFC and dry reforming catalysis
- Ruδ+-Engineered La2Ti2-xRuxO7 Perovskite with Dynamic Lattice Oxygen Vacancies for Efficient and Stable Photothermal Dry Reforming of Methane.
- Iron–Nitride Isomerization as a Deactivation Pathway in Ammonia Oxidation: A Computational Study of Sequential HAT Mechanisms
BibTeX
@article{cavazzani2026exsolutionengineered,
title = {{Exsolution-Engineered Ni-Based Titanate Perovskites for Dry Reforming of Methane: Activity-Stability Trade-Offs and Deactivation Mechanisms}},
author = {Jonathan Cavazzani and Andrea Osti and Lorenzo Rizzato and Giovanni Agostini and Antonella Glisenti},
journal = {ACS Omega},
year = {2026},
month = nov,
doi = {10.1021/acsomega.6c07908},
url = {https://pubs.acs.org/acsodf/article/doi/10.1021/acsomega.6c07908/5466127/Exsolution-Engineered-Ni-Based-Titanate},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Exsolution-Engineered Ni-Based Titanate Perovskites for Dry Reforming of Methane: Activity-Stability Trade-Offs and Deactivation Mechanisms
AU - Jonathan Cavazzani
AU - Andrea Osti
AU - Lorenzo Rizzato
AU - Giovanni Agostini
AU - Antonella Glisenti
PY - 2026
DA - 2026/11/07
JO - ACS Omega
DO - 10.1021/acsomega.6c07908
UR - https://pubs.acs.org/acsodf/article/doi/10.1021/acsomega.6c07908/5466127/Exsolution-Engineered-Ni-Based-Titanate
AB - Syngas production via dry reforming of methane (DRM) represents a promising route for the valorization of carbon-based molecules, CH4 and CO2, in the emerging decarbonization era. However, the harsh operating conditions required by DRM demand highly active and robust catalysts to exploit this process for hydrogen production. In this context, the rational design of thermally stable catalysts with enhanced resistance to deactivation becomes essential. Herein, we focus on elucidating the structural and morphological evolution of Ni-, Ni–Co-, and Ni–Fe-doped titanates with a perovskite framework during guest cation incorporation and subsequent exsolution. Structural, compositional, and surface modifications were investigated by XRD, SEM, EDX, XAFS, N2 physisorption, and XPS. The catalytic performance of the exsolved materials was evaluated in DRM. The Ni-doped titanate (LSTNO-H) exhibited higher catalytic activity than Ni/γ-Al2O3 for CO2 conversion, reaching 80% conversion at 708 °C compared to 715 °C under short-term tests. However, the titanates still show room for improvement in long-term activity and durability. To elucidate the mechanisms governing catalyst deactivation, DRM tests were performed under diluted conditions, enabling a comparative assessment of structural and surface changes during reaction. Under such conditions, catalyst deactivation was mainly associated with nanoparticle sintering, with partial metal oxidation potentially contributing to activity loss, while no significant carbon deposition was detected. In contrast, the benchmark Ni/γ-Al2O3 catalyst showed carbon deposition, although no measurable deactivation occurred under the investigated conditions. Overall, this study highlights the potential of exsolution-based titanates for DRM while providing insights into the deactivation behavior of exsolved Ni under the investigated conditions.
SN - 2470-1343
ER -