Activation engineered Sr rich Ruddlesden–Popper oxides for robust SOFC and dry reforming catalysis
Abstract
Activation engineering is proposed as a process-centric design strategy that shifts focus from stabilizing pristine oxides to tailoring metastable states through controlled reduction histories to unlock functional properties inaccessible at thermodynamic equilibrium. Unlike defect engineering or conventional doping, it operates exclusively through process variables applied to a fixed precursor to address United Nations SDGs 7, 9, and 13. Using real-time in situ neutron diffraction on layered Ruddlesden–Popper (RP, An+1BnO3n+1) oxides, Ln₀.₅Sr₁.₅Mn₀.₇Ni₀.₃O₄ (LN3 for Ln = La; PN3 for Ln = Pr), we demonstrate that a single precursor can be steered toward divergent functional architectures. A moderate activation (5% H₂/N₂, 700°C, 48 h) exsolves ≈1 wt% Ni, templated by surface SrO nanodomains, creating a Solid Oxide Fuel Cell anode with a benchmark Area Specific Resistance, ASR of 0.74 Ω·cm² for RP oxides at 700 °C, stable over 135 hours. Conversely, intense activation (pure H2, 750 °C, 12 h) drives deep reduction ≈5 wt% Ni exsolution), enabling >28 hours of dry reforming stability at 39% CH4 conversion. Crucially, Raman spectroscopy and Transmission electron microscopy (TEM) reveal an exsolution paradox: PN3 exsolves finer particles, they undergo rapid graphitic encapsulation (ID/IG ≈ 1.3±0.2), whereas LN3 accumulates carbon in a dispersed, Raman-invisible morphology that leaves active sites accessible. Post-reaction analysis rationalizes these divergent fates through contrasting reconstruction pathways: LN3 transforms into a stable Ni/La2O2CO3/LaMnO3 nanocomposite where the oxycarbonate buffer sustains activity, whereas PN3 undergoes structural collapse. These findings validate activation history as a primary design variable for crafting multifunctional energy materials.
Related
- Electronic modulation-driven Co-doped Ruddlesden-Popper for bifunctional OER/HER overall water splitting
- Polar Ruddlesden–Popper Rare-Earth Aluminum Oxynitrides with Partial Anion Order
- Multistep microwave-assisted approach for the controlled insertion of Cu(II) into Dion–Jacobson and Ruddlesden–Popper layered perovskites
- Topochemical Fluorination of the Ruddlesden−Popper In/Sb-Mixed Oxide Ba2In0.5Sb0.5O4; Staged Anion Insertion and Structural Evolution toward the Fluorine-Rich Oxyfluoride Ba2In0.5Sb0.5O2F4
- Exsolution-Engineered Ni-Based Titanate Perovskites for Dry Reforming of Methane: Activity-Stability Trade-Offs and Deactivation Mechanisms
BibTeX
@article{bahout2026activation,
title = {{Activation engineered Sr rich Ruddlesden–Popper oxides for robust SOFC and dry reforming catalysis}},
author = {Mona Bahout and Thi Thuy Duyen Nguyen and Elodie Quenard and Thomas C Hansen and Vincent Dorcet and Marcia Araque-Marin and Serge Paofai and Noee Dumait and Annie Le Gal La Salle and Olivier Joubert},
journal = {Next Energy},
year = {2026},
month = oct,
doi = {10.1016/j.nxener.2026.100680},
url = {https://hal.science/hal-05645834v2},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Activation engineered Sr rich Ruddlesden–Popper oxides for robust SOFC and dry reforming catalysis
AU - Mona Bahout
AU - Thi Thuy Duyen Nguyen
AU - Elodie Quenard
AU - Thomas C Hansen
AU - Vincent Dorcet
AU - Marcia Araque-Marin
AU - Serge Paofai
AU - Noee Dumait
AU - Annie Le Gal La Salle
AU - Olivier Joubert
PY - 2026
DA - 2026/10/08
JO - Next Energy
DO - 10.1016/j.nxener.2026.100680
UR - https://hal.science/hal-05645834v2
AB - Activation engineering is proposed as a process-centric design strategy that shifts focus from stabilizing pristine oxides to tailoring metastable states through controlled reduction histories to unlock functional properties inaccessible at thermodynamic equilibrium. Unlike defect engineering or conventional doping, it operates exclusively through process variables applied to a fixed precursor to address United Nations SDGs 7, 9, and 13. Using real-time in situ neutron diffraction on layered Ruddlesden–Popper (RP, An+1BnO3n+1) oxides, Ln₀.₅Sr₁.₅Mn₀.₇Ni₀.₃O₄ (LN3 for Ln = La; PN3 for Ln = Pr), we demonstrate that a single precursor can be steered toward divergent functional architectures. A moderate activation (5% H₂/N₂, 700°C, 48 h) exsolves ≈1 wt% Ni, templated by surface SrO nanodomains, creating a Solid Oxide Fuel Cell anode with a benchmark Area Specific Resistance, ASR of 0.74 Ω·cm² for RP oxides at 700 °C, stable over 135 hours. Conversely, intense activation (pure H2, 750 °C, 12 h) drives deep reduction ≈5 wt% Ni exsolution), enabling >28 hours of dry reforming stability at 39% CH4 conversion. Crucially, Raman spectroscopy and Transmission electron microscopy (TEM) reveal an exsolution paradox: PN3 exsolves finer particles, they undergo rapid graphitic encapsulation (ID/IG ≈ 1.3±0.2), whereas LN3 accumulates carbon in a dispersed, Raman-invisible morphology that leaves active sites accessible. Post-reaction analysis rationalizes these divergent fates through contrasting reconstruction pathways: LN3 transforms into a stable Ni/La2O2CO3/LaMnO3 nanocomposite where the oxycarbonate buffer sustains activity, whereas PN3 undergoes structural collapse. These findings validate activation history as a primary design variable for crafting multifunctional energy materials.
SN - 2949-821X
ER -