Biomechanical and finite element analysis of a novel annular multi-axial locking plate for patellar fracture fixation.
- 1Department of Orthopaedics, Longhua Hospital affiliated to Shanghai University of Traditional Chinese Medicine, No. 99, Hangdu Road, Pudong New Area, Shanghai, 200032, China.
- 2Department of Orthopaedics, Longhua Hospital affiliated to Shanghai University of Traditional Chinese Medicine, No. 99, Hangdu Road, Pudong New Area, Shanghai, 200032, China. [email protected].
Abstract
Background
Traditional tension band structures for patellar fractures have multiple complications such as wires lossening and soft tissue irritation. In response to the above problems, a new type of annular multi-axis locking plate has been designed for the treatment of patellar fractures. This study aims to compare the biomechanical performance of two methods for stabilizing patellar fractures.Methods
A three-dimensional finite element model was established to evaluate the biomechanical performance of annular multi-axis locking steel plate fixation for patellar fractures at knee flexion angles of 20, 45, and 90°. Furthermore, four pairs of matched fresh-frozen cadaveric transverse patellar fracture models (AO/OTA 34B1) stabilized with annular multi-axis locking steel plates (AMALP, experimental group) and cable tension band (CTB, control group) were established to compare the biomechanical performance of the two internal fixation methods. Dynamic fatigue testing was performed by moving the knee from 90to 0° under a load of 6 kg until 200 cycles were completed or the internal device failures. Using a testing machine to evaluate the ultimate force required for the failure of each internal device at knee flexion angles of 20, 45, and 90°. The fracture displacement distance and the ultimate load were recorded.Results
The outcome of finite element analysis (FEA) demonstrated the max value of Von-Mises stress of the three knee flexion angles simulated were between 45.328 MPa to 109.191 MPa,which is lower than the yield strength value of the plate(351-429 MPa).The displacement value was between 0.1645 and 0.3487 mm, which is acceptable according to clinical criterion(< 2 mm).After 200 cycles of knee flexion fatigue testing, neither group showed any failure of internal fixation. After 100, 150, and 200 cycles of knee flexion fatigue testing, the displacement of the fracture on the anterior surface (0.36 ± 0.05 mm, 0.41 ± 0.04 mm, 0.49 ± 0.08 mm) and joint surface (0.29 ± 0.05 mm, 0.36 ± 0.07 mm, 0.44 ± 0.09 mm) in AMALP were significantly lower than those in the CTB (anterior surface: 0.54 ± 0.09 mm, 0.66 ± 0.11 mm, 0.73 ± 0.09 mm) (joint surface: 0.45 ± 0.06 mm, 0.52 ± 0.06 mm, 0.59 ± 0.08 mm) (P < 0.05).Across all three knee flexion angles (20, 45, and 90°), the AMALP exhibited significantly higher ultimate failure loads (812.40 ± 46.62 N, 546.59 ± 45.22 N, and 370.52 ± 36.41 N, respectively) compared to the CTB(669.60 ± 65.43 N, 423.71 ± 39.46 N, and 264.57 ± 48.15 N, respectively; P < 0.05).Conclusion
The novel plate features an anatomically contoured profile that closely conforms to the patellar surface, adhering to the principles of tension-band fixation. The screw trajectories are designed with a centripetal orientation, generating intrinsic compressive forces that facilitate axial compression across the fracture site. This not only helps maintain patellar integrity but also enhances knee joint stability, aligning well with established biomechanical principles. Collectively, these design characteristics position the novel plate as a promising new internal fixation option for the treatment of patellar fractures.
Related
- Addition of a McLaughlin cerclage to locking plate fixation of distal patellar pole fractures reduces interfragmentary displacement – a biomechanical human cadaveric study
- Subject-Specific Finite Element Modelling of Le Fort I Osteotomy Fixation: Biomechanical Insights Comparing Patient-Specific Implants and Conventional Miniplates
- Biomechanical comparative analysis of minimally invasive decompression and minimally invasive fusion with internal fixation in the treatment of lumbar spinal stenosis with degenerative spondylolisthesis: a finite element study.
- The influence of mandibular third molar classification on fixation stability of mandibular angle fractures: a biomechanical finite element analysis
- Importance of correct femoral tunnel placement to avoid MPFL graft failure: a case report of habitual patellar dislocation after proximal physis fixation.
