Biogenic Magnetosomes as Magnetically Recoverable Catalysts for Benzyl Alcohol Oxidation
- 1Aston University , , Aston Triangle , ,
- 2University of Leeds , , ,
- 3University of Birmingham , , Edgbaston, ,
Abstract
Biogenic magnetosomes are intracellular single-domain magnetic nanoparticles (MNPs) produced by Magnetospirillum gryphiswaldense MSR1, consisting of crystalline magnetite (Fe3O4) encapsulated within an organic membrane. Despite their controlled structure and widespread study in biomedical and magnetic applications, their use in catalysis has not been explored. Here, magnetosomes are demonstrated for the first time as heterogeneous catalysts for benzyl alcohol oxidation using hydrogen peroxide. Under aqueous batch conditions, catalytic performance was tested, varying catalyst loading and temperature. Among the loadings tested, the highest conversion was achieved using 5.2 mol % Fe3O4 equivalent, reaching 64 ± 4% after 24 h with 36 ± 5% benzaldehyde selectivity. At approximately matched Fe3O4 contents, this performance was broadly comparable to commercial Fe3O4, which produced 72 ± 2% conversion and 38 ± 3% selectivity. Temperature screening of magnetosome catalysts increased conversion up to 75 ± 11% at 85 °C with 30 ± 4% benzaldehyde selectivity. Meanwhile milder conditions improved selectivity to 43 ± 2% at the expense of lower conversion, reflecting the expected conversion/selectivity trade-offs seen in wider iron oxide-catalyzed peroxide systems. Catalytic recyclability was demonstrated over five reaction cycles, where magnetic recovery enabled the spent mixture to be removed and replaced without centrifugation or filtration. During these cycles conversion decreased only modestly from 71 ± 5% to 65 ± 4% with selectivity remaining between 33 and 38%. Overall, this work demonstrates that biogenic magnetosomes can function as catalytic materials and expands the potential applications of magnetotactic bacteria-derived nanostructures.
Related
- Nanoscale identification of organic pigments in biogenic calcite by atom probe tomography
- Magnetically guided programmable thermomechanical protection enabled by biomimetic asymmetric design
- Triphenylphosphonium compounds preferentially inhibit long-chain fatty acid oxidation in cardiac mitochondria
- Fluorescence imaging-induced phospholipid oxidation drives membrane phase separation by shifting miscibility boundaries
- Biomolecular condensates can function as inherent catalysts
BibTeX
@article{bond2026biogenic,
title = {{Biogenic Magnetosomes as Magnetically Recoverable Catalysts for Benzyl Alcohol Oxidation}},
author = {Josh Bond and Marcia Mendes de Carvalho and Amin Osatiashtiani and Tim William Overton and Oliver Brooks and Vesna Najdanovic-Visak and Alfred Fernandez-Castane},
journal = {ACS Omega},
year = {2026},
month = oct,
doi = {10.1021/acsomega.6c07960},
url = {https://pubs.acs.org/acsodf/article/11/41/63744/5448081/Biogenic-Magnetosomes-as-Magnetically-Recoverable},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Biogenic Magnetosomes as Magnetically Recoverable Catalysts for Benzyl Alcohol Oxidation
AU - Josh Bond
AU - Marcia Mendes de Carvalho
AU - Amin Osatiashtiani
AU - Tim William Overton
AU - Oliver Brooks
AU - Vesna Najdanovic-Visak
AU - Alfred Fernandez-Castane
PY - 2026
DA - 2026/10/09
JO - ACS Omega
DO - 10.1021/acsomega.6c07960
UR - https://pubs.acs.org/acsodf/article/11/41/63744/5448081/Biogenic-Magnetosomes-as-Magnetically-Recoverable
AB - Biogenic magnetosomes are intracellular single-domain magnetic nanoparticles (MNPs) produced by Magnetospirillum gryphiswaldense MSR1, consisting of crystalline magnetite (Fe3O4) encapsulated within an organic membrane. Despite their controlled structure and widespread study in biomedical and magnetic applications, their use in catalysis has not been explored. Here, magnetosomes are demonstrated for the first time as heterogeneous catalysts for benzyl alcohol oxidation using hydrogen peroxide. Under aqueous batch conditions, catalytic performance was tested, varying catalyst loading and temperature. Among the loadings tested, the highest conversion was achieved using 5.2 mol % Fe3O4 equivalent, reaching 64 ± 4% after 24 h with 36 ± 5% benzaldehyde selectivity. At approximately matched Fe3O4 contents, this performance was broadly comparable to commercial Fe3O4, which produced 72 ± 2% conversion and 38 ± 3% selectivity. Temperature screening of magnetosome catalysts increased conversion up to 75 ± 11% at 85 °C with 30 ± 4% benzaldehyde selectivity. Meanwhile milder conditions improved selectivity to 43 ± 2% at the expense of lower conversion, reflecting the expected conversion/selectivity trade-offs seen in wider iron oxide-catalyzed peroxide systems. Catalytic recyclability was demonstrated over five reaction cycles, where magnetic recovery enabled the spent mixture to be removed and replaced without centrifugation or filtration. During these cycles conversion decreased only modestly from 71 ± 5% to 65 ± 4% with selectivity remaining between 33 and 38%. Overall, this work demonstrates that biogenic magnetosomes can function as catalytic materials and expands the potential applications of magnetotactic bacteria-derived nanostructures.
SN - 2470-1343
ER -