Crystallographic-orientation dependence of the early-stage oxidation of Zr single crystals: an XPS study of suboxide formation and in-depth distribution
Abstract
The influence of crystallographic orientation on the early stages of the oxidation of pure Zr single crystals was studied by X ray photoelectron spectroscopy (XPS). Two samples, cut from the same a-Zr single crystal, were oxidized simultaneously at room temperature and O2 pressures of 1 X 10-8, 1 X 10-7 and 1 X 10-6 torr: one with its surface normal parallel to the c-axis (Z1, basal (0001) plane) and the other with its normal 12deg from that of a prismatic plane (Z2, near-prismatic orientation). At all three pressures the oxidation kinetics of both samples followed a three stage, logarithmic type behaviour, but the near prismatic sample (Z2) incorporated oxygen faster and to a greater extent than the basal sample (Z1) in every case. Deconvolution of the Zr 3d core level spectra resolved, in addition to metallic Zr and ZrO2, two sub-stoichiometric Zr O compounds, denoted (ZrO)a and (ZrO)b, with binding-energy shifts of 1.3 and 2.3 eV with respect to metallic Zr, consistent with sub oxides previously reported for polycrystalline Zr. Angle resolved XPS showed that ZrO2 is the outermost compound in both orientations, while the two sub-oxides are distributed nearly homogeneously through the film. Oxide thicknesses, calculated from the attenuation of the metallic Zr 3d signal, ranged from 10 to 13 A for Z1 and from 14 to 19 A for Z2 depending on the oxidation pressure, in close agreement with earlier measurements on cold worked polycrystalline Zr, whose surface texture is dominated by prismatic-oriented grains.
Versions
Related
- Quantification of the crystallographic anisotropy and thermal dependence of Tb diffusion coefficients in the Nd2Fe14B phase through single-crystal diffusion couples
- Dependence of the acoustic propulsion of nano- and microcones on their orientation and aspect ratio
- The variance of the CMB temperature gradient: a dependence on the spatial orientation and anisotropy of a multiply connected Universe
- Scalability bottlenecks in entanglement-based satellite quantum key distribution: downlink asymmetry, orbit dependence and finite-key effects
- Formation of the titanium oxyl at an electrochemical interface: limiting the role of solvent re-orientation in strong electric fields
BibTeX
@misc{sacanell2026crystallographicorientation,
title = {{Crystallographic-orientation dependence of the early-stage oxidation of Zr single crystals: an XPS study of suboxide formation and in-depth distribution}},
author = {Joaquin Sacanell and Flavio Conde},
howpublished = {arXiv},
year = {2026},
month = sep,
doi = {10.48550/arxiv.2609.31496},
eprint = {2609.31496},
archivePrefix = {arXiv},
url = {https://arxiv.org/abs/2609.31496},
note = {CC BY 4.0},
}
RIS
TY - UNPB
TI - Crystallographic-orientation dependence of the early-stage oxidation of Zr single crystals: an XPS study of suboxide formation and in-depth distribution
AU - Joaquin Sacanell
AU - Flavio Conde
PY - 2026
DA - 2026/09/25
PB - arXiv
DO - 10.48550/arxiv.2609.31496
UR - https://arxiv.org/abs/2609.31496
AB - The influence of crystallographic orientation on the early stages of the oxidation of pure Zr single crystals was studied by X ray photoelectron spectroscopy (XPS). Two samples, cut from the same a-Zr single crystal, were oxidized simultaneously at room temperature and O2 pressures of 1 X 10-8, 1 X 10-7 and 1 X 10-6 torr: one with its surface normal parallel to the c-axis (Z1, basal (0001) plane) and the other with its normal 12deg from that of a prismatic plane (Z2, near-prismatic orientation). At all three pressures the oxidation kinetics of both samples followed a three stage, logarithmic type behaviour, but the near prismatic sample (Z2) incorporated oxygen faster and to a greater extent than the basal sample (Z1) in every case. Deconvolution of the Zr 3d core level spectra resolved, in addition to metallic Zr and ZrO2, two sub-stoichiometric Zr O compounds, denoted (ZrO)a and (ZrO)b, with binding-energy shifts of 1.3 and 2.3 eV with respect to metallic Zr, consistent with sub oxides previously reported for polycrystalline Zr. Angle resolved XPS showed that ZrO2 is the outermost compound in both orientations, while the two sub-oxides are distributed nearly homogeneously through the film. Oxide thicknesses, calculated from the attenuation of the metallic Zr 3d signal, ranged from 10 to 13 A for Z1 and from 14 to 19 A for Z2 depending on the oxidation pressure, in close agreement with earlier measurements on cold worked polycrystalline Zr, whose surface texture is dominated by prismatic-oriented grains.
ER -