BibTeX
@article{zou2026biomechanical,
title = {{Biomechanical and finite element analysis of a novel annular multi-axial locking plate for patellar fracture fixation.}},
author = {Hanlin Zou and Lin Zhou and Qiang Zhou and Jianwei Yang and Yunchu Sun and Lei Zhang},
journal = {Journal of orthopaedic surgery and research},
year = {2026},
month = jul,
doi = {10.1186/s13018-026-07115-5},
url = {https://europepmc.org/article/MED/42902319},
note = {CC BY-NC-ND},
}
RIS
TY - JOUR
TI - Biomechanical and finite element analysis of a novel annular multi-axial locking plate for patellar fracture fixation.
AU - Hanlin Zou
AU - Lin Zhou
AU - Qiang Zhou
AU - Jianwei Yang
AU - Yunchu Sun
AU - Lei Zhang
PY - 2026
DA - 2026/07/01
JO - Journal of orthopaedic surgery and research
DO - 10.1186/s13018-026-07115-5
UR - https://europepmc.org/article/MED/42902319
AB - Background Traditional tension band structures for patellar fractures have multiple complications such as wires lossening and soft tissue irritation. In response to the above problems, a new type of annular multi-axis locking plate has been designed for the treatment of patellar fractures. This study aims to compare the biomechanical performance of two methods for stabilizing patellar fractures.Methods A three-dimensional finite element model was established to evaluate the biomechanical performance of annular multi-axis locking steel plate fixation for patellar fractures at knee flexion angles of 20, 45, and 90°. Furthermore, four pairs of matched fresh-frozen cadaveric transverse patellar fracture models (AO/OTA 34B1) stabilized with annular multi-axis locking steel plates (AMALP, experimental group) and cable tension band (CTB, control group) were established to compare the biomechanical performance of the two internal fixation methods. Dynamic fatigue testing was performed by moving the knee from 90to 0° under a load of 6 kg until 200 cycles were completed or the internal device failures. Using a testing machine to evaluate the ultimate force required for the failure of each internal device at knee flexion angles of 20, 45, and 90°. The fracture displacement distance and the ultimate load were recorded.Results The outcome of finite element analysis (FEA) demonstrated the max value of Von-Mises stress of the three knee flexion angles simulated were between 45.328 MPa to 109.191 MPa,which is lower than the yield strength value of the plate(351-429 MPa).The displacement value was between 0.1645 and 0.3487 mm, which is acceptable according to clinical criterion(< 2 mm).After 200 cycles of knee flexion fatigue testing, neither group showed any failure of internal fixation. After 100, 150, and 200 cycles of knee flexion fatigue testing, the displacement of the fracture on the anterior surface (0.36 ± 0.05 mm, 0.41 ± 0.04 mm, 0.49 ± 0.08 mm) and joint surface (0.29 ± 0.05 mm, 0.36 ± 0.07 mm, 0.44 ± 0.09 mm) in AMALP were significantly lower than those in the CTB (anterior surface: 0.54 ± 0.09 mm, 0.66 ± 0.11 mm, 0.73 ± 0.09 mm) (joint surface: 0.45 ± 0.06 mm, 0.52 ± 0.06 mm, 0.59 ± 0.08 mm) (P < 0.05).Across all three knee flexion angles (20, 45, and 90°), the AMALP exhibited significantly higher ultimate failure loads (812.40 ± 46.62 N, 546.59 ± 45.22 N, and 370.52 ± 36.41 N, respectively) compared to the CTB(669.60 ± 65.43 N, 423.71 ± 39.46 N, and 264.57 ± 48.15 N, respectively; P < 0.05).Conclusion The novel plate features an anatomically contoured profile that closely conforms to the patellar surface, adhering to the principles of tension-band fixation. The screw trajectories are designed with a centripetal orientation, generating intrinsic compressive forces that facilitate axial compression across the fracture site. This not only helps maintain patellar integrity but also enhances knee joint stability, aligning well with established biomechanical principles. Collectively, these design characteristics position the novel plate as a promising new internal fixation option for the treatment of patellar fractures.
SN - 1749-799X
ER